Kinetic studies of attachment and re-orientation of octyltriethoxysilane for formation of self-assembled monolayer on a silica substrate.

The present study deals with kinetic studies of the chemical modification for synthesizing a hydrophobic silica surface. Surface silanization (modification) via formation of Self-Assembled Monolayer (SAM) using a short chain triethoxyoctylsilane (TEOS) was carried out under inert atmosphere at room temperature. Fourier transmission infrared (FTIR) spectroscopy, water contact angle (WCA) and atomic force microscopy (AFM) were employed to investigate surface modification. FTIR analysis in the range from 900-1200cm(-1) and 2850-3000cm(-1) confirmed surface modification and re-orientation of the attached molecules. Kinetic studies of TEOS SAM formation were fitted by Exponential Association function. Kinetic fitting of FTIR data in the range from 900-1200cm(-1) revealed a very fast attachment of TEOS molecules resulting in total surface coverage within 16min whereas re-orientation rate was slow and continued till 512min. Further, change in orientation from lying-down to standing-up state was supported by contact angle analysis. AFM images initially showed small islands of ~20nm, which in-fill with time indicating formation of a smooth monolayer. Our findings indicate that formation of octyl SAM is fast process and completes within 8.5h in contrary to reported 24h in conventional SAM formation protocols. The kinetic fitting data can be explored to design a nanopatterned surface for a specific application.