Self-assembled lecithin/chitosan nanoparticles for oral insulin delivery: preparation and functional evaluation.

PURPOSE: Here, we investigated the formation and functional properties of self-assembled lecithin/chitosan nanoparticles (L/C NPs) loaded with insulin following insulin-phospholipid complex preparation, with the aim of developing a method for oral insulin delivery.
METHODS: Using a modified solvent-injection method, insulin-loaded L/C NPs were obtained by combining insulin-phospholipid complexes with L/C NPs. The nanoparticle size distribution was determined by dynamic light scattering, and morphologies were analyzed by cryogenic transmission electron microscopy. Fourier transform infrared spectroscopy analysis was used to disclose the molecular mechanism of prepared insulin-loaded L/C NPs. Fast ultrafiltration and a reversed-phase high-performance liquid chromatography assay were used to separate free insulin from insulin entrapped in the L/C NPs, as well as to measure the insulin-entrapment and drug-loading efficiencies. The in vitro release profile was obtained, and in vivo hypoglycemic effects were evaluated in streptozotocin-induced diabetic rats.
RESULTS: Our results indicated that insulin-containing L/C NPs had a mean size of 180 nm, an insulin-entrapment efficiency of 94%, and an insulin-loading efficiency of 4.5%. Cryogenic transmission electron microscopy observations of insulin-loaded L/C NPs revealed multilamellar structures with a hollow core, encircled by several bilayers. In vitro analysis revealed that insulin release from L/C NPs depended on the L/C ratio. Insulin-loaded L/C NPs orally administered to streptozotocin-induced diabetic rats exerted a significant hypoglycemic effect. The relative pharmacological bioavailability following oral administration of L/C NPs was 6.01%.
CONCLUSION: With the aid of phospholipid-complexation techniques, some hydrophilic peptides, such as insulin, can be successfully entrapped into L/C NPs, which could improve oral bioavailability, time-dependent release, and therapeutic activity.

Introduction

With the development of biotechnology, peptide-based pharmaceuticals have been introduced into clinical practice.1 Insulin, a major protein hormone secreted by pancreatic β-cells, plays a crucial role in the regulation of glucose metabolism and is used as a drug to control type-1 diabetes mellitus. Insulin is commonly administered by daily subcutaneous (sc) injections, leading to low patient compliance and unsatisfactory metabolic regulation.2 Oral insulin administration is more convenient, less invasive, and mimics physiological uptake via the hepatic route;3 therefore, various oral insulin-delivery systems such as liposomes,4 emulsions,5 microspheres,6 and polymer-based nanoparticles (NPs)7,8 have been developed. However, the bioavailability of orally administered insulin preparations is not satisfactory because of their inherent instabilities in the gastrointestinal tract and inefficient absorption due to low permeability across biological membranes.

Chitosan is a natural polycationic polymer with mucoadhesive properties, which can facilitate protein absorption in the intestinal tract through opening tight junctions between epithelial cells.9,10 Chitosan can be obtained from chitin by alkaline deacetylation and has been used to prepare NPs by the ionotropic method11 or the emulsification solvent-diffusion method.12 Significant progress has been achieved in synthesizing and purifying chitosan, as well as in applications of modified chitosan NPs for efficient oral insulin delivery.13,14 However, the above-mentioned methods have drawbacks, such as the requirement of chemical cross-linking agents and/or repeated washing and precipitation steps. Based on the development of the self-assembly technique, a novel self-assembled nanoparticulate system consisting of lecithin and chitosan was fabricated by the solvent-injection method.15 Through self-association, negatively charged phospholipids and positively charged chitosan formed stiff and stable nanostructures, which demonstrated good biocompatibility and biodegradability, excellent mucosal adhesiveness, and minimal cytotoxicity.16,17 This novel delivery system improved the bioavailability of model drugs and prolonged their retention times in the body. Several recent studies have investigated the efficiency of this novel nanocarrier in delivering various model drugs via different routes, including oral and transmucosal administration.18–21 However, it is believed that only hydrophobic molecules such as progesterone and natamycin can be entrapped into this self-assembled nanocarrier with high entrapment efficiency, whereas poor drug loading (DL) was observed for hydrophilic drugs.22

Insulin is a large, highly hydrophilic protein that cannot be loaded directly into chitosan–lecithin nanocarriers. However, results from a previous study demonstrated that insulin lipophilicity can be increased through chemical modifications or physical assemblage with phospholipids, which may facilitate its mucosal permeability and stability to enzymatic degradation.23 Because chemical modifications of high-molecular weight proteins often result in structural changes, insulin–phospholipid complexes are preferable.24 In our previous study, we developed a milder method to prepare insulin–phospholipid complexes with a high complexation rate of ~100%. Compared with insulin alone, the obtained insulin–phospholipid complexes had improved lipophilicity, and their solubility in n-octyl alcohol increased by >40,000-fold, while the biological activity of insulin was retained.25

In this study, we present a novel application of self-assembled lecithin/chitosan nanoparticles (L/C NPs) to entrap a hydrophilic therapeutic peptide with high molecular weight (insulin). We prepared insulin-loaded L/C NPs, which demonstrated high drug entrapment efficiency of phospholipid-complexed insulin. Insulin-entrapped L/C NPs were characterized in terms of their physicochemical properties, in vitro insulin release profile, and in vivo hypoglycemic effects in streptozotocin (STZ)-induced diabetic rats.

Materials and methods

Materials

Recombinant human insulin was purchased from Dongbao Enterprise Group Co. Ltd. (Jilin, People’s Republic of China), lecithin (70% phosphatidylcholine/30% phosphatidylethanolamine, Lipoid S75) was obtained from Shanghai Toshisun Biology & Technology Co. Ltd. (Shanghai, People’s Republic of China), chitosan (90%–95% deacetylated) was from Fluka (Buchs, Sweden), and STZ was from Sigma-Aldrich (St Louis, MO, USA). Phosphate buffer solution (PBS; pH 7.4, without calcium or magnesium, Hyclone) was from Thermo Scientific (Waltham, MA, USA). Other chemicals and solvents were of analytical or chromatography grade.

Animals

Male Sprague Dawley rats were purchased from the Experimental Animal Center of National Institutes for Food and Drug Control. All rats were raised in the Institute of Materia Medica, Chinese Academy of Medical Sciences & Peking Union Medical College (Beijing, People’s Republic of China). All of the experiments were performed with the approval of the Laboratory Animal Care and Use Committee of Peking Union Medical College.

Preparation of insulin–phospholipid complexes

The preparation of insulin–phospholipid complexes was performed as described previously.25 Briefly, insulin (10 mg) was dissolved in 0.1% trifluoroacetic acid–methanol (1 mL), and Lipoid S75 (100 mL) was dissolved in dichloromethane (10 mL). After mixing insulin and Lipoid S75 together, the organic solvents were removed by rotary evaporation in a vacuum. Nitrogen was then flushed into the flask to remove the organic solvents thoroughly, and the flask was left in the vacuum oven (37°C) overnight. On the following day, the resulting complex was stored at −20°C.

Preparation of insulin-loaded L/C NPs

Insulin-loaded L/C NPs were prepared using a modified solvent-injection method. Briefly, chitosan was dissolved in 1% (v/v) acetic acid to obtain a 1% (w/v) chitosan stock solution, which was used to prepare various dilutions in distilled water. Then, 8 mL of each insulin–phospholipid complex in ethanol (insulin–phospholipid complex concentration, 27.5 mg/mL, which contains 25 mg lecithin and 2.5 mg insulin in 1 mL liquid) was injected through a syringe needle (0.7 mm, inner diameter) into 92 mL of each chitosan dilution to achieve lecithin/chitosan (L/C) ratios ranging from 10:0 to 40:1 (w/w), and stirred to obtain drug-loaded L/C NPs.

For comparison purposes, insulin-free (empty) L/C NPs were fabricated by substituting insulin–phospholipid complexes with lecithin solution in ethanol using the same procedure. In addition, insulin-loaded S75 phospholipid vesicles were prepared by injecting insulin–lecithin complexes into distilled water.

Characterization of particle size, surface charge, and morphology

Dynamic light scattering (Nicomp 380 ZLS, Particle Size System; Santa Barbara, CA, USA) was used to measure the average particle size. Prior to analysis, samples were diluted in distilled water filtered through a 0.22 μm membrane to avoid multiple scattering. Measurements were performed at room temperature using a scattering angle of 90°. The zeta potential was determined by measuring the Doppler electrophoretic laser shift at 28°C and analyzing light scattering at −14°C, using a Nicomp 380 ZLS instrument. The morphology of prepared NPs and vesicles was evaluated by cryogenic transmission electron microscopy (TECNAI 20; Philips, Amsterdam, the Netherlands). NP suspensions were deposited on polycarbonate grids and rapidly cooled with liquid nitrogen; the obtained thin, vitrified aqueous films were used for morphological observations.

FT-IR analysis

Fourier transform infrared spectroscopy (FT-IR) analysis (Nicolet 5700; Thermo Electron Corporation, Waltham, MA, USA) was performed using lyophilized NPs to study whether insulin–phospholipid complexes dissociated during the preparation of insulin-loaded L/C NPs. Spectra were collected at 20°C in the scanning range of 4,000–400 cm−1.

Determination of insulin loading

The amount of total insulin in suspension was measured by dissolving NP suspensions in pH 7.4 PBS (without calcium or magnesium, Hyclone; Thermo Scientific). Briefly, 1% Triton X100 was added to 2 mL of NP suspension. Subsequently, the solution was adjusted to a volume of 10 mL by pH 7.4 PBS. Then, a reversed-phase high-performance liquid chromatography (RP-HPLC) assay was performed to measure the amount of insulin in the solvent.

The encapsulation efficiency (EE) of insulin-loaded L/C NPs was measured using a fast ultrafiltration method. Briefly, 1 mL of each prepared NP suspension was placed in a centrifugal filter tube (Amicon Ultra-4 centrifugal devices, 100K NMWL; Millipore, Billerica, MA, USA) and centrifuged at 4,000 rpm for 20 minutes to separate free and entrapped insulin in NPs. After ultrafiltration, the RP-HPLC assay was used to measure the amount of insulin in ultrafiltrates with Agilent Technologies 1200 series HPLC system (Agilent, Santa Clara, CA, USA) and a 300SB-C8 column (4.6×250 mm, 5 μm, Agilent). The following conditions according to the China Pharmacopeia (2010) were used – mobile phase: 0.1 M sulfate buffer/acetonitrile (73:27, v/v), flow rate: 1 mL/min, ultraviolet detection: 214 nm, injection volume: 20 μL, and column oven temperature: 40°C. Then, 0.1 M sulfate buffer containing 0.1 M sodium sulfate and trifluoroacetic acid was added to adjust the pH value to 2.3. Each sample was analyzed in triplicate.

L/C NP EE and DL efficiency were calculated according to the following equations:19 where Wtotal insulin is the total amount of insulin in NP suspension, Wfree insulin is the amount of insulin in the filtrate solvent, and Wtotal NPs is the amount of NPs measured after freeze-drying.

In vitro insulin release

The release profile of insulin from NPs was determined in PBS adjusted to pH 1.2 or pH 6.8, in the absence of added enzymes. In each case, 1.0 mL insulin-loaded L/C NP suspension (insulin concentration, 0.1 mg/mL) was transferred into a centrifugal filter tube and centrifuged at 4,000 rpm for 20 minutes. Next, the ultrafiltrate was collected and dispersed into 10 mL release medium (pH 1.2 or pH 6.8). In vitro drug-release tests were performed in a shaking water bath at 37°C and 50 rpm. At different time intervals, a 500 μL aliquot was withdrawn, centrifuged at 3,000 rpm for 20 minutes, and the supernatant containing free insulin was collected and measured using the RP-HPLC assay. Each experiment was performed in triplicate.

In vivo hypoglycemic effect of insulin-loaded L/C NPs

The pharmacological bioactivity of insulin delivered by orally administered L/C NPs was evaluated in diabetes-model rats by assessing the hypoglycemic effect. All animal experiments were performed in accordance with principles of laboratory animal care, and approved by the Institutional Animal Ethical Committee of Beijing (People’s Republic of China).

Before animal experiments were initiated, male Sprague Dawley rats were acclimated in an animal facility for 2 weeks. Diabetes was induced in rats with STZ (60 mg/kg in citrate buffer, pH 4.2), which was administrated by intraperitoneal injection. After blood glucose levels were stabilized for 1 week, STZ-induced diabetic rats (200±20 g, blood glucose levels ≥16.7 mM) were fasted overnight and randomly divided into four groups (n=3 in each group). Group 1 was the control group, which received oral administration of insulin solution (60 IU/kg) by gavage. Group 2 was the positive control group, which was treated with sc injections of insulin in PBS (2 IU/kg). Groups 3 and 4 received insulin-loaded L/C NPs at doses of 40 and 60 IU/kg, respectively, by gavage. Blood samples were collected from the tail veins at 0, 0.5, 1, 2, 4, 6, 8, 10, and 12 hours after administration, and blood glucose levels were measured using a Blood Analyzer (ONETOUCH Ultra; Johnson & Johnson, New Brunswick, NJ, USA).

The relative pharmacological bioavailability (Fp) of insulin after oral administration was calculated according to the following equation:26 where Doseoral and Dosesc are the insulin doses administered orally or subcutaneously, respectively, and AAC is the area above the curve of the reduction in blood glucose level over time.

Statistical analysis

The data were expressed as the mean ± standard deviation and analyzed by one-way analysis of variance. Differences were considered statistically significant at P<0.05.

Results

In this study, insulin-loaded L/C NPs were prepared to investigate their characteristics and drug EEs. First, we studied the conditions of insulin loading into L/C NPs. Preliminary experiments showed that the pH of chitosan solution affected the EE of insulin in NPs. To determine the optimal pH for insulin loading into L/C NPs, an L/C ratio of 20:1 (w/w) was used, and the pH of the chitosan solution during L/C NP preparation was varied by extra addition of glacial acetic acid or 1 N NaOH. As shown in Table 1, the insulin EE increased in parallel with pH increases up to the isoelectric point of recombinant human insulin (pI =5.4). In fact, as the chitosan used in experiments would precipitate when the pH exceeded 6.5, further studies using higher pH values of the chitosan solution were not performed. These results were consistent with previous results.27

Table 1

Influence of the pH of chitosan solution on the characteristics of insulin-loaded L/C NPsa

Formulation	pH of CS solution	EE (%)b	DL (%)b	Size (nm)b	Zeta potential (mV)b
A1	2.0	18.01±0.72	0.67±0.04	128.33±9.45	22.48±2.14
A2	3.0	66.25±1.89	2.16±0.21	149.14±5.88	23.56±1.97
A3	4.0	83.04±1.66	3.31±0.11	177.36±11.07	21.87±2.05
A4	5.0	90.49±1.06	3.81±0.16	168.27±7.35	24.24±3.47
A5	5.5	94.69±0.20	4.60±0.16	180.30±15.92	24.40±1.75
A6	6.0	Floccules	Floccules	Floccules	Floccules

Notes:

The L/C ratio of 20:1 was used.

The data are presented as the mean ± SD (n=3).

Abbreviations: L/C NPs, lecithin/chitosan nanoparticles; CS, chitosan; EE, entrapment efficiency; DL, drug loading; SD, standard deviation.

Next, we determined the optimal L/C ratio, using the selected pH value (5.4) for the chitosan solution and differing L/C ratios (10:0, 5:1, 10:1, 20:1, and 40:1) during insulin loading. As shown in Table 2, the L/C ratio affected particle sizes, zeta potentials, and insulin EEs. In our experiments, insulin did not form phospholipid complexes with other lecithin types, such as S45 (40% phosphatidylcholine/60% phosphatidylethanolamine, Lipoid S45). Thus, we did not study L/C NPs with other lecithin types.

Table 2

Influence of different lecithin-to-chitosan ratios on main characteristics of insulin-loaded L/C NPs

Formulation	L/C ratio	EE (%)a	DL (%)a	Size (nm)a	Zeta potential (mV)a
B1	10:0	78.90±6.12	9.37±0.87	43.38±23.30	−21.49±2.01
B2	5:1	89.03±1.55	5.75±1.79	125.05±22.16	22.36±0.72
B3	10:1	94.32±0.34	8.82±0.18	159.42±7.17	24.97±2.41
B4	20:1	94.69±0.20	4.60±0.35	180.12±15.72	24.40±1.75
B5	40:1	93.10±0.44	2.61±0.10	202.08±9.00	20.02±1.22

Note:

The data are presented as the mean ± SD (n=3).

Abbreviations: L/C NPs, lecithin/chitosan nanoparticles; L/C, lecithin/chitosan; EE, entrapment efficiency; DL, drug loading; SD, standard deviation.

For comparison purposes, phospholipid vesicles loaded with 10 mg insulin were prepared without chitosan (Table 2; L/C ratio, 10:0). Compared with insulin-loaded L/C NPs, these insulin-loaded lecithin vesicles had a narrow size distribution and negative zeta potentials, whereas NPs prepared with the L/C ratios 10:1 and 20:1 had the highest insulin EEs (Table 2). Thus, the optimal conditions for insulin loading in L/C NPs were L/C ratios of 10:1 and 20:1, and a chitosan solution pH of 5.4.

Morphological characterization

Cryogenic transmission electron microscopy analysis of insulin-loaded L/C NPs (L/C ratio, 20:1) revealed multi-lamellar structures with a hollow core circled by multiple bilayers (Figure 1A). In contrast, the morphology of the insulin-loaded phospholipid vesicles (L/C ratio, 10:0) was significantly different, showing a typical shell–core structure (Figure 1B).

Figure 1

Morphology of insulin-loaded nanoparticles.

Notes: Cryogenic transmission electron microscopy images of insulin-loaded lecithin/chitosan nanoparticles (L/C ratio, 20:1) (A) and insulin-loaded vesicles (L/C ratio, 10:0) (B).

Abbreviation: L/C, lecithin/chitosan.

The FT-IR spectra of chitosan, insulin, lecithin, insulin–phospholipid complexes, and insulin-loaded L/C NPs (L/C ratio, 20:1) are shown in Figure 2. Compared to our previous results,25 the characteristic absorption peaks of insulin at 1,660 cm−1 (ν [CO]) and 1,520 cm−1 (δ [NH]) were shifted to shorter wavelengths (blue shifted), whereas the absorption peak typical for phospholipids demonstrated a slight red shift (from 1,238.9 cm−1 to 1,235.5 cm−1, ν [P=O]). In the spectrum of insulin-loaded L/C NPs, the characteristic absorption peaks of insulin did not shift to their original wavelengths, indicating that the insulin–phospholipid complexes did not dissociate during the preparation of insulin-loaded L/C NPs.

Figure 2

Fourier transform infrared spectroscopy analysis of the components of insulin-loaded L/C NPs.

Notes: I: chitosan, II: insulin–lecithin complex, III: insulin, IV: insulin-loaded L/C NPs (L/C ratio of 20:1), and V: lecithin.

Abbreviations: L/C NPs, lecithin/chitosan nanoparticles; L/C, lecithin/chitosan.

In vitro insulin release from L/C NPs

As insulin dissolved in solution can be easily digested by enzymes and therefore cannot be measured, insulin release profiles from lecithin–chitosan self-assembled NPs were determined in simulated gastric fluid (SGF) and simulated intestinal fluid (SIF), without enzymes. As shown in Figure 3, the time-dependent release of insulin from L/C NPs was affected by the L/C ratio. Insulin-loaded L/C NPs with an L/C ratio of 20:1 clearly demonstrated lower drug release, compared to those with an L/C ratio of 10:1.

Figure 3

In vitro time-dependent release profiles of insulin-loaded lecithin/chitosan nanoparticles with different L/C ratios.

Note: The data are presented as the mean ± SD (n=3).

Abbreviations: L/C, lecithin/chitosan; SD, standard deviation; SGF, simulated gastric fluid; SIF, simulated intestinal fluid.

L/C NPs with 20:1 L/C ratio released ~20%–30% of the loaded insulin over 2 hours in SGF and 20% over 12 hours in SIF. However, L/C NPs with 10:1 L/C ratio released 50%–60% of the loaded insulin in the first 2 hours in SGF and 50% after 12 hours in SIF. These results clearly indicated that insulin-loaded NPs with an L/C ratio of 20:1 demonstrated slower insulin release than those with a 10:1 ratio. Therefore, the former L/C NPs were used to test the hypoglycemic effect of insulin in vivo. In addition, insulin-loaded S75 lecithin vesicles dissociated and precipitated in both SGF and SIF.

To determine the hypoglycemic effect of insulin-loaded L/C NPs, they were orally administered to diabetic rats after overnight fasting, and blood samples were analyzed for blood glucose levels. As shown in Figure 4, significant difference in blood glucose reduction between rats receiving free insulin (Group 1) and insulin-loaded L/C NPs (Groups 3 and 4) was observed until the end of the experiment (P<0.05). Glucose levels barely changed within 12 hours in Group 1, whereas a hypoglycemic effect in Group 4 was evident.

Figure 4

Time-dependent reduction in blood glucose levels in diabetic rats.

Notes: Streptozotocin-treated rats were administered insulin at the dose of 60 IU/kg by gavage (Group 1) or 2 IU/kg subcutaneously (Group 2), or insulin-loaded lecithin/chitosan nanoparticles (L/C ratio, 20:1) at the dose of 40 IU/kg (Group 3) or 60 IU/kg (Group 4) by gavage. The data are presented as the mean ± SD (n=3); *P<0.05 and **P<0.01 versus Group 1.

Abbreviations: L/C, lecithin/chitosan; SD, standard deviation.

After sc injection of insulin, blood glucose was reduced by 85% of the initial level after 2 hours; this hypoglycemic effect was observed for up to 5 hours, after which it subsided. Orally administered insulin-loaded L/C NPs demonstrated slower but prolonged blood glucose reduction, which was maximal at 4 hours (47% and 65% decrease by 40 and 60 IU/kg L/C NPs, respectively) and lasted for 12 hours. These results indicate that insulin-loaded L/C NPs provided gradual long-lasting insulin delivery into the blood and that, considering the results of in vitro release experiments, the insulin entrapped in the NPs was released slowly and thus prolonged the hypoglycemic effects. Table 3 shows that the pharmacological bioavailability (Fp) of insulin significantly increased when delivered by L/C NPs (6.01% versus 0.53% for insulin solution orally administered, P<0.05).

Table 3

AAC0→12 h and Fp of insulin-loaded L/C NPs and free insulin

Formulation	AAC0→12 h	Fp (%)
Insulin solution (2 IU/kg, sc)	344.29±13.42	100.00
Insulin solution (60 IU/kg, gavage)	55.11±21.56	0.53
Insulin-loaded L/C NPs (L/C ratio of 20:1, 60 IU/kg, gavage)	621.09±8.85	6.01**

Notes: AAC0→12 h data are presented as the mean ± SD (n=3).

P<0.01 versus insulin solution administered by gavage.

Abbreviations: AAC, area above the curve; Fp, pharmacological bioavailability; L/C NPs, lecithin/chitosan nanoparticles; sc, subcutaneous; L/C, lecithin/chitosan; SD, standard deviation.

Discussion

In this study, insulin-loaded L/C NPs with high drug EE were successfully prepared and analyzed for physicochemical properties and hypoglycemic effects in an experimental rat model of diabetes.

In previous studies, self-assembled L/C NPs have been used to deliver lipophilic drugs; however, some lipophilic compounds showed low solubility in methanol or ethanol with lecithin, and solubilizing agents such as tocopheryl polyethylene glycol succinate and isopropyl myristate were necessary.28 Nevertheless, poor hydrophilic DL into L/C NPs (<1%) has been observed.15,22

Pure insulin is insoluble in absolute ethanol; however, we showed that insulin in complex with phospholipids had increased solubility in ethanol, which enabled successful encapsulation in L/C NPs with high entrapment efficiency (~94%). Our results suggest that phospholipid complexation may widen the potential clinical applications for L/C NPs because drug–phospholipid complexes soluble in ethanol or methanol could be used to prepare drug-loaded L/C NPs for successful drug delivery and appropriate time-dependent release.

We determined that the L/C ratio influenced particle size and the zeta potential, whereas the pH of the chitosan solution affected insulin-entrapment efficiency in NPs. Different combinations of insulin with lecithin were not tested because we previously determined that an insulin–phospholipid ratio of 10:1 was optimal for obtaining stable insulin–phospholipid complexes,25 which was used in the current experiments. Under these conditions, we obtained a maximal insulin-loading rate of 10%.

Furthermore, the L/C ratio affected in vitro time-dependent release of insulin from L/C NPs. In all formulations, we used an excess amount of chitosan.22 The increase in lecithin concentration strengthened the electrostatic interaction in NPs and increased the number of bilayers, ensuring slow release of insulin entrapped in multilayered NPs. Thus, stronger electrostatic interactions can account for differences between NPs prepared with different L/C ratios.

Finally, we developed a self-assembled oral insulin-delivery system, which has several advantages over previous approaches. Specifically, insulin-loaded L/C NPs could be obtained without the use of cross-linking agents such as tripolyphosphate29 or glutaraldehyde26 through a simpler preparation procedure, which did not require homogenization or repeated washing and precipitation as done in previous studies.30,27 Furthermore, the EE of self-assembled insulin-loaded L/C NPs was much higher than that of other delivery systems.

Although insulin–lecithin complexes could be self-assembled into L/C NPs, in vivo experiments with diabetic rats did not demonstrate a significant improvement in pharmacological bioavailability of insulin, compared with previous findings.4,7,30,31 Another limitation of this study is that pharmacokinetic/pharmacodynamic analyses to compare insulin bioavailability after oral and sc administration were not performed. Further research is required to address these issues.

It has been reported that improved oral bioavailability of NPs and protection from proteolytic degradation in the gastrointestinal tract could be helpful in reducing the insulin burst release.32,33 Relevant approaches include enteric coating and/or modification of NP surfaces. Thus, Eudragit S100 and HP-55 have demonstrated potential as enteric coatings for insulin-loaded L/C NPs.34,35 In our preliminary studies, Eudragit S100 microspheres provided a 5% decrease in the initial burst release of insulin in SGF during the first 2 hours (data not shown). In studies of insulin release using orally administered L/C NPs, parameters such as the serum insulin level should be analyzed to assess drug absorption and to accurately determine its relative bioavailability.

Conclusion

In the present study, we show that large hydrophilic peptides such as insulin can be successfully loaded into self-assembled L/C NPs after complexation with phospholipids. Using this approach, a high insulin-entrapment efficiency of ~94% was achieved, and insulin-containing L/C NPs of ~180 nm in size were obtained. Insulin encapsulation into multilayered L/C NPs provided improved insulin release after oral administration, which resulted in the reduction of blood glucose levels in diabetic rats. Our findings suggest that L/C NPs can be successfully used for the delivery of hydrophilic drugs.