A vacuum-annealing strategy for improving near-infrared super long persistent luminescence in Cr(3+) doped zinc gallogermanate nanoparticles for bio-imaging.

Novel Cr(3+) doped zinc gallogermanate (ZGGO) nanoparticles with 697 nm near-infrared (NIR) super long afterglow were prepared via a hydrothermal method. Subsequently, a vacuum-annealing strategy was adopted to improve NIR afterglow in ZGGO:Cr(3+) nanoparticles. For the sample annealed at 800 °C, no variation in the particle size is observed, the persistent luminescence increases by an order of magnitude (∼14 times) and the NIR afterglow time reaches more than 15 hours relative to the as-prepared sample. After annealing at temperatures higher than 880 °C, the persistent luminescence of the nanoparticles is enhanced, but they show aggregated-surface behavior. Meanwhile, shallow and deep traps are generated, related to the antisite defects and VGe-Cr(3+)-VO defect clusters, respectively. Finally, we apply ZGGO:Cr(3+) persistent luminescence nanoparticles (PLNPs) to a human serum albumin (HSA) colloid solution, and more than 1 h of NIR persistent luminescence is detected under 320 nm excitation. The quenching effect of NIR luminescence by OH(-) in the HSA solution is observed based on the reduced contribution of surface Cr(3+) in PLNPs to NIR luminescence. Our results suggest that ZGGO:Cr(3+) PLNPs have potential applications for in vivo bio-imaging.