Porous VO(x)N(y) nanoribbons supported on CNTs as efficient and stable non-noble electrocatalysts for the oxygen reduction reaction.

Novel nanocomposites of carbon nanotubes supported porous VO(x)N(y) nonoribbons (VO(x)N(y)-CNTs) have been synthesized by the annealing of the sol-gel mixture of CNTs and V2O5 under NH3 atmosphere as well as the ageing process in air. Besides the morphological and structural characterizations revealed by TEM, SEAD, EDS, XRD and XPS measurements, typical electrochemical tests including cyclic voltammetry (CV), rotating disk electrode (RDE) and chronoamperometry have been employed to determine the oxygen reduction reaction (ORR) performance of VO(x)N(y)-CNTs. Inspiringly, the results indicate that VO(x)N(y)-CNTs catalyst exhibits a 0.4 mA/cm(2) larger diffusion-limited current density, a 0.10  V smaller onset potential value, a 10.73% less of ORR current decay and an excellent methanol-tolerance compared with commercial Pt/C catalyst. Therefore, we have reasonable grounds to believe that this new VO(x)N(y)-CNTs nanocomposites can be regarded as a promising non-precious methanol-tolerant ORR catalyst candidate for alkaline fuel cells.

With the highly social development of industrialization and urbanization, the critical energy shortages mainly from the depletion of fossil fuels have motivated and accelerated intensive researches in developing alternative energy conversion and storage devices (ECSDs) with higher power and energy densities12345. Among various potential ECSDs for practical applications, polymer electrolyte membrane fuel cells (PEMFCs) have been extensively regarded as ideal power sources for future mobile and stationary applications due to their high energy efficiency, high power density and low level of emissions678. As important as the biological respiration in life processes, the oxygen reduction reaction (ORR) as the key cathodic process in PEMFCs will determine the behavior of the whole device due to the sluggish kinetics with respect to the anodic electrochemical reactions9. Thus, Pt-dominated materials have been used as highly desired catalysts to accelerate the ORR process in order to obtain an enhanced overall performance of PEMFCs. However, the elevated price and extreme CO or methanol sensitivities of the scarce platinum element have limited their widespread use in practical applications, and therefore developing non-precious ORR catalysts with efficient activity and stability has increasingly become the key issue for the commercialization of fuel cells.

Meanwhile, transition n class="Chemical">metal nitrides and oxynitrides have been intensively researched as suitable electrode or catalyst materials in recent years for various ECSDs, including fuel cells, metal-air batteries, lithium-ion batteries (LIBs), dye-sensitized solar cells (DSSCs) and electrochemical capacitors (ECs)10111213141516, due to the unique physical and chemical properties such as high intrinsic conductivity, relatively good electrochemical stability as well as the Pt-like electrocatalytic activity. And more especially, great interests have also been aroused in the development of vanadium nitrides and oxynitrides as advanced electrode materials by the nitridation of various vanadium oxides precursors. For example, Zhou et al. synthesized VN powder by calcining V2O5 xerogel under NH3 atmosphere with a promising supercapacitive specific capacitance of 161 F/g in 1M KOH at 30 mV/s17. Glushenkov prepared porous nanocrystalline VN by temperature-programmed ammonia reduction of V2O5 powder which exhibited a capacitance of 186 F/g in 1M KOH electrolyte at a current load of 1 A/g18. Porto’s group investigated the capacitances of VOxNy obtained from the nitridation of commercial V2O5 and VO2 precursors with the best specific capacitance of 186 F/g in 1M KOH at 10 mV/s19. To further enhance the electrochemical properties of VOxNy powders, Chen and his coworker synthesized carbon-supported VOxNy nanocrystalline using a mixture of melamine and V2O5 xerogel as precursor and obtained a specific capacitance of 273 F/g in 1M KOH at the scan rate of 30 mV/s20. Shu et al. also developed a soft-template synthesis of VOxNy-C nanomaterials for supercapacitors with a maximum specific capacitance of 271 F/g at 1A/g using ployvinylpyrrolidone (PVP) as the template and V2O5 xerogel as vanadium source. Their results demonstrated that the intimate contact between VOxNy grains and remaining carbon will result in a better electronic conductivity and the larger surface area will furnish more surface active redox sites21.

Although the occurrence of fast faradic redox reactions as well as the formation of electrical double-layer on the surface of VN and n class="Chemical">VOxNy have been suggested as the supercapacitive mechanism, few works have yet employed vanadium nitrides and oxynitrides as possible non-precious catalysts towards ORR. Huang et al. developed a hydrothermal route followed by calcination to prepare VN powder, which exhibited a comparable diffusion-limited current density but an inferior onset potential to commercial Pt/C catalyst22. Our previous work about VN/C catalyst also indicated the same tendency with the addition of the superior stability and methanol-tolerance23. Other than loading with Pt particles to obtain an enhanced ORR performance as shown in Yin’s work24, the introduction of porous structure and high surface area supporter can also elevate their electrochemical behaviors due to the increased conductivity and number of active sites925. Currently, the development of novel multifunctional composites/hybrids by structuring porous materials into the other nanostructures has been regarded as a rapidly developing research area. It is because that the composites/hybrids usually exhibit new properties that are superior to those of the individual components due to the collective behavior of the functional units. Thus, these emerging composites/hybrids will stimulate the emergence of innovative industrial applications in various important fields, including functional and protective coatings, storage and separation, heterogeneous catalysis, sensing and biology2627. Herein, we have successfully synthesized novel CNTs-supported porous VOxNy nanoribbons composites with an improvement of structural features as efficient and durable non-precious ORR catalysts in alkaline electrolyte using V2O5 nanoribbons and CNTs as raw materials.

Results

Figure 1 shows the morphological characters of as-prepared samples by transmission electron microscope (TEM) equipped with the selected area electron diffraction (SAED). It can be seen that there are plentiful pores distributing in the n class="Chemical">VOxNy nanoribbons due to the topotactic transformation whether supported by CNTs or not (Fig. 1A,D). The high-resolution TEM images show clear lattice fringes with an interfringe spacing of 0.203 nm which corresponds to the d-spacing of (200) planes (Fig. 1C). As for VOxNy-CNTs composites, VOxNy nanoribbons with a few tens of nanometers in widths and lengths up to micrometer range are randomly supported by plentiful tortuous CNTs (which are more transparent to the electron beam). Moreover, the element mapping spectra visually displayed in Fig. 2 demonstrate the locations of VOxNy nanoribbons in the composites. Figure 2B shows the C element from CNTs supporter which distributes everywhere and randomly, while the distributions of V, O and N elements are in accordance with the VOxNy nanoribbons to a great extent and the messy existence of O and N elements in Fig. 2C,D is believed to come from the surface species of CNTs. As the XRD patterns shown in Fig. 3, five main peaks ranging from 35° to 85° for both VOxNy and VOxNy-CNTs can match well with (111), (200), (220), (311) and (222) planes of the typical stoichiometric face-centered (fcc) VO (JCPDS No. 75-0048) or VN (JCPDS No. 73–0528) structures, where the figure of merit (FOM) values are 1.2 and 5.6 respectively. This result can be ascribed to the penetration of oxygen atoms into the VN crystal lattice17, which happened once the prepared samples were taken off from the furnace. Moreover, the broad peak for VOxNy-CNTs sample appears at about 26° which corresponds to the (002) plane of graphite carbon (JCPDS No. 75–1261) and confirms the existence of CNTs.

Figure 1

TEM images at different magnifications of VOxNy (A and B) and VOxNy-CNTs (D and E); SAED image (C) of VOxNy-CNTs.

Figure 2

TEM image (A) and element mapping spectra about C (B), V (C), O (D) and N (E) of VOxNy-CNTs.

Figure 3

XRD Patterns of VOxNy and VOxNy-CNTs with the standard patterns of VN, VO and graphite carbon.

XPS analysis in Fig. 4 further reveals that the components of n class="Chemical">VOxNy and VOxNy-CNTs are consist of V, N, O, and C elements from the survey spectra. Compared with the high intensity peak of CNTs in VOxNy-CNTs nanocomposites, it is notable that the signal of C 1S peak for pure VOxNy nanoribbons can be attributed to the air contamination on surface28, which exhibits a symmetric peak at 284.8 eV (Fig. 4D). Figure 4B shows the high-resolution XPS spectra of O 1 s and V 2p, where two peaks at 514.2 V (2p 3/2) and 521.5 eV (2p 1/2) can be ascribed to vanadium atoms in the VN crystalline, other four vanadium-based peaks at 515.7, 517.3, 523.4 and 525.1 eV are belong to vanadium oxides and the peaks at 532.2 and 530.3 eV of O 1s can be attributed to lattice oxygen in VxOy due to the ageing process in air and surface adsorbed hydroxyl oxygen, respectively2930313233. In addition, it is found that the chemical states of N and C elements for VOxNy-CNTs are quite different from pure VOxNy nanoribbons as shown in Fig. 4C,D. The peak of N 1s spectra at 397.5 eV can be assigned to the corresponding metal nitrides while the other two peaks at 399.5 and 401.3 eV are belonging to pyrrolic and quaternary-graphitic separately31. The C 1S spectrum also exhibits a typical aromatic C-N coordination in a graphitic carbon nitride framework at 288.2 eV except for the non-oxygenated ring C (284.8 eV, C-C, C = C) as well as the C-O bond at 286.3 eV3435. These results indicate that a surface modification and N-doping of CNTs happened sequentially during the acid treatment and annealing process, which have been proved to show excellent ORR activity363738.

Figure 4

XPS spectra of VOxNy and VOxNy-CNTs: survey (A), O 1 s and V 2P (B), N 1S (C) and C 1S (D).

The ORR performances of VOxNy and VOxNy-CNTs catalysts with VOxNy-XC 72R and commercial Pt/C as the references have been further investigated in alkaline electrolyte. As shown in Fig. 5, the ORR polarization curves for all kinds of catalysts at 1600 rpm in O2-saturated 0.1 M KOH exhibit a combined kinetic-diffusion control of charge transfer and mass transport process at different potentials. It is obvious that the support of carbon can improve the onset potential, half-wave potential and the diffusion-limited current density of pure VOxNy nanoribbons catalyst, and the hybrid with CNTs displays the strongest competitiveness with respect to the commercial Pt/C. Although the onset potential (0.88 V Vs. RHE) and half-wave potential (0.77 V Vs. RHE) of VOxNy-CNTs are 0.10 and 0.07 V smaller than those of Pt/C electrode, the diffusion-limited current density is about 0.4 mA/cm2 larger. Meanwhile, the stabilities of VOxNy-based electrodes are quite superior to that of Pt/C electrode no matter whether adding 3M Methanol at 500 s. As shown in the inset of Fig. 6, the current densities of pure VOxNy electrode, VOxNy-Xc 72R electrode, VOxNy-CNTs electrode and Pt/C electrode remain 98.73%, 89.76%, 93.68% and 82.95% after 1000 s compared with the initial ones. The increased loss with the addition of XC 72R and CNTs can be attributed to the oxidation of carbon under dynamic potential conditions and high-oxygen environment3940. Furthermore, unlike the instantaneous current density jump for Pt/C electrode due to the addition and the following electro-oxidation of methanol41, all VOxNy-based electrodes exhibit superior methanol tolerance with negligible changes. In addition, the ORR performance in alkaline electrolyte of VOxNy-CNTs is also highly comparable to other widely studied non-precious electrocatalysts, such as 3D nitrogen-doped graphene aerogel-supported Fe3O4 nanoparticles (Fe3O4/N-GAs)42, carbon nanotubes supported MnOx hybrids (MnOx/CNTs)43, carbon-supported CoSe2 nanocatalyst (CoSe2/C)44, cobalt and nitrogen-cofunctionalized graphene (Co-N-GN)45 and Fe2N-N-doped graphitic nanocarbons composite (Fe2N-NGC)46.

Figure 5

ORR activities of different VOxNy-based catalysts compared with Pt/C catalyst at 1600 rpm.

Figure 6

The chronoamperometric responses of different VOxNy-based electrodes as well as commercial Pt/C electrode with or without (insert) adding 3M MeOH at 500 s.

Discussion

To further understand the enhanced performance of VOxNy-CNTs catalysts with respect to VOxNy-XC 72R and pure VOxNy electrodes, cyclic voltammetry (CV) curves under both N2- and O2-saturated 0.1 M KOH electrolyte have been also recorded in Fig. 7. As can be seen, there are no obvious oxidation or reduction current peaks in all CV curves under N2-saturated KOH solution differing from Fe-N/C catalysts which present redox couples due to the existence of instable metal ions47. Thus, this result also indicates the high electrochemical stability of VOxNy over the whole measured potential range. Meanwhile, significant ORR peaks can be observed for VOxNy-XC 72R (0.65 V vs. RHE) and VOxNy-CNTs (0.75 V vs. RHE) electrodes under the O2-saturated condition compared with pure VOxNy electrode, which suggests the decreased overpotential and favorable charge transfer process for ORR4849. Considering the above results of ORR polarization curves and chronoamperometric responses, VOxNy-CNTs composites exhibit a fascinating ORR activity and stability. As is well-known to all, ORR is a surface chemical process where the consumption of oxygen occurs on the surface of electrode materials. Therefore, the enhanced performance of VOxNy-CNTs composites is believed to be closely related to the surface chemical states: (i) the bond between the carbon and the nitrogen is favorable to elevate the ORR electro-catalytic activity; (ii) the surface VOxNy layer itself benefits the stability and tolerance of methanol.

Figure 7

CV curves of VOxNy (A), VOxNy-XC 72R (B) and VOxNy-CNTs (C) as ORR catalysts in N2/O2-saturated 0.1 M KOH solution.

On the other hand, the increased overall conductivity also contributes to the decrease of overpotential as demonstrated before50. To further monitor the different conductivity of n class="Chemical">Pt/C and all VOxNy-based electrodes, representative Nyquist plots of electrochemical impedance spectroscopy (EIS) are displayed in Fig. 8, where the high frequency region (see the inset) can be associated with the charge-transfer process as well as the properties of electrochemical reaction resistance and the low frequency straight lines relate to the properties of the diffusion process51. It is obvious that the initial resistances corresponding to the combination of solution resistance and the film resistance are 39.3, 40.2, 40.6 and 41.4 Ω for VOxNy-CNTs, VOxNy-XC 72R, commercial Pt/C and bare VOxNy electrodes respectively, which indicates the enhanced electrochemical conductivity due to the introduction of carbon support for VOxNy catalyst. Moreover, the apparent arc-shaped region for just bare VOxNy electrode which is relative to the charge-transfer resistance is also responsible for its large ORR overpotential. Thus, the highest overall conductivity of VOxNy-CNTs is beneficial to the higher ORR onset potential, i.e., the lower overpotential.

Figure 8

Nyquist plots corresponding to all referred electrodes in 0.1 M KOH solution from 100 kHz-1 Hz; The inset shows the low impedance region.

Furthermore, since the ORR is a multi-electron charge transn class="Chemical">fer reaction with two main possible paths in alkaline electrolyte: one is one step direct pathway, involving four electrons transfer to produce while the other one is two steps indirect pathway, involving two electrons transfer to produce and then the get another two electrons to transform into , rotating disk electrode (RDE) voltammetry (i.e. linear-sweep voltammetry, LSV) was performed in oxygen-saturated 0.1 M KOH solution at a scan rate of 5 mV/s with the rotation rate from 400 to 2000 rpm to gain further insight into the ORR process. Figure 9 shows that all VOxNy-based electrodes display elevated ORR current densities with the increase of rotation rate and VOxNy-CNTs perform best in view of all above three electrochemical parameters. In addition, the numbers of electrons transferred per oxygen molecule in ORR have been estimated on the basis of the well-known Koutechy-Levich (K-L) equation:

Figure 9

ORR polarization curves of VOxNy (A), VOxNy-XC 72R (B) and VOxNy-CNTs (C) as electrocatalysts in O2-saturated 0.1 M KOH solution.

where J and J are the measured and kinetic current density, is the rotation rate in the form of rpm, is the transn class="Chemical">ferred electron number, is the Faraday constant (96485 C mol−1), is the concentration of O2 (1.210−6 mol cm−3), is the diffusion coefficient of O2 (1.910−5 cm2 s−1), is the kinematic viscosity (0.01 cm2 s−1) in 0.1 M KOH solution52. As shown in Fig 10, the electron transfer numbers of VOxNy, VOxNy-XC 72R and VOxNy-CNTs electrodes at all selected potentials increase in sequence with the average electron transfer numbers of 3.54, 3.82 and 3.90 respectively. Thus, this results indicate that VOxNy-CNTs catalyst exhibits a direct 4-electron dominated reduction process. And consistent with the analysis of EIS measurements, the increased number of electron transferred also suggests that the addition of carbon support can facilitate the transfer of electron from the surface of catalysts to oxygen molecule.

Figure 10

Koutechy-Levich (K-L) plots at different potentials for VOxNy (A), VOxNy-XC 72R (B) and VOxNy-CNTs (C) electrodes.

In conclusion, we have successfully prepared novel porous n class="Chemical">VOxNy-CNTs nonocomposite which exhibits tremendous potential to be used as an appropriate non-noble ORR electrocatalyst with superior stability, excellent methanol-tolerance and competitive activity. Combining the results of electrochemical tests and structural characterizations, the porous structure among VOxNy nanoribbons can help the electrolyte and oxygen make adequate contact with the catalysts, the presence of CNTs as well as the formation of carbon-nitrogen bonds can further enhance the overall conductivity and reduce the overpotential for the motivation of ORR while the surface VOxNy layer itself benefits the tolerance of methanol.

Methods

Synthesis of VOxNy-CNTs nanocomposite

V2O5 nanobelts un class="Chemical">sing as precursor were first prepared by a typical hydrothermal process, in which 2 mmol V2O5 powder was added into a mixture of 30 mL DI water and 5 mL H2O2 (30%) under vigorous stirring for 30 min to obtain a clear dark red solution before being transferred into a 50 mL of Teflon-sealed autoclave at 200 °C for four days. Meanwhile, 0.5 g of home-made CNTs (8–15 nm in diameter and 0.5–2 μm in length) were added into 50 mL of 98% H2SO4 and 14 mL of 65% HNO3 solution, refluxed at 80 °C for 90 min and then recovered by centrifugation. Then, V2O5 nanobelts and acid-treated CNTs (V2O5: CNTs = 6: 4) were mixed together uniformly in certain DI water with the aids of ultrasonication and stirring. After the vacuum filtration, peeling off from the membrane and drying treatment, the obtained mixture powder was further annealed in NH3 at 600 °C for 1 h with a ramping rate of 5 °C/min. Subsequently, the as-prepared sample was cooled down to room temperature under high purity nitrogen atmosphere. Moreover, pure VOxNy sample was obtained under the same conditions without the addition of CNTs.

Structure analysis of the VOxNy-based samples

Morphology and microstructure of the samples were characterized by powder X-ray diffractometry (XRD, X’pert PRO, Panalytical) using Cu Kα as radiation source, transmisn class="Chemical">sion electron microscopy (TEM, ARM200F, JEM) equipped with energy-dispersive X-ray spectroscopy (EDS). XPS measurements were carried out on an ESCALAB 250Xi spectrometer by Thermo Scientific with C 1s peak at 284.8 eV as an internal standard.

Electrochemical measurement of the VOxNy-based electrodes

All of the electroch-emical tests were performed on a three-electrode system (a glassy carbon electrode of 5 mm in diameter with a catalyst loading of 0.5 mg cm−2 as the working electrode, a n class="Chemical">Pt foil as the counter electrode and an Hg/HgO electrode as the reference electrode) using Autolab PGSTAT-204 and CHI 660E workstations. All potential values were calibrated with respect to reversible hydrogen electrode by ERHE = EHg/HgO + 0.92 V. What’s more, the preparation of VOxNy, VOxNy-XC 72R (60% VOxNy) and VOxNy-CNTs electrodes are similar to our previous works2353. Cyclic voltammetry (CV) measurements were performed at a scan rate of 50 mv s−1 in N2-/O2-saturated 0.1 M KOH electrolyte. Rotating disk electrode (RDE) tests were conducted at different rotating speeds from 400 to 2000 rpm in O2-saturated 0.1M KOH solution at a scan rate of 5 mv s−1. The chronoamperometry responses (i-t curves) were carried on a constant voltage of 0.65 V in O2-saturated 0.1 M KOH solution with or without adding 3M methanol at 500 s. Electrochemical impedance spectra (EIS) were measured from 1 Hz to 100 kHz with a potential amplitude of 10 mV.

Additional Information

How to cite this article: Huang, K. et al. Porous VOxn class="Chemical">Ny nanoribbons supported on CNTs as efficient and stable non-noble electrocatalysts for the oxygen reduction reaction. Sci. Rep. 5, 17385; doi: 10.1038/srep17385 (2015).