A reduced graphene oxide-based fluorescence resonance energy transfer sensor for highly sensitive detection of matrix metalloproteinase 2.

A novel fluorescence nanoprobe (reduced nano-graphene oxide [nrGO]/fluorescein isothiocyanate-labeled peptide [Pep-FITC]) for ultrasensitive detection of matrix metalloproteinase 2 (MMP2) has been developed by engineering the Pep-FITC comprising the specific MMP2 substrate domain (PLGVR) onto the surface of nrGO particles through non-covalent linkage. The nrGO was obtained by water bathing nano-graphene oxide under 90°C for 4 hours. After mixing the nrGO and Pep-FITC for 30 seconds, the fluorescence from Pep-FITC was almost completely quenched due to the fluorescence resonance energy transfer between fluorescein isothiocyanate (FITC) and nrGO. Upon cleavage of the amide bond between Leu and Gly in the Pep-FITC by protease-MMP2, the FITC bound to nrGO was separated from nrGO surface, disrupting the fluorescence resonance energy transfer process and resulting in fluorescence recovery of FITC. Under optimal conditions, the fluorescence recovery of nrGO/Pep-FITC was found to be directly proportional to the concentration of MMP2 within 0.02-0.1 nM. The detection limit of the nrGO/Pep-FITC was determined to be 3 pM, which is approximately tenfold lower than that of the unreduced carboxylated nano-graphene oxide/Pep-FITC probe.

Introduction

Matrix metalloproteinases (MMPs) are a family of zinc-dependent endoproteases capable of degrading virtually all kinds of extracellular matrix and basement membrane components.1 MMPs target substrates, including proteinases, proteinase inhibitors, clotting factors, cell–cell adhesion molecules, chemotactic molecules, latent growth factors, growth factor-binding proteins, and cell surface receptors.2 MMPs were also found to interfere with the induction of apoptosis in malignant cells, especially after chemotherapy, by cleaving Fas ligand from the surface of cancer cells with MMP7.3 Tumors are highly vascularized tissues, and the formation of new blood vessels can be triggered by the release of vascular endothelial growth factor that is mainly facilitated by MMP2 and MMP9.4 In addition, degradation of extracellular matrix components and other extracellular molecules by MMPs may generate fragments with new bioactivities inhibiting angiogenesis.5 For example, it was reported that degradation of plasminogen by MMP2, MMP9, and MMP12 produced significant amounts of angiostatin, a cleavage product with antiangiogenic function.6,7

Sensitive, rapid, and accurate detection of MMPs is of great significance for clinical disease diagnosis, therapy, and MMP inhibitors screening. High levels of MMPs have been observed in the serum/blood,8,9 saliva,10 and urine11 of patients with cancers, and in the plasma of patients with diabetes12 or hypertensions.13 Gelatin zymography is a qualitative MMPs detection method.14 Enzyme-linked immunosorbent assay, a conventional and most widely used method in clinical assay, is very sensitive, but the antibody proteins are expensive and difficult to be acquired. In addition, enzyme-linked immunosorbent assay method needs tedious separation operations with at least 5 hours to detect the activity of MMPs.15 Fluorescence resonance energy transfer (FRET) refers to the energy transfer between donor and acceptor fluorophores within 1–10 nm distance range, and the rate of this long-range resonance energy transfer was suggested to have a (distance)−6 dependence.16 Therefore, many FRET-based sensors have been developed for sensitive and rapid detection of MMPs17,18 and other trace molecules.19

Graphene oxide (GO), a novel one-atom-thick two-dimensional carbon material, has been demonstrated to be a remarkable FRET acceptor for various fluorescent dyes owing to the excellent ability for absorbing visible light.19–22 Many kinds of GO-based FRET sensors have been developed for sensitive MMP2 detection.23–25 Reduced graphene oxide (rGO) is a more effective quencher due to the higher ability to absorb visible light over GO.26–28 There are many ways to prepare rGO by using strong alkaline, alcohols, natural extracts, or overheated supercritical water in sealed container as reductant.29–32 We recently bathed covalently PEGylated nano-graphene oxide (nGO-PEG, here “PEG” means polyethylene glycol) in pure water under 90°C for 24 hours to obtain the reduced nGO-PEG that had an ~7.6-fold increment in near-infrared (NIR) absorption at 808 nm over nGO-PEG and was stable for >3 months under 4°C.33,34

In this study, we developed a reduced nano-graphene oxide (nrGO)-based FRET sensor (nrGO/fluorescein isothiocyanate-labeled peptide [Pep-FITC]) for highly sensitive MMP2 detection. As illustrated in Figure 1, the functionalized nrGO/Pep-FITC sensor was prepared by non-covalent binding of Pep-FITC (H2N-PEG-CALNNGPLGVRGRAK-FITC) containing the core cleavage substrate sequence (PLGVR) of MMP225 to nrGO that was reduced by bathing carboxylated nano-graphene oxide (c-nGO) in water at 90°C for 4 hours. The nrGO/Pep-FITC sensor was able to quantitatively detect the concentration of MMP2 in the range of 0.02–0.1 nM. The detection limit of the nrGO/Pep-FITC was determined to be 3 pM, which is approximately tenfold lower than that of the c-nGO/Pep-FITC probe. To the best of our knowledge, this is the first report on an nrGO-based biosensing platform for analyzing MMP2.

Figure 1

Strategy of nrGO/Pep-FITC probe for MMP2 detection.

Notes: Blue arrows indicate 480 nm excitation light, green arrows indicate 518 nm emission fluorescence.

Abbreviations: nrGO, reduced nano-graphene oxide; Pep-FITC, fluorescein isothiocyanate-labeled peptide; MMP2, matrix metalloproteinase 2; GO, graphene oxide; nGO, nano-graphene oxide; c-nGO, carboxylated nano-graphene oxide; PEG, polyethylene glycol; FITC, fluorescein isothiocyanate.

Materials and methods

Chemicals and materials

Pep-FITC (H2N-PEG-CALNNGPLGVRGRAK-FITC) was synthesized by Shanghai ABBiochem Co, Ltd (Shanghai, People’s Republic of China). Graphite powder was purchased from Nanjing XFNano Materials Tech Co, Ltd (Nanjing, People’s Republic of China). Latent proMMP2 was purchased from Sino Biological Inc Co, Ltd (Beijing, People’s Republic of China). 4-Aminophenylmercuric acetate (APMA), 1,10-phenanthroline, and dimethyl sulfoxide were purchased from Sigma-Aldrich (St Louis, MO, USA). Other reagents employed were all of analytical grade, and were used without further purification. All the buffers were prepared with tri-distilled water, which was purified with a water purification system (ELGA; High Wycombe, Bucks, UK) to a specific resistance of 18.2 MΩ⋅cm.

Synthesis of c-nGO and nrGO

GO was prepared by a modified Hummer’s method utilizing expandable graphite flake.35,36 GO was sonicated with Ultrasonic Cell Crusher (JY92-2D; Xinzhi Ultrasonic Equipment Co, Ningbo, People’s Republic of China) for 1.5 hours to give a clear solution in an ice bath to obtain nano-graphene oxide (nGO) suspension. c-nGO was obtained by the reaction with NaOH (1.2 g) and ClCH2COOH (1 g) for 0.5 hour following the known procedure.37

c-nGO solution (~1 mg/mL) was transferred to a sealed glass bottle and then bathed at 90°C for 4 or 12 hours to get nrGO (nrGO [4 h] or nrGO [12 h]).

Characterizations

The hydrodynamic diameters and ζ-potentials of nGO, c-nGO, nrGO (4 h), and nrGO (12 h) were measured by Zetasizer Nano ZS (Malvern Instruments Ltd, Malvern, UK). The materials were imaged with tapping mode atomic force microscope (OLTESPA probe, Bruker Dimension Icon; Bruker, Ettlingen, Germany) on a mica substrate. The images of all samples were recorded using a digital camera (Nikon, Tokyo, Japan) with 1,280×1,280 pixels resolution. Ultraviolet–visible (UV–vis) spectra were obtained by a UV–vis spectrometer (Lambda 35; PerkinElmer, Waltham, MA, USA) with a 1 cm quartz cuvette. Fourier transfer infrared (FTIR) spectra were recorded on a Nicolet 6700 FTIR spectrometer (Thermo Fisher Scientific, Waltham, MA, USA). Raman spectra were taken with a Renishaw (Wotton-under-Edge, UK) inVia micro-Raman spectroscopy system equipped with a 514.5 nm Ar+ laser. X-ray diffraction spectra were obtained using a D8 ADVANCE (Bruker) using Cu Kα (1.5406 Å) radiation. Luminescence Spectrometer (LS 55; PerkinElmer) was used to measure fluorescence emission. The excitation wavelength and emission wavelength were 480 and 518 nm, respectively. Both the excitation and emission slits were set at 10 nm.

Preparation of c-nGO/Pep-FITC and nrGO/Pep-FITC sensors

Unless otherwise noted, nrGO/Pep-FITC sensor was prepared by treating the Pep-FITC (100 nM) with nrGO (1 μg/mL) in the TCNB (50 mM Tris, 10 mM CaCl2, 150 mM NaCl, and 0.05% Brij 35; pH 7.5) buffer. c-nGO/Pep-FITC was prepared as described for the nrGO/Pep-FITC.

Detection of MMP2 with c-nGO/Pep-FITC and nrGO/Pep-FITC sensors

Before detection, latent proMMP2 was first activated with APMA according to the known procedure.38 MMP2 in TCNB buffer was added with 1 mM APMA (final concentration), and the mixture was incubated in heating thermostat blender (LTH-100; Shanghai LNB Instrument Co, Ltd, Shanghai, People’s Republic of China) at 37°C for 1 hour with gentle shaking.

In an Eppendorf tube loaded with 100 nM c-nGO/Pep-FITC or nrGO/Pep-FITC (final concentration), 1 μg/mL of activated MMP2 was added, and the mixtures were incubated at 37°C with gentle shaking for 2 hours, and fluorescence intensity of each sample was then recorded with λex/em =480/518 nm.

Results and discussion

Preparation and characterization of nrGO

The hydrodynamic sizes of nGO, c-nGO, nrGO (4 h), and nrGO (12 h) nanoparticles were firstly analyzed by dynamic light scattering (DLS). In order to assess the effect of bathing time on GO reduction degree, we bathed GO under 90°C for 4 and 12 hours. As shown in Figure 2A, the DLS hydrodynamic diameter of nGO, c-nGO, nrGO (4 h), and nrGO (12 h) was holding ~50, 50, 50, and 120 nm, respectively, during 1 month. We next used atomic force microscopy (AFM) images to further measure the diameters of the nGO, c-nGO, nrGO (4 h), and nrGO (12 h) nanoparticles. AFM data showed sheets of ~80 nm diameter (assuming that these are in round shape) for nGO, c-nGO, nrGO (4 h), and nrGO (12 h), and the sheet thickness of nGO, c-nGO, nrGO (4 h), and nrGO (12 h) waŝ1.5 nm (Figure 2B and C). Difference between AFM size and DLS hydrodynamic size may be due to the sheet-like structures of GO and rGO.

Figure 2

Size of nano-materials.

Notes: Hydrodynamic diameters (A), AFM images (B), Diameter and thickness (C) (data corresponds to the lines in figure [B]) of nGO, c-nGO, nrGO (4 h), and nrGO (12 h). nrGO (4 h) and nrGO (12 h) were formed by bathing nGO under 90°C water for 4 and 12 hours, respectively. The materials were stored under 4°C.

Abbreviations: AFM, atomic force microscopy; nGO, nano-graphene oxide; c-nGO, carboxylated nano-graphene oxide; nrGO, reduced nano-graphene oxide; h, hours.

It is well known that the edges of nGO or/and some parts of its basal plane are terminated by hydrogen, hydroxyl, carboxylic, and epoxy groups.39 Reduction reaction is unable to remove all oxygen groups of nGO, and the residual negatively charged oxygen functional groups allow nrGO solution to be dispersed well in water due to electrostatic repulsion mechanism,40,41 which may be the reason why the sizes of nrGO remain stable during 1 month at 4°C (Figure 2A). This view was further confirmed by the stable ζ-potential values (~−40 mV) of the nGO, c-nGO, nrGO (4 h), and nrGO (12 h) during 1 month (Figure 3A). The stable diameter and ζ-potential demonstrated that the nGO, c-nGO, nrGO (4 h), and nrGO (12 h) solutions were very stable at 4°C during at least a month, which was also further verified by the stable images of nGO, c-nGO, nrGO (4 h), and nrGO (12 h) (Figure 3B). The suspension remained clear under the same conditions. Moreover, the color of nGO, c-nGO, nrGO (4 h), and nrGO (12 h) solutions changed from brown to yellowish brown, dark brown, and black brown (Figure 3B), an evidence for the reduction of nGO. Furthermore, UV–vis spectrometer was used to detect the UV–vis spectra of nGO, c-nGO, nrGO (4 h), and nrGO (12 h). As shown in Figure 3C, nGO had a strong optical absorption peak at 228 nm and a weak shoulder at 300 nm. Compared with nGO, c-nGO exhibited higher absorbance at long wavelength (>300 nm), probably due to the partial and slight reduction of nGO under strong alkaline conditions.29 Compared with c-nGO, nrGO (4 h) and nrGO (12 h) exhibited ~4.29- and 6.88-fold increment in NIR absorption at 808 nm (Figure 3C), which further verified the degree of reduction. Moreover, the absorption peak (226.5 nm) of c-nGO corresponding to π→π* transitions of aromatic C=C bonds red-shifted to ~235.5 and 249.5 nm for nrGO (4 h) and nrGO (12 h), respectively, and the shoulder peak (300 nm) nearly disappeared for both nrGO (4 h) and nrGO (12 h), indicating partial restoration of the π-conjugation network of GO carbon structure and the effect of deoxygenation.42

Figure 3

Characterizations of nano-materials.

Notes: Zeta potentials (A), photographs (B), UV–vis absorption spectra (C), FTIR spectra (D), XRD patterns (E), and Raman spectra (F) of nGO, c-nGO, nrGO (4 h), and nrGO (12 h). nrGO (4 h) and nrGO (12 h) were formed by bathing nGO under 90°C water for 4 and 12 hours, respectively.

Abbreviations: FTIR, Fourier transform infrared; XRD, X-ray diffraction; nGO, nano-graphene oxide; c-nGO, carboxylated nano-graphene oxide; nrGO, reduced nano-graphene oxide; au, arbitrary unit; UV-vis, ultraviolet–visible; ID/IG, the intensity ratio of D band to G band in Raman spectra; h, hours.

FTIR spectroscopy revealed the existence of OH (~3,400 cm−1), C=O (~1,720 cm−1), C=C (~1,620 cm−1), C–OH (~1,380 cm−1), and C–O (~1,060 cm−1) functional groups in the nGO (Figure 3D),43 which indicated that the abundant oxygen-containing moieties were present on nGO surfaces. We activated nGO sample with chloroacetic acid under strongly basic conditions in order to activate epoxide and ester groups, and to convert hydroxyl groups to carboxylic acid moieties.44 This c-nGO having good water solubility and more carboxylic acid groups exhibited the characteristic peak of ~1,600 cm−1 for carboxyl groups (–COO−).25 After water-bathing treatment, the FTIR spectra of nrGO (4h) and nrGO (12h) were similar to that of c-nGO, indicating similar structure of the reduced graphene material with the c-nGO.

As shown in the X-ray diffraction patterns (Figure 3E), the d-spacing of sharp feature peak (001) was 1.01 nm (at 8.74°) for nGO, 0.89 nm (at 9.84°) for c-nGO, 0.86 nm (at 10.25°) for nrGO (4 h), and disappeared for nrGO (12 h), which indicated that most of the oxygen functional groups, having marked effects on the d-spacing, had been reduced in this condition. The d-spacing of sharp feature peak (002) was 0.48 nm (at 18.22°) for nGO, 0.39 nm (at 22.46°) for c-nGO, 0.37 nm (at 23.40°) for nrGO (4 h), and 0.36 nm (at 24.38°) for nrGO (12 h), further confirming the gradual reduction of c-nGO with increasing water bath-treated times at 90°C.45

Raman spectroscopy was used to characterize nGO, c-nGO, nrGO (4 h), or nrGO (12 h) (Figure 3F). The typical features in Raman spectra are the G band at 1,600 cm−1 and the D band at 1,350 cm−1. The G band is usually assigned to the E2g phonon of C sp2 atoms, while the prominent D band is an indication of disorder corresponding to defects associated with vacancies, grain boundaries, and amorphous carbon species.34 The intensity ratio (ID/IG) of D band to G band was ~0.812 for nGO, 0.888 for c-nGO, 0.849 for nrGO (4 h), and 0.817 for nrGO (12 h). Compared with nGO, c-nGO had larger ID/IG value. However, the ID/IG value of nrGO (4 h) or nrGO (12 h) was lower than that of c-nGO, suggesting that the reduction reaction in this facile and green reduction strategy developed here was able to recover the aromatic structures by repairing defects.

Preparation and optimization of nrGO/Pep-FITC sensors

nrGO/Pep-FITC sensor was prepared by treating Pep-FITC (100 nM) with nrGO (1 μg/mL) in TCNB buffer, and c-nGO/Pep-FITC served as a control. The binding of biomolecules to GO is generally through π–π and electrostatic interactions,46 and thus, the electrically charged nature of c-nGO and nrGO needs to be examined. As shown in Figure 3B, the ζ-potential values of the c-nGO, nrGO (4 h), and nrGO (12 h) were ~−40 mV, indicating that c-nGO, nrGO (4 h), and nrGO (12 h) were negatively charged. The pI value of our peptide calculated by ProtParam47 was 11.3, so the peptide (Pep-FITC) would be positively charged at physiological pH of ~7.24 In addition, the left side of the peptide chain was linked with PEG-NH2, which was more conducive to the formation of the probes. In order to optimize the amount of nrGO or c-nGO as nanoquencher, different volumes of c-nGO, nrGO (4 h), or nrGO (12 h) solution (0.1 mg/mL) were mixed with Pep-FITC (100 nM) in TCNB buffer, and the fluorescence intensity of the solution was measured after incubation for 10 minutes. We found that the fluorescence-quenching efficiency (QE [%] =100× [1−β], where β is the ratio of fluorescence of the quenched-to-completely dequenched state) of Pep-FITC gradually increased along with the increasing concentration of c-nGO, nrGO (4 h), and nrGO (12 h), and the QE value was 72.82%, 90.18%, and 92.91% for 1 μg/mL of c-nGO, nrGO (4 h), and nrGO (12 h), respectively (Figure 4A). The higher QE of nrGO over the unreduced c-nGO is due to the higher ability of nrGO to absorb visible light. Compared with c-nGO, nrGO showed a significant increment in NIR absorption (Figure 3C), leading to a bigger overlap area between the absorption spectrum of nrGO, the acceptor here, and the emission spectrum of the donor-FITC, and increasing the fluorescence-quenching efficiency of nrGO. Since there was no significant difference in the fluorescence-quenching ability between nrGO (12 h) and nrGO (4 h) (Figure 4A), we chose nrGO (4 h) as nrGO for following test without indication.

Figure 4

Quenching effect of nano-materials.

Notes: Dose-dependent quenching efficiencies (QE) (A) of c-nGO, nrGO (4 h), and nrGO (12 h) on Pep-FITC (100 nM) and time-dependent fluorescence quenching (B) of Pep-FITC (100 nM) in TCNB buffer with 1 μg/mL c-nGO (a), nrGO (4 h) (b), and nrGO (12 h) (c).

Abbreviations: c-nGO, carboxylated nano-graphene oxide; nrGO, reduced nano-graphene oxide; Pep-FITC, fluorescein isothiocyanate-labeled peptide; TCNB, Tris (50 mM), CaCl2 (10 mM), NaCl (150 mM), and Brij 35 (0.05%) (pH 7.5); FL, fluorescence; au, arbitrary unit; min, minutes; h, hours.

We next investigated time dependence of the fluorescence quenching between nrGO and Pep-FITC. The fluorescence intensity (λex/em =480/518 nm) of nanoprobes during preparation was monitored as a function of time using microplate reader (Infinite M200; Tecan, Männedorf, Switzerland). The fluorescence quenching of Pep-FITC by nrGO was very fast (<30 seconds) after adding nrGO (1 mg/mL) to the Pep-FITC solution (100 nM), and the quenched fluorescence remained quite stable thereafter (Figure 4B), indicating that the binding equilibrium between nrGO and Pep-FITC was achieved immediately, ensuring a constant background for the subsequent MMP2 sensing.

Detection of MMP2 using nrGO/Pep-FITC sensor

We first examined the principle of nrGO/Pep-FITC for MMP2 detection. The fluorescence spectrum of c-nGO/Pep-FITC sensors (100 nM) after adding the target MMP2, activated with APMA according to the known procedure,38 was obviously enhanced (Figure 5, curve b compared with curve a). However, the enhanced fluorescence spectrum of c-nGO/Pep-FITC sensors after adding the mixture of MMP2 (1.4 nM) and 10 μM 1,10-phenanthroline, a broad-spectrum inhibitor of MMPs, was largely abolished (Figure 5, curve d compared with b), indicating that the MMPs inhibitor inhibited MMP2 activation largely. We further assessed the effect of the inhibitor on the fluorescence intensity, and found that there was hardly any change in the fluorescence intensity of c-nGO/Pep-FITC (Figure 5, curve a and c) or free Pep-FITC (Figure 6) before and after adding the inhibitor, suggesting that the inhibitor had no direct effect on the fluorescence intensity of the sensor or free FITC. These data demonstrated that fluorescence recovery of the c-nGO/Pep-FITC sensor in the presence of MMP2 was due to the cleavage of the peptide by the activated MMP2.

Figure 5

Fluorescence spectra of different reaction systems.

Notes: c-nGO/Pep-FITC (100 nM) (a); (a) + MMP2 (1.4 nM) (b); (a) + 1,10-phenanthroline (10 μM) (c), and (a) +1,10-phenanthroline (10 μM) + MMP2 (1.4 nM) (d).

Abbreviations: c-nGO, carboxylated nano-graphene oxide; Pep-FITC, fluorescein isothiocyanate-labeled peptide; MMP2, matrix metalloproteinase 2; FL, fluorescence; au, arbitrary unit.

Figure 6

Effect of additional MMP2 inhibitor (1,10-phenanthroline) on the FITC fluorescence intensity.

Notes: Pep-FITC (100 nM) (a) and Pep-FITC (100 nM) +1,10-phenanthroline (10 μM) (b).

Abbreviations: MMP2, matrix metalloproteinase 2; FITC, fluorescein isothiocyanate; Pep-FITC, fluorescein isothiocyanate-labeled peptide; FL, fluorescence; au, arbitrary unit.

Before we applied the nrGO/Pep-FITC sensor to detect the protease activities of MMP2, the reaction time for the detecting system was optimized. After adding MMP2 (0.28 nM), the fluorescence intensity of nrGO/Pep-FITC sensor (100 nM) increased gradually along with the cleavage time until it reached a plateau at 2 hours under 37°C in TCNB buffer (Figure 7). We thus chose 2 hours for the following detection.

Figure 7

Time optimization of probes for MMP2 detection.

Notes: Effect of reaction time on the fluorescence change of the c-nGO/Pep-FITC (a) and nrGO/Pep-FITC (b) probes (100 nM) reacting with MMP2 (0.28 nM) in TCNB buffer at 37°C.

Abbreviations: c-nGO, carboxylated nano-graphene oxide; Pep-FITC, fluorescein isothiocyanate-labeled peptide; nrGO, reduced nano-graphene oxide; MMP2, matrix metalloproteinase 2; TCNB, Tris (50 mM), CaCl2 (10 mM), NaCl (150 mM), and Brij 35 (0.05%) (pH 7.5); ΔF, changeable fluorescence intensity; au, arbitrary unit; h, hours.

After mixing 100 nM nrGO/Pep-FITC with MMP2 at 37°C for 2 hours with gentle shaking, we detected the enhanced fluorescence intensity ΔF (ΔF = F−F0, where F and F0 stand for the fluorescence intensity of nrGO/Pep-FITC sensor after and before reacting with MMP2, respectively) of nrGO/Pep-FITC sensor in the presence of various concentrations (0–1.4 nM) of MMP2. As shown in Figure 8A, the fluorescence recovery of FITC was dependent on the concentration of MMP2 introduced. Moreover, the enhanced fluorescence intensity ΔF was linearly correlated with the MMP2 concentration in the range of 0.02–0.1 nM (inset in Figure 8A). The detection limit (3S/m, in which S is the standard deviation of blank measurements, n=10, and m is the slope of the linear equation)24 of the nrGO/Pep-FITC was determined to be 3 pM, which is approximately tenfold lower than that of the c-nGO/Pep-FITC probe (Figure 8B), attributing to the higher ability of nrGO to absorb visible light (Figure 3C). The 3 pM detection limit of nrGO/Pep-FITC for MMP2 is at least elevenfold lower than that of the GO-Pep-FITC sensor developed by Song et al25 as well as 16-fold lower than that of the GO-peptide sensor developed by Feng et al.24

Figure 8

Linear concentration range of probes for MMP2 detection.

Notes: The changed fluorescence intensity of nrGO/Pep-FITC (A) and c-nGO/Pep-FITC (B) probes (100 nM) versus MMP2 concentration. The insets at the bottom right indicate the linear regression of the enhanced fluorescence intensity (ΔF, at 518 nm) versus the concentration of MMP2. Linear detection range is indicated by dotted rectangle.

Abbreviations: nrGO, reduced nano-graphene oxide; Pep-FITC, fluorescein isothiocyanate-labeled peptide; c-nGO, carboxylated nano-graphene oxide; MMP2, matrix metalloproteinase 2; ΔF, changeable fluorescence intensity; au, arbitrary unit.

To test the selectivity, the reaction of the nrGO/Pep-FITC (100 nM) with KCl (150 mM), MgCl2 (2.5 mM), ZnCl2 (2.5 mM), glucose (10 mM), glycine (1 mM), glutamine (1 mM), bovine serum albumin (100 nM), human serum albumin (100 nM), MMM9 (another member of MMPs, 2 nM), and MMP2 (2 nM) was examined in parallel under the same conditions (incubated at 37°C for 2 hours). As shown in Figure 9, the nrGO/Pep-FITC sensor exhibited the strongest fluorescence response to 2 nM of MMP2 and very weak fluorescence response to 2 nM of MMP9, and did not show obvious response to KCl, MgCl2, ZnCl2, glucose, glycine, glutamine, bovine serum albumin, and human serum albumin even with micromole-level concentrations. These data clearly indicate that the nrGO/Pep-FITC sensor possesses a high specificity for MMP2, which is ascribed to the cleavage of the specific substrate by MMP2.

Figure 9

Fluorescence responses of the nrGO/Pep-FITC (100 nM) to various substances: KCl (150 mM), MgCl2 (2.5 mM), ZnCl2 (2.5 mM), glucose (10 mM), glycine (1 mM), glutamine (1 mM), BSA (100 nM), HSA (100 nM), MMP9 (2 nM), and MMP2 (2 nM).

Notes: ΔF is the difference of the fluorescence intensity of nrGO/Pep-FITC in the presence and absence of a substance.

Abbreviations: nrGO, reduced nano-graphene oxide; Pep-FITC, fluorescein isothiocyanate-labeled peptide; BSA, bovine serum albumin; HSA, human serum albumin; MMP9, matrix metalloproteinase 9; MMP2, matrix metalloproteinase 2.

Based on the powerful light quenching of rGO, we here devoted ourselves to develop the nrGO/Pep-FITC sensor for rapid and ultrasensitive measurement of MMP2. In fact, the nrGO/Pep-FITC sensor can also be used to monitor the trace amount of other proteases and protease inhibitors by changing polypeptide chain. For example, the expression of MMP10 in healthy human plasma is commonlŷ0.03 nM,13 and the levels of MMPs in urine and saliva are much lower than that in plasma.48,49 We can replace the MMP2 cleavage substrate in the Pep-FITC with MMP10 cleavage substrate for the sensitive MMP10 detection. In reality, the nrGO/Pep-FITC sensor tends to be destroyed when other similar molecules competitively bind with nrGO, limiting its practical application in complex biological samples, which is a key issue to be overcome in the near future.

Conclusion

In summary, a novel nrGO/Pep-FITC sensor for sensitive, rapid, and accurate analysis of a protease biomarker (MMP2) has been developed through non-covalent binding of Pep-FITC to nrGO. Compared with the unreduced c-nGO/Pep-FITC, nrGO/Pep-FITC developed here has lower background signals and a tenfold lower detection limit for MMP2. Attributed to the simple preparation and facile manipulation, we envision that this work may inspire many people to develop multifunctional rGO-based biosensor platforms for the ultrasensitive detection of trace elements by functionalizing rGO with many kinds of functional probes and expand the application fields of rGO-based sensor.