PURPOSE: To evaluate changes in the physicochemical properties, water sorption (WS), solubility (SO), modulus of elasticity (E), ultimate tensile strength (UTS), and microhardness (MH) tests were undertaken in zinc-doped dental adhesives. METHODS: Two bonding resins, Adper Single Bond Plus (SB) and Clearfil SE Bond (SEB), were zinc-doped by mixing them with 5, 10 or 20 wt% of ZnO powder, or with 1 or 2 wt% ZnCl2. Resin disks were made of each adhesive blend for the evaluation of WS, SO, and MH, and dumbbell-shaped specimens were prepared for E and UTS testing. RESULTS: An increase in WS and SO was observed for adhesives doped with ZnCl2. A reduction in WS was observed for the adhesive blends containing 10% or 20 wt% ZnO, while the SO was not altered in any of the ZnO-doped adhesives. An increase in E values was observed only for the SB adhesive doped with ZnCl2. For SEB-blends, the incorporation of zinc compounds did not alter the E values. UTS values decreased when SEB was doped with ZnO. SB-blends doped with 20 wt% ZnO significantly increased their MH, and the addition of zinc to the SEB-blends augmented the MH values in all cases.
PURPOSE: To evaluate changes in the physicochemical properties, water sorption (WS), solubility (SO), modulus of elasticity (E), ultimate tensile strength (UTS), and microhardness (MH) tests were undertaken in zinc-doped dental adhesives. METHODS: Two bonding resins, Adper Single Bond Plus (SB) and Clearfil SE Bond (SEB), were zinc-doped by mixing them with 5, 10 or 20 wt% of ZnO powder, or with 1 or 2 wt% ZnCl2. Resin disks were made of each adhesive blend for the evaluation of WS, SO, and MH, and dumbbell-shaped specimens were prepared for E and UTS testing. RESULTS: An increase in WS and SO was observed for adhesives doped with ZnCl2. A reduction in WS was observed for the adhesive blends containing 10% or 20 wt% ZnO, while the SO was not altered in any of the ZnO-doped adhesives. An increase in E values was observed only for the SB adhesive doped with ZnCl2. For SEB-blends, the incorporation of zinc compounds did not alter the E values. UTS values decreased when SEB was doped with ZnO. SB-blends doped with 20 wt% ZnO significantly increased their MH, and the addition of zinc to the SEB-blends augmented the MH values in all cases.