Zein/Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) electrospun blend fiber scaffolds: Preparation, characterization and cytocompatibility.

In the present work, a series of Zein/Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blend fiber scaffolds have been prepared by electrospinning method. The electrospun fibers showed a circular and uniform morphology with random distribution. The blend fiber scaffolds possessed well interconnected porous fibrous network structure with high porosity and large aspect surface areas. The FTIR and XPS spectra of Zein/P(3HB-co-4HB) blend fibers demonstrated the same characteristics to that of pure Zein and P(3HB-co-4HB) electrospun fibers. However, Zein might hinder the crystallization of P(3HB-co-4HB) owing to the formation of weak intermolecular interactions, which can affect the preferential orientation of P(3HB-co-4HB) molecules. Only one glass transition temperature (Tg) can be detected for electrospun Zein/P(3HB-co-4HB) blend fiber scaffolds implying the miscibility of Zein and P(3HB-co-4HB) in the blend fibers. The Zein/P(3HB-co-4HB) blend fiber scaffolds showed about 50% of improvement in tensile strength and 400% of increase in elongation at break by increasing P(3HB-co-4HB) content from 20% to 80%. The cytocompatibility of the Zein/P(3HB-co-4HB) blend fiber scaffolds was preliminarily evaluated by cell culture in vitro. The as-prepared electrospun Zein/P(3HB-co-4HB) blend fiber scaffolds with the characteristics of good biocompatibility, excellent pore characteristic as well as sufficient mechanical properties should be more promising for applications as tissue engineering scaffold.