Three-dimensional Nitrogen-Doped Graphene Supported Molybdenum Disulfide Nanoparticles as an Advanced Catalyst for Hydrogen Evolution Reaction.

An efficient three-dimensional (3D) hybrid material of nitrogen-doped graphene sheets (N-RGO) supporting molybdenum disulfide (MoS(2)) nanoparticles with high-performance electrocatalytic activity for hydrogen evolution reaction (HER) is fabricated by using a facile hydrothermal route. Comprehensive microscopic and spectroscopic characterizations confirm the resulting hybrid material possesses a 3D crumpled few-layered graphene network structure decorated with MoS(2) nanoparticles. Electrochemical characterization analysis reveals that the resulting hybrid material exhibits efficient electrocatalytic activity toward HER under acidic conditions with a low onset potential of 112 mV and a small Tafel slope of 44 mV per decade. The enhanced mechanism of electrocatalytic activity has been investigated in detail by controlling the elemental composition, electrical conductance and surface morphology of the 3D hybrid as well as Density Functional Theory (DFT) calculations. This demonstrates that the abundance of exposed active sulfur edge sites in the MoS(2) and nitrogen active functional moieties in N-RGO are synergistically responsible for the catalytic activity, whilst the distinguished and coherent interface in MoS(2)/N-RGO facilitates the electron transfer during electrocatalysis. Our study gives insights into the physical/chemical mechanism of enhanced HER performance in MoS(2)/N-RGO hybrids and illustrates how to design and construct a 3D hybrid to maximize the catalytic efficiency.

Hydrogen has emerged as an efn class="Chemical">fective alternative to fossil fuels because it is environment-friendly energy with water as exhaust1. Hydrogen formation from water has long been considered as a promising approach for solar energy storage2. To improve the hydrogen transition efficiency, advanced catalysts are continuously explored to reduce the overpotential of the hydrogen evolution reaction (HER), a basic step involved in electrochemical water splitting (2H+ + 2e− → H2)234. The widespread application of the most effective catalysts (drawn from the Pt group of metals) are limited by their low natural abundance and high cost5. Therefore, there is an urgent need to develop sustainable well-performing alternatives for HER electrocatalysis with high natural abundance and low cost67. Various transition metals including Co, Fe, Ni and their derivatives, and metal-free catalysts like graphitic-carbon nitride coupled with nitrogen-doped graphene have been widely reported for HER8910111213. However, these non-precious-metal catalysts suffer from instability and low catalytic activity in acidic conditions1314. Empirical results and theoretical predications have demonstrated that molybdenum disulphide (MoS2) and its derivatives possess high-performance electrocatalytic activity towards HER1516. It has been identified that the edge site of MoS2 can act as a promising hydrogen evolution catalyst, leading to a lateral dimension size-dependent catalytic activity5. However, the deficiencies of aggregation and low conductivity of MoS2 are still challenging problems which limit their widespread application. Monolayer metallic MoS2 with high conductivity have been explored for HER catalyst1718. For example, metallic nanosheets of 1T-MoS2 chemically exfoliated via lithium intercalation from semiconducting 2H-MoS2 nanostructures grown directly on graphite was reported as a highly competitive earth-abundant catalyst due to favorable kinetics, metallic conductivity, and proliferation of active sites17. Meanwhile, the functionalization of MoS2 materials with conductive templates or supports to form a multidimensional structure has been recently presented as an effective approach to improve the catalytic activity19. Carbon materials are promising candidates to support catalysts due to their unique physicochemical properties. Increasing evidence has demonstrated that the significantly improved HER performance of MoS2 can be implemented by incorporating MoS2 with carbon nanotube (CNTs), graphene, graphite or other mesoporous carbon to form a MoS2-based hybrid or composite2021222324. For example, Dai et al. developed an HER advanced catalyst of MoS2 nanoparticles grown on graphene via a facile solvothermal approach, the resulted highly exposed edges and excellent electrical coupling to the underlying graphene sheets endowed the hybrid catalyst with excellent HER activity25. The high electrical conductance of the carbon architecture facilitates the electron charge transfer leading to enhanced performance, whilst the active site introduced in the supports is another effective method to enhance the activity of the catalyst. The incorporation of electron-rich nitrogen atoms into the carbon architecture promotes the interaction between neighboring carbons and electrons, providing a superior heteroatom-doped catalyst2326. Nitrogen-doped graphene is one of the most promising candidates owing to its high chemical stability, good electrical conductivity and intrinsic moderate catalytic activity for hydrogen evolution27. For instance, Qiao’s group has obtained porous C3N4 nanolayers@N-graphene films by integrating porous C3N4 nanolayers with nitrogen-doped graphene sheets, displaying an unbeatable HER performance which stems from highly exposed active sites, hierarchical porous structure and 3D conductive graphene network28. Furthermore, it has been reported that the p-type MoS2 nanoplatelets grown on the n-type nitrogen-doped reduced graphene oxide (N-RGO) can form p−n junctions on nanoscale and act as an outstanding catalyst in photocatalytic HER29. However, to the best of our knowledge, little work on the influence of the composition and morphology of the nitrogen-doped graphene support to the HER has been reported.

Herein, we report MoS2 nanoparticles den class="Chemical">corated nitrogen-doped reduced graphene oxide (N-RGO), a three-dimensional (3D) hybrid structure with macro-porosity by a hydrothermal route, which can efficiently catalyze HER under acidic conditions with low overpotential and small Tafel slope. The resulting MoS2/N-RGO hybrid materials display high-performance HER catalytic activity. By controlling the elemental composition, electrical conductance and morphology of the as-prepared 3D MoS2/N-RGO hybrid, the enhanced electrocatalytic activity mechanism toward hydrogen evolution was investigated in detail.

Results

Structural and compositional characterization

Firstly, graphene oxide (n class="Chemical">GO) and (NH4)2MoS4 were sonicated in N, N-dimethylformamide (DMF) to generate a highly dispersed suspension. Hydrazine and polypyrrole (PPy) were then slowly added into the suspension, followed by hydrothermal assembly at 180 °C for 12 h. Besides as a reductant, hydrazine could work as a nitrogen source as PPy during the assembly process. Regarding to PPy, it acted not only as the nitrogen source, but also was used to fabricate 3D network structure which promoted the BET specific surface and conductivity of the final product. The hydrothermal environment plays a significant role in the nitrogen doping because in the absence of hydrothermal environment, the GO could be reduced directly without the incorporation of nitrogen into the graphene network. During the hydrothermal process, (NH4)2MoS4 and GO were reduced to MoS2 nanoparticles and RGO respectively by hydrazine; and MoS2 nanoparticles were grown on the RGO accompanied by incorporation of nitrogen species into the graphene lattice22. In order to sustain the perfect 3D structure, the as-prepared hybrid was directly dehydrated by a vacuum freeze drier and then heated at 600 °C for 3 h under nitrogen (Fig. 1). Other samples were also fabricated in the same way for comparison: N-RGO where (NH4)2MoS4 is removed from the starting materials; MoS2’/N-RGO where nitrogen-doped graphene sheets decorated with half quantity of MoS2; MoS2/N’-RGO where the addition order of hydrazine and PPy is exchanged; MoS2/N-RGO’ is the sample fabricated by GO of higher oxidation degree.

Figure 1

Schematic present of synthetic method and resultant 3D MoS2/N-RGO hybrid for hydrogen evolution reaction.

The 3D MoS/N-RGO synthesized was n class="Chemical">comprehensively characterized by a number of microscopic and spectroscopic tools. Scanning electron microscopic (SEM) images revealed a 3D network structure with crumpled few-layered graphene sheets with plenty of folded edges conglutinated by PPy and decorated by numerous MoS2 nanoparticles with a lateral dimension of about 35 nm (Fig. 2A,B). The large area of graphene provided a large attachment surface for MoSnanoparticle growth and created an efficient template to restrain the aggregation of particles. The information presented by the transmission electron microscopic (TEM) images was consistent with the SEM in that there were laminar structures of graphene in the catalyst and MoSnanoparticles were evenly distributed on N-RGO sheets, suggesting successful assembly between the nanoparticles and the graphene sheets (Fig. 2C). The high resolution TEM (HRTEM) images of the 3D MoS/N-RGO structure showed the MoS with a lattice spacing of 0.4 nm, consistent with the spacing between the two sulfur atoms, which indicates the presence of MoS. The thickness of N-RGO was 0.34 nm, in accordance with the theoretical prediction30 (Fig. 2D). The corresponding selected area electron diffraction (SAED) revealed several sets of diffraction signals assigned to planes of hexagonal-phase of MoS2 and N-RGO (inset in Fig. 2D). The two separated diffraction rings can be indexed to the (100) and (110) planes of MoS2, and the diffraction of the (103) assigned to the N-RGO can also be observed. Notably, a distinguished and coherent interface was observed in MoS/N-RGO, which is known to facilitate the electron transfer to enhance catalytic activity30.

Figure 2

(A) SEM and (B) magnified SEM images of 3D MoS2/N-RGO hybrid. (C) TEM images and (D) high-resolution TEM images of the 3D MoS2/N-RGO hybrid.

X-ray photoelectron spectroscopy (XPS) measurements were performed to investigate the n class="Chemical">components of the prepared 3D MoS2/N-RGO hybrid. As shown in Fig. 3A, the XPS survey spectrum of the 3D MoS2/N-RGO hybrid shows the characteristic peaks of N-RGO; including a prominent graphitic C 1 s peak at 284 eV, a strong O 1 s peak at 532 eV and an N 1 s peak located at 402 eV. The peaks assigned to Mo 3d and S 2p in MoS2 were also present in the survey spectrum, which confirmed the successful assembly between the nanoparticles and the graphene sheets. The detailed information of elemental composition is presented in Fig. 3B. The corresponding element analysis revealed that the atomic ratio of Mo (0.75%) to S (1.46%) was about 1:2, consistent with the theoretical value of MoS2. It is worthy mentioning that the N/C atomic ratio of the 3D MoS2/N-RGO hybrid was calculated up to be 5.9%, much higher than that of N-doped graphene from previous reports313233. The higher nitrogen element included in the 3D MoS2/N-RGO hybrid could lead to a more efficient catalytic activity30.

Figure 3

(A) The survey XPS spectrum and (B) corresponding elemental compositions of 3D MoS2/N-RGO catalyst. High-resolution (C) C 1 s, (D) N 1 s, (E) Mo 3d and (F) S 2p XPS spectra of 3D MoS2/N-RGO (the red curve: background; the black curve: fitting line; the open circle: raw date).

In the high resolution XPS of C 1 s (Fig. 3C), a prominent C = N peak (285.2 eV) can be observed, confirming the successful inn class="Chemical">corporation of N atoms into the 3D MoS2/N-RGO hybrid. The binding energy of C-C/C=C (284.5 eV) in the 3D MoS2/N-RGO hybrid was downshifted by ∼0.5 eV compared to the graphitized carbon peak of pristine GO (285.0 eV)34. This implies a remarkable amount of charge transfer from graphene to MoS2, which can improve both the current density and catalytic activity of the catalyst. The N 1 s region shown in Fig. 3D can be divided into four peaks: (1) the peak at 395.7 ± 0.3 eV is attributed to nitride-like species or aromatic N-imines; the pyridine-like peak located at 398.7 ± 0.3 eV; (3) the pyrrolic or amine moieties peak at 400.3 ± 0.3 eV; and (4) the graphitic nitrogen peak at 401.4 ± 0.3 eV3536. The high content of nitride-like peak was attributed to the adsorbed N2H437. It was reported that hydrazine were reducing reagents37, the nitride-like peak located at 395.7 eV should be ascribed to the adsorbed hydrazine, even samples experienced several-times washing and dialysis37. PPy was an efficient nitrogen precursor to fabricate nitrogen-doped graphene due to its excellent catalytic activity and high durability, which mainly existed in forms of pyrrolic N (401.0 ± 0.2 eV) and pyridinic N (398.1 ± 0.2 eV) in NGO name38. The characteristic peaks of nitride-like peak, pyrrolic and pyridinic N in the resulting hybrid materials indicated that hydrazine and PPy were both nitrogen source.

As shown in Fig. 3E, five characteristic peaks located at 228.8, 232.7, 230.0, 235.9 and 226.7 eV, corresponding to Mo4+ 3d5/2, Mo4+ 3d3/2, n class="Chemical">MoO3 or MoO42−, Mo5+ and S 2 s, respectively, are displayed in the high resolution XPS of Mo 3d39. The two main Mo 3d5/2 and Mo 3d3/2 peaks are close to the meta-stable 1 T phase of MoS2 (associating with better HER performance)4041, and the peak of Mo6+ results from the oxidation of the catalyst in air to form MoO3 or MoO42− 34 and the partial reduction of Mo6+ results in the formation of Mo5+ 39. The deconvolution of S 2p spectra (Fig. 3F) has yielded four main peaks located at 162.3, 163.4, 164.8 and 168.7 eV, which are assigned to S 2p3/2, S 2p1/2, S22− (or S2−) ligands and the S4+ of sulfate groups, respectively404344. The existence of S22− and/or S2− is likely to be caused by the doping of S in the graphene sheet or formation of an S-rich MoS2 structure. This facilitates the development of high HER activity at the active sites for HER on the edge of MoSwhere the unsaturated S atoms are exposed to adsorb H7404344.

The porosity structures of the 3D MoS/N-RGO hybrid were characterized using the n class="Chemical">nitrogen isotherm (Fig. 4A). The N2 adsorption-desorption isotherm of 3D MoS/N-RGO hybrid showed an intermediate shape between types II and IV (in the IUPAC classification) with a small H3 hysteresis loop extending from P/P0 = 0.45 to 0.95, demonstrating the presence of mesoporous structure and slit-shaped pores45. The N2 adsorption-desorption measurement revealed the as-prepared 3D MoS/N-RGO hybrid had a Brunauer-Emmett-Teller (BET) specific surface area of 1066.6 m2 g−1, which was significantly larger than many reported porous carbon nanomaterials46474849. The superior BET specific surface area was resulted from that unique 3D structure of MoS2/N-RGO hybrid materials and formation of numerous porous structures during the sintering and elimination process in the presence of PPy. The pore-size distribution of the 3D MoS/N-RGO hybrid calculated by the DFT method exhibited one dominant peak at 5.30 nm and another two weak peaks at ∼1.56 and 3.79 nm, respectively (Inset of Fig. 4A), suggesting that micropores and mesopores co-exist within the 3D MoS/N-RGO hybrid. Figure 4B showed XRD patterns of the 3D MoS/N-RGO hybrid, N-RGO and GO. The sharp oxidation peak at 11.7° distinctly exhibited in GO but had completely disappeared in MoS/N-RGO and N-RGO. However, for the latter a broad peak centered at around 24° which was associated with a graphitic crystal structure, implying that the GO was efficiently deoxidized during the hydrothermal process. In comparison with N-RGO, the diffraction peaks at 33.5°, 39.4° and 58.9° corresponding to (100), (103) and (110) of MoS2 could be observed in MoS/N-RGO, indicating the MoS2 nanoparticles have been successfully grown on the N-RGO surface. The disappearance of the typical (002) peak of MoSlocated at 14.1° resulted from the small size of the MoS nanoparticles preferring to attach to the surface of the silicon supports505152.

Figure 4

(A) Nitrogen adsorption-desorption isotherm and pore-size distribution (inset) of 3D MoS2/N-RGO. (B) XRD patterns of GO, N-RGO and 3D MoS2/N-RGO.

The successful fabrication of the 3D MoS/N-RGO hybrid was further n class="Chemical">confirmed by Raman spectra analysis. As shown in Fig. 5A, the characteristic peaks located at ~1346 and 1599 cm−1 associated with the D and G bands of graphene can be observed in GO, N-RGO and MoS2/N-RGO. The reduction of GO induces the recovery of the graphene structure, which leads to the increase of 2D bands in N-RGO and MoS2/N-RGO. Notably, compared to the GO with a G band at 1599 cm−1, the G band of N-RGO (1586 cm−1) and MoS2/N-RGO (1593 cm−1) showed a downshift due to the incorporation of N heteroatoms49. The characteristic peaks of MoS2 located at 375.5 and 403.5 cm−1 (and assigned to the in-plane E12g and out-of-plane A1g vibrational modes of the hexagonal MoS2) were observed in the Raman spectrum of MoS2/N-RGO ranging from 300 to 450 cm−1 (Fig. 5B)53. In comparison with MoS2, the decreasing difference between the peak frequencies of E12g and A1g for MoS2/N-RGO (27 cm−1) suggested that the interaction between the Mo precursors and graphene could efficiently avoid the aggregation of MoS239.

Figure 5

(A) Raman spectra of 3D MoS2/N-RGO, GO and N-RGO. (B) Raman spectra of 3D MoS2/N-RGO in the range of 300–450 cm−1.

Electrochemical activity and durability

The electrocatalytic activity of the as-prepared 3D MoS/N-RGO hybrid toward the HER was investigated in 0.5 M HSO solution with n class="Chemical">commercial Pt catalyst (10 wt % Pt on carbon black) as the reference. N-RGO, MoS2’/N-RGO, MoS2/N-RGO, MoS2/N’-RGO and MoS2/N-RGO’ were also prepared to investigate in detail the influence of composition and structure to the HER catalytic activity. XPS (Fig. S1), XRD (Fig. S2) and SEM (Fig. S3) confirmed the successful synthesis of the three catalysts. As shown in Fig. 6A, the polarization curves revealed that the as-generated 3D MoS/N-RGO displayed a small onset potential of 112 mV for HER activity, after which the cathodic current rose rapidly. In contrast, the MoS2’/N-RGO (210 mV), MoS2/N’-RGO (155 mV) and MoS2/N-RGO’ (200 mV) showed more negative onset potential, indicating lower HER activity. The current intensity of the 3D MoS/N-RGO hybrid was higher than the other catalysts along the whole potential region. To further investigate the HER activity, the linear portions of the Tafel plots were fitted to the Tafel equation (η = a + b log |j|), where j is the current density and b is the Tafel slope. In Fig. 6B, the generated MoS/N-RGO hybrid showed a Tafel slope of 44 mV per decade, which outperformed MoS2’/N-RGO of 114 mV per decade, MoS2/N’-RGO of 71 mV per decade and MoS2/N-RGO’ of 57 mV per decade. The slight higher Tafel slope compared to MoS2 nanoparticle on graphene with a value of 41 mV25 and metallic MoS2 nanosheets on graphite with a value of 43 mV17 may be resulted from the reduce of the conductivity of nitrogen dopants. Notably, the lower HER activity of other catalysts prepared led to higher Tafel slopes than the MoS/N-RGO hybrid. Electrochemical impedance spectroscopy (EIS) was measured to evaluate the HER catalytic activity of these catalysts. The MoS/N-RGO displayed the lowest faradaic impedance among these prepared catalysts (Fig. 6C) and was comparable with Pt/C, suggesting a small charge transfer resistance in the MoS/N-RGO54. Such a low charge transfer resistance resulted both from a distinguished and coherent interface between the MoS/N-RGO hybrid and from the good conductivity of N-RGO, leading to efficient electrical communication between the catalytic edge sites and underlying electrodes to facilitate the kinetic response of HER5556. Stability is a significant criterion to evaluate the practicality of a HER catalyst. After a long period of 1000 potential-cycling between −0.4 and 0 V, the as-generated MoS/N-RGO hybrid exhibited a negligible decrease in the current density, indicating outstanding electrochemical stability (Fig. 6D). The unique three-dimensional structure of the MoSnanoparticles grown on N-doped graphene may account for the good stability that was observed. The supports of the N-doped graphene restrain the agglomeration of MoSnanoparticles and facilitate the transport of electrolyte ions5657. In addition, the intercalation of sulfur into the graphene structure to form a stable covalent bond also contributes to the excellent stability (Fig. 3F).

Figure 6

(A) Polarization curves obtained of catalysts as indicated and (B) corresponding Tafel plots recorded on glassy carbon electrodes with a catalyst loading of 0.28 mg/cm2 (solid lines), and fitted Tafel plots (dashed dot). (C) Nyquist plots of the 3D MoS2/N-RGO catalyst recorded in nitrogen-purged 0.5 M H2SO4 from 10−2 to 106 Hz with an AC amplitude of 5 mV. (D) Stability test for the 3D MoS2/N-RGO catalyst. Negligible current was lost after 1000 cycles from −0.2 to −0.8 V at 10 mV/s.

Discussion

These results demonstrated that the 3D MoS/N-RGO hybrid exhibited superior electrochemical catalytic activity to MoS’/N-Rn class="Chemical">GO, MoS/N’-RGO and MoS/N-RGO’, the reasons for the enhanced mechanism of MoS/N-RGO hybrid toward HER activity can be explained as followed. Firstly, structure analysis derived from Nitrogen Sorption date (Fig. S4) showed that the 3D MoS/N-RGO hybrid had an 87% mesoporous surface area ratio (the mesopore surface area to BET total surface area), which was larger than MoS2’/N-RGO and MoS2/N’-RGO, which lead to better reactant accessibility and superior efficiency of build of the triple-phase boundaries (gas–electrode–electrolyte)5859. Secondly, both of the N-RGO without decorated MoS (Fig. S5) and MoS’/N-RGO with less decorated MoS (Fig. 6A) displayed a little HER activity compared to the proposed MoS/N-RGO hybrid, indicating the composition of MoSnanoparticles played a critical role in the active HER catalytic performance13.

Furthermore, the proposed hybrid contains efn class="Chemical">fective catalytic sites originated from sulfur in MoS2 and nitrogen impurities in RGO boost the activity of the catalyst. The relative content (RC) of S22− and/or apical S2−related to active HER catalytic activity, where RC is mean that sulfur elemental compositions (wt %) (Table S1) multiply sulfur distribution (at. %) (Table S2), in MoS/N-RGO hybrid is 3.5-folds and 1.9-folds higher than MoS’/N-RGO (Fig. 7B), MoS/N-RGO’ (Fig. 7F), while the distribution of S22− and/or apical S2− in MoS/N’-RGO (Fig. 7) was not observed. For the nitrogen impurities, it was found the nitrogen hybrid species are sensitive to the graphene oxidation degree, MoS2, PPy and hydrazine (Fig. 7). The MoS/N-RGO hybrid contains more pyrrolic N and less pyridinic N than MoS’/N-RGO, MoS/N’-RGO and MoS/N-RGO’ (Fig. 7A,C,E, Table S3), it was speculated that the pyrrolic N instead of pyridinic N is more active towards HER catalysis. The overall HER pathway can be described by a three-state diagram comprising an initial state H+ + e−, an intermediate adsorbed H*, and a final product 1/2H260. The Gibbs free-energy of the intermediate state, |∆GH*|, has been considered as a major descriptor of the HER activity for a wide variety of metal catalysts. The optimum value of |∆GH*| should be zero. Density Functional Theory (DFT) calculations showed that graphite N shows the smallest Gibbs free-energy (|∆GH*|) value of 0.76 eV, followed by pyrrole N of 1.10 eV and pyridinic N of 1.73 eV, indicating graphite N was the best electrocatalytic activity from the viewpoint of thermodynamics and pyrrolic N also possessed the enhanced electrocatalytic activity than pyridinic N toward HER (Fig. 8). Additionally, the higher oxidation degree of the RGO’ can induce the more nitrogen hybrid (Table S1), larger mesopore surface area but larger faradaic impedance (Fig. 6C), which led to a lower HER performance. Therefore, it was demonstrated that the efficient active nitrogen and sulfur species combined with the good conductance and large mesoporous surface area ratio of 3D MoS/N-RGO hybrid were all beneficial to the enhanced HER catalytic activity.

Figure 7

High-resolution XPS spectra of (A), (C), (E) N 1 s and (B), (D), (F) S 2p of the MoS2’/N-RGO, MoS2/N’-RGO and MoS2/N-RGO’ (the red curve: background; the black curve: fitting line; the open circle: raw date).

Figure 8

The calculated free-energy diagram of HER for graphite N, pyridinic N and pyrrole N catalysts.

Conclusion

In summary, we have developed an efficient hydrothermal route to successfully synthesize a 3D hybrid material of nitrogen-doped graphene n class="Chemical">oxide sheets-supported molybdenum disulfide nanoparticles with high capability of hydrogen evolution. The morphology and element of the as-generated 3D MoS/N-RGO hybrid were characterized by comprehensively microscopic and spectroscopic methods including SEM, TEM, HRTEM, BET, XRD, XPS and Raman spectroscopy. Electrochemical characterization data including low onset potential, small Tafel slope, low charge transfer resistance and high electrochemical stability revealed the high performance of the MoS/N-RGO hybrid toward HER catalytic activity compared to analogous composites. Detailed experimental analysis implies that the abundant active S22− and/or S2− ligand species and pyrrolic nitrogen and graphene N of the 3D MoS/N-RGO hybrid and its good conductance were all beneficial to its enhanced HER catalytic activity. The exploration of the enhanced HER mechanism of the MoS2/N-RGO hybrid provides guidelines to design and construct 3D hybrids to maximize their catalytic efficiency.

Methods

Materials synthesis

Graphene oxide (n class="Chemical">GO, made from graphite flake, GO’, small flakes and dry platelets) was obtained from XF NANO, INC and graphene supermarket, respectively. Hydrazine monohydrate (N2H4·H2O, 80%) was purchased from Guangdong Guanghua Sci-Tech Co., Ltd (JHD). (NH4)2MoS4, Polypyrrole (PPy,) and Pt/C (10% Pt) were obtained from Sigma-Aldrich. N, N-dimethylformamide (DMF, ≥99.5%) and KOH were purchased from Sinopharm Chemical Reagent Co., Ltd. Sulfuric acid (H2SO4, 95–98%) and ethanol (99.9%) was acquired from Beijing Chemical Works. All aqueous solutions were prepared with doubly distilled water.

Materials preparation

22 mg of (NH4)2MoS4 and 10 mg of n class="Chemical">GO was dispersed in 10 ml of DMF by 10 min of sonication at room temperature. Then 0.1 ml of N2H4•H2O was added to the above solution followed by 30 min of sonication. 100 mg PPy was then added, followed by sonication for 10 min to form a stable complex solution. The mixture solution was transferred to a 40 mL Teflon-lined autoclave and heated in an oven at 180 °C for 12 h with no intentional control of ramping or cooling rate. The product was collected by centrifugation at 10000 rpm for 5 min and washed with DI water several times to remove most of the DMF. Subsequently, the product was redispersed in 3 ml of DI water and freeze-dried overnight, followed by thermal treatment at 600 °C for 3 h in N2 gas with 400 standard cubic centimeters per minute (sccm) to remove the organic species (DMF) and improving crystallinity. The obtained product was denoted as 3D MoS2/N-RGO. Other samples were also fabricated in the same way for comparison: N-RGO where (NH4)2MoS4 is removed from the starting materials; MoS2’/N-RGO where Nitrogen-doped graphene sheets decorated with half quantity of MoS2; MoS2/N’-RGO where the addition order of hydrazine and PPy is exchanged; MoS2/N-RGO’ is the sample fabricated by GO of higher oxidation degree.

Characterizations

X-ray diffraction (XRD) was performed with a Rigaku X-ray diffractometer with Cu KR target. The porosity was measured with a nitrogen adsorn class="Chemical">ption-desorption isotherm using a surface area analyzer (QuadraSorb SI 2000-08, Quantachrome Instruments). The structure of products was observed under a field-emission scanning electron microscope (SEM; JEOL-6300 F, 3 kV) and a transmission electron microscope (TEM; JEM-2010, 200 kV). X-ray photoelectron spectroscopy (XPS) spectra were obtained using an AXIS ULTRADLD instrument equipped with an Al Kα X-ray source. Raman spectrum of powder samples were recorded on an InVia-Reflex Raman microscope with a laser excitation wavelength of 532 nm.

Electrochemical measurement

All electrochemical studies were performed using a CHI 852C electrochemical workstation (Shanghai Chenhua Instrument Co., China) in a standard three-electrode setup. A three-electrode n class="Chemical">configuration consisting of a saturated calomel electrode (SCE) as the reference electrode, a graphite rod as the counter electrode and a glass carbon RDE after loading the catalyst as the working electrode was employed. Typically, 0.5 mg of catalyst was dispersed in 500 μl of DI water by sonication to form a homogeneous ink. Then, 20 μl of the catalyst ink (containing 20 μg of catalyst) was loaded onto a glassy carbon electrode (GCE) of 3 mm in diameter (loading ~0.283 mg/cm2). After the catalyst ink dried, 5 μl of 1 wt% Nafion solution was dropped onto the GCE and the working electrode was prepared. Liner sweep voltammetry (LSV) was conducted in nitrogen-purged 0.5 M H2SO4 at a scan rate of 3 mV s−1 at 1400 rpm. Electrochemical impedance spectroscopy (EIS) was carried out in the same configuration in nitrogen-purged 0.5 M H2SO4 from 10−2 to 106 Hz with a modulation amplitude of 5 mV. SCE was calibrated with respect to reversible hydrogen electrode (RHE). The calibration was performed in the high purity H2 saturated electrolyte with a Pt wire as the working electrode and the counter electrode. LSV were run at a scan rate of 0.1 mV s−1, and the potential at which the current crossed zero was taken to be the thermodynamic potential for the hydrogen electrode reactions. In 0.5 M H2SO4, E (RHE) = E (SCE) + 0.314 V. All the potentials reported in our manuscript are against RHE.

Density Functional Theory (DFT) calculations

The computations for DFT calculations were performed using the ab initio density functional n class="Chemical">code VASP with the PBE exchange correlation functional and PAW potentials. The PBE functional was chosen in order to obtain reasonable adsorption energies. The Brillouin zone is sampled using a 1 × 1 × 1 Monkhorst-Pack grid for the geometry optimizations and a 9 × 9 × 1 Monkhorst-Pack grid for the calculations of electronic properties. A basis set with the cut-off energy of 400 eV was chosen. The convergence criteria for energies and forces are set to 1.0 × 10−4 eV and −0.05 eV/Å, respectively. All calculations were performed using spin unrestricted method.

Additional Information

How to cite this article: Dong, H. et al. Three-dimensional Nitrogen-Doped Graphene Supported n class="Chemical">Molybdenum Disulfide Nanoparticles as an Advanced Catalyst for Hydrogen Evolution Reaction. Sci. Rep. 5, 17542; doi: 10.1038/srep17542 (2015).