Shape-Controlled Synthesis of All-Inorganic CsPbBr3 Perovskite Nanocrystals with Bright Blue Emission.

We developed a colloidal synthesis of CsPbBr3 perovskite nanocrystals (NCs) at a relative low temperature (90 °C) for the bright blue emission which differs from the original green emission (∼510 nm) of CsPbBr3 nanocubes as reported previously. Shapes of the obtained CsPbBr3 NCs can be systematically engineered into single and lamellar-structured 0D quantum dots, as well as face-to-face stacking 2D nanoplatelets and flat-lying 2D nanosheets via tuning the amounts of oleic acid (OA) and oleylamine (OM). They exhibit sharp excitonic PL emissions at 453, 472, 449, and 452 nm, respectively. The large blue shift relative to the emission of CsPbBr3 bulk crystal can be ascribed to the strong quantum confinement effects of these various nanoshapes. PL decay lifetimes are measured, ranging from several to tens of nanoseconds, which infers the higher ratio of exciton radiative recombination to the nonradiative trappers in the obtained CsPbBr3 NCs. These shape-controlled CsPbBr3 perovskite NCs with the bright blue emission will be widely used in optoelectronic applications, especially in blue LEDs which still lag behind compared to the better developed red and green LEDs.