C Fornaini1, G Lagori2, E Merigo2, J-P Rocca2, M Chiusano2, A Cucinotta3. 1. Group of Applied ElectroMagnetic, Information Engineering Department, University of Parma, Parma, Italy; Micoralis Laboratory, Faculty of Dentistry, University of Nice, Nice, France. 2. Micoralis Laboratory, Faculty of Dentistry, University of Nice, Nice, France. 3. Group of Applied ElectroMagnetic, Information Engineering Department, University of Parma, Parma, Italy.
Abstract
BACKGROUND AND AIMS: A 405 nm diode laser is indicated for composite materials polymerizing, thanks to the recent evolution in their compositions, absorbing in blue part of the spectrum. The purpose of this research was to evaluate its performance on two different kinds of composite resins. MATERIALS AND METHODS: Two different composites were polymerized with a traditional halogen lamp, a LED device and a 405 nm diode laser. The depth of the cure, the volumetric shrinkage, and the degree of the conversion (DC%) of the double bond during the curing process were measured. One-way ANOVA test, Kruskal-Wallis tests, and Dunn comparison tests were used for statistic analysis. RESULTS: Regarding the depth of polymerization, the laser had the worst performance on one composite while on the other, no significant difference with the other devices was observed. The volumetric shrinkage showed that laser produced the lowest change in both of the composites. The DC% measure confirmed these findings. CONCLUSIONS: Based on the results of this preliminary study, it is not possible to recommend the 405 nm diode laser for the polymerization of dental composites.
BACKGROUND AND AIMS: A 405 nm diode laser is indicated for composite materials polymerizing, thanks to the recent evolution in their compositions, absorbing in blue part of the spectrum. The purpose of this research was to evaluate its performance on two different kinds of composite resins. MATERIALS AND METHODS: Two different composites were polymerized with a traditional halogen lamp, a LED device and a 405 nm diode laser. The depth of the cure, the volumetric shrinkage, and the degree of the conversion (DC%) of the double bond during the curing process were measured. One-way ANOVA test, Kruskal-Wallis tests, and Dunn comparison tests were used for statistic analysis. RESULTS: Regarding the depth of polymerization, the laser had the worst performance on one composite while on the other, no significant difference with the other devices was observed. The volumetric shrinkage showed that laser produced the lowest change in both of the composites. The DC% measure confirmed these findings. CONCLUSIONS: Based on the results of this preliminary study, it is not possible to recommend the 405 nm diode laser for the polymerization of dental composites.
Authors: Richard B T Price; Daniel Labrie; Frederick A Rueggeberg; Christopher M Felix Journal: J Esthet Restor Dent Date: 2010-12 Impact factor: 2.843
Authors: Francisco G Rego-Filho; Maria T de Araujo; Kleber T de Oliveira; Vanderlei S Bagnato Journal: J Fluoresc Date: 2014-07-03 Impact factor: 2.217