CZTS x Se1-x nanocrystals: Composition dependent method of preparation, morphological characterization and cyclic voltammetry data analysis.

In this article, synthesis procedures of preparation of copper zinc tin sulpho-selenide (CZTS x Se1-x ) alloy nanocrystals and the data acquired for the material characterization are presented. This data article is related to the research article doi: http://dx.doi.org/10.1016/j.solmat.2016.06.030 (Jadhav et al., 2016) [1]. FTIR data have been presented which helped in confirmation of adsorption of oleylamine on CZTS x Se1-x . Transmission electron microscopy (TEM), Field emission scanning electron microscopy (FESEM) and atomic force microscopy (AFM) data have been presented which have been used to reveal the morphological details of the nanocrystals. The Energy dispersive X-ray analysis (EDAX) based elemental mapping data has been presented to confirm the elemental composition of nanocrystals. Procedure for the preparation of CZTS x Se1-x based working electrode for the CV measurements have been given. The summary table for the optical, electrochemical band gaps, valance and conduction band edges as a function of composition are listed for the ready reference.

Specification Table

Value of the data

Detail Solvothermal procedure for the preparation CZTSSe1− (x=0–1) nanocrystals have been presented.

Detail FTIR data analysis has been presented for the adsorbed oleylamine molecules on the CZTSSe1− nanocrystals.

AFM, TEM and FESEM data have been used to demonstrate composition independent morphological similarity of CZTSSe1−. The EDAX mapping data have been used to confirms the absence of phase segregation and formation of uniform composition.

Composition dependent band edge positions have been presented in tabular form which will act as a guideline to design novel heterojunction photovoltaic device by band alignment engineering.

Data

The data given in this data article are in the form of seven figures and one table. It describes detail synthesis, characterization and procedure followed for cyclic voltammetry investigation of CZTSSe1−(x=0–1) nanocrystals. TEM data have been presented for highlight the morphology and size distribution. The topography has been recorded by FESEM and AFM image analysis. The EDAX spectra give the details about composition and stoichiometry. Uniform distributions of the constituent elements are seen in the elemental mapping images. The adsorption of capping agent, oleylamine has been confirmed by FTIR data. The procedure for the preparation of working electrode for the electrochemical investigation is described in detail.

Experimental design, materials and methods

Synthesis setup and CZTSSe1− alloy nanocrystals synthesis

The Synthesis of the CZTSSe1−(x=0–1) nanocrystals carried out using hot injection method suggested by Agrawal and Riha et al. [2], [3]. A typical synthesis setup used in present investigation [1] is shown in Fig. 1. The sequence of addition is marked as red-arrows. Weighed amount of all the constituents (salts in oleylamine (OLA)) are first transferred into the three necked flask, mounted on heating mantle, having temperature controller. Upon heating to 130 °C with constant stirring, all the metal complexes dissolved and from brown transparent solution. Temperature is raised further to 225 °C (Refer Fig. 1(A)) and into it freshly prepared S/Se in OLA solution was added, which leads to black color product (Refer Fig. 1(C)).

Fig. 1

Experimental setup used and sequence of the addition followed in the synthesis of CZTSSe1− (x=0–1) alloy nanocrystals.

Drop-casting of films on the working electrode

The electrochemical measurements on the samples have been done on CZTSSe1− coated gold-disk working electrode (2 mm diameter). For that, the sample was applied on the electrode by method of drop-casting. For that, the electrode was mounted vertically in a desiccator. 75 μL dispersion of nanocrystals in dichloromethane was applied carefully onto the electrode surface. The drop was allowed to dry by the help of mild vacuum (diaphragm vacuum pump) for 15 min. This helps solvents to evaporate quickly and form a film on the electrode surface. Adhesion of the film was found to be good and did not show any tendency to fall down or fouling in the solvent, during the measurements. From the weight of the loading, area of the electrode and density of samples, the thickness of the films were estimated and found to be in the range 58 μm. Such modified electrodes were used as prepared without any post annealing.

Characterization of CZTSSe1− alloy nanocrystals

FTIR spectroscopy data on CZTS Sample

Fig. 2(A) shows the FTIR spectra recorded on CZTS nanocrystals powder samples and its comparison with a neat oleylamine sample (coordinating solvent). The band at 3372 cm−1 and 3292 cm−1 in OLA sample is attributed to the asymmetric and symmetric stretching from primary NH2 group [4]. These bands are replaced by new band at 3170 cm−1 in CZTS samples those matched with stretching vibration from the secondary amine group. This observation is explained on the basis of change in bond order during the adsorption. Similarly, the intensity of bending vibrations at 795 cm−1 for the NH2 in OLA is decreased and shifted to 802 cm−1 in CZTS sample. Intensity of the CH3 and corresponding to C–C bending vibrations at 1465 cm−1 and 722 cm−1 are decreased in case of OLA adsorbed on CZTS. In both the cases, neat OLA and OLA on CZTS show the C–H symmetric and asymmetric stretching vibrations [4] because of the methylene and methyl group at 2923 cm−1 and 2852 cm−1. The bending vibration due to C–N at 1071 cm−1 is broadened in case of OLA with CZTS. In CZTS sample a strong band at 605 cm−1 is observed which corresponds to metal nitrogen stretching mode [5]. Over all, from the FTIR data analysis, co-ordination of OLA with CZTS nanocrystals is confirmed. Fig. 2(B) shows the similar bands in case of rest all the composition.

Fig. 2

(A) FTIR spectra recorded on oleylamine (OLA) and CZTS nanocrystals. Inset shows the expanded region of the amine stretching and metals nitrogen bond characteristic stretching bands. (B) FTIR spectra for CZTSSe1− nanocrystals with varied composition.

Morphological, topological analysis of CZTSSe1− nanocrystals by TEM, AFM and FESEM

Fig. 3 shows the TEM micrographs for the CZTSSe1− alloy nanocrystals for varied composition. Fig. 3(A) and (D) represents the low resolution and high resolution images for x=0.17 respectively, Fig. 3(B) and (E) represent the low and high resolution images for x=0.42 respectively, Fig. 3(C) and (F) represents the low and high resolution images for x=0.74 respectively. The TEM images for the x=1 and x=0 are shown in [1]. For all compositions faceted morphology with polyhedron shapes having size ranging from 10 to 30 nm are observed.

Fig. 3

Low resolution TEM images recorded on CZTSSe1− nanocrystals for varied composition. (A) x=0.17,(B) x=0.42, (C) x=0.74 and corresponding high resolution TEM images (D)–(F) respectively.

Stoichiometry/composition and elemental distribution of CZTSSe1− nanocrystals by EDAX spectra and elemental mapping

Fig. 4(A–E) shows the AFM images recorded on CZTSSe1−nanocrystals for x=0–1. (A) x=1 (B) x=0.74, (C) x=0.42, (D) x=0.17 and (E) x=0. In the AFM images, the faceted and nearly spherical nanocrystals are observed. The average height for all the CZTSSe1− nanocrystals is in the range of 20 nm, suggesting the uniform topology. The size distributions are in the range of 20–30 nm.

Fig. 4

AFM images recorded on CZTSxSe1-x nanocrystals dispersion dropcasted on silicon wafer for x=0–1. (A) x=1 (B) x=0.74, (C) x=0.42, (D) x=0.17 and (E) x=0.

Fig. 5(A–E) shows the FESEM micrographs recorded on CZTSSe1− nanocrystals for x=0–1. (A) x=1 (B) x=0.74, (C) x=0.42, (D) x=0.17 and (E) x=0. The Fig. 5(A) and (E) show the mono-disperse nanocrystals spread over the silicon substrate. While Fig. 5(C)–(E) shows the poly disperse nature of nanocrystals. From the FESEM images, the size distributions were in the range of 10–30 nm and it matches very well with the size estimated from the TEM and AFM.

Fig. 5

FESEM images recorded on CZTSSe1− nanocrystals dispersion dropcasted on silicon wafer, for x=0–1. (A) x=1 (B) x=0.74, (C) x=0.42, (D) x=0.17 and (E) x=0.

Fig. 6(A–E) shows the EDAX spectrum recorded on CZTSSe1− nanocrystals for x=0–1. (A) x=1 (B) x=0.74, (C) x=0.42, (D) x=0.17 and (E) x=0. From all the EDAX spectra, the compositions were estimated [1]. It shows good agreement between the ratios of precursor used in the synthesis and compositions estimated from EDAX. The distribution of elements in all the samples are measured by EDAX based elemental mapping. It is presented in Fig. 7(A–E). The inset of Fig. 7(A–E) shows the bar chart for stoichiometry as element vs. atomic % (stoichiometry). Mapping data underlines uniform stoichiometric distribution in the samples.

Fig. 6

(A–E) EDAX Spectra recorded on CZTSSe1−nanocrystals for x=0–1. (A) x=1, (B) x=0.74, (C) x=0.42, (D) x=0.17 and (E) x=0. The inset shows the elemental distribution table obtained from EDAX.

Fig. 7

(A–E) shows the elemental mapping images for CZTSSe1− alloys with ‘x’ ranging from 1 to 0. The insets show bar charts for stoichiometry.

Table 1 summarizes the data for optical band gaps form UV–Visible spectroscopy and electrochemical band gaps from cyclic voltammetry. From the voltammetric measurement the band edge parameters viz. valance band and conduction band edge were estimated vs. NHE and local vacuum respectively. Along with band edge parameters the crystals structure parameters like lattice constants and d-spacing calculated from X-ray diffraction pattern also presented in Table 1.

Table 1

The optical band gap, electrochemical band gap with band edge positions vs. NHE. local vacuum and lattice constants as a function of composition for CZTSSe1− alloy nanocrystals.

Sr. no	Nanocrystal composition	Optical band gap(εgapop)eV	Electrochemical band gap(εgapec)	EVBVs. vacuum (V)	ECBVs. vacuum (V)	EoxVs. NHE (eV)	EredVs. NHE (eV)	Lattice constant ‘a’ (Å)	Lattice constant ‘c’ (Å)	d112spacing (Å)
1	CZTSxSe1−x(x=1)	1.50	1.55	−5.49	−3.94	0.99	−0.56	5.4300	10.6900	3.1304
2	CZTSxSe1−x(x=0.74)	1.40	1.48	−5.33	−3.85	0.85	−0.65	5.5200	10.9500	3.1841
3	CZTSxSe1−x(x=0.42)	1.32	1.39	−5.44	−4.05	0.96	−0.45	5.5800	11.1200	3.2281
4	CZTSxSe1−x(x=0.17)	1.24	1.16	−5.46	−4.3	0.94	−0.20	5.6100	11.2500	3.2594
5	CZTSxSe1−x(x=0)	1.16	1.08	−5.55	−4.47	1.05	−0.03	5.6890	11.3400	3.2818

Subject area	Chemistry
More specific subject area	Materials Chemistry/Electrochemistry
Type of data	Table, figure, images
How data was acquired	Instruments used- Bruker FTIR-ATR, Tensor-37 Spectrometer with a diamond ATR attachment, FESEM- FEI make Nova NanoSEM 450 FESEM with EDAX using Bruker XFlash 6I30. TEM-Philips CM200 TEM 200 kV, AFM- Bruker, Multimode 8.0.
Data format	Analyzed
Experimental factors	CZTSxSe1−x(x=0–1) Nanocrystals with varied composition have been synthesized by hot injection method. These were characterized by FTIR, TEM, FESEM, AFM and EDAX analysis. Band edge parameters have been estimated by cyclic voltammetry.
Experimental features	The modified electrodes for the voltammetry measurements have been prepared by drop-casting the dispersion of samples. Cyclic Voltammetry measurements have been carried out in non-aqueous solvents under inert atmosphere.
Data source location	Savitribai Phule Pune University, Pune, Maharashtra, India
Data accessibility	Data is supplied with in this article