Mehmet Emin Kaval1, Hakan Akin2, Pelin Guneri3. 1. Department of Endodontology, School of Dentistry, Ege University, Izmir, Turkey. 2. Faculty of Dentistry, Department of Prosthodontics, Cumhuriyet University, Sivas, Turkey. 3. Department of Oral and Maxillofacial Radiology, School of Dentistry, Ege University, Izmir, Turkey.
Abstract
PURPOSE: To evaluate the radiopacity of five post materials using a digital image analysis method. MATERIALS AND METHODS: Twelve specimens from each post type (two zirconia and three fiber based) of 2 mm in thickness were obtained using a diamond blade mounted on a cutting machine, and digital radiographs were taken along with aluminum step-wedge and dentin discs under standard exposure conditions. The mean gray-values of specimens were measured using a computer graphics program. Data were analyzed using one-way ANOVA followed by Holm-Sidak multicomparison test (p = 0.05). RESULTS: The highest radiopacity was observed in custom zirconia (5.842 millimeters of equivalent Al [mmAl]), and the lowest value was detected with FRC-Postec (Ivoclar Vivadent) (1.716 mmAl). Significant differences were revealed between the radiopacity values among all groups (p < 0.05), except the Zr post materials (p = 0.56). CONCLUSIONS: All tested post materials had higher radiopacity than dentin. Further studies will be required to clarify optimum radiopacity properties of the post materials to provide a precise clinical observation.
PURPOSE: To evaluate the radiopacity of five post materials using a digital image analysis method. MATERIALS AND METHODS: Twelve specimens from each post type (two zirconia and three fiber based) of 2 mm in thickness were obtained using a diamond blade mounted on a cutting machine, and digital radiographs were taken along with aluminum step-wedge and dentin discs under standard exposure conditions. The mean gray-values of specimens were measured using a computer graphics program. Data were analyzed using one-way ANOVA followed by Holm-Sidak multicomparison test (p = 0.05). RESULTS: The highest radiopacity was observed in custom zirconia (5.842 millimeters of equivalent Al [mmAl]), and the lowest value was detected with FRC-Postec (Ivoclar Vivadent) (1.716 mmAl). Significant differences were revealed between the radiopacity values among all groups (p < 0.05), except the Zr post materials (p = 0.56). CONCLUSIONS: All tested post materials had higher radiopacity than dentin. Further studies will be required to clarify optimum radiopacity properties of the post materials to provide a precise clinical observation.