Water adsorption and O-defect formation on Fe2O3(0001) surfaces.

The stability and reactivity of the hematite, Fe2O3(0001) surface are studied by density functional theory including an on-site Coulomb term (DFT+U). Even under oxygen rich conditions, the metal-terminated surface is shown to be stable. On this surface termination, the isolated water molecule forms a heterolytically dissociated structure with the OH- group attached to a surface Fe3+ ion and the proton to a surface O2- ion. Dissociative adsorption is strongly enhanced at oxygen vacancy sites. Here, the OH- group fills the oxygen vacancy site. Dehydrogenation accompanied by defect healing is favoured compared to water desorption (178 kJ mol-1 compared to 236 kJ mol-1). The water adsorption energies (at 0 K) for the clean and defective surfaces are 100 kJ mol-1 and 288 kJ mol-1, respectively.