Preparation and Evaluation of Newly Developed Chitosan Salt Coating Dispersions for Colon Delivery without Requiring Overcoating.

Although chitosan (CS) has been recognized as a good material for colon-specific drug delivery systems, an overcoating with an enteric coating polymer on the surface of CS is absolutely necessary because CS is soluble in acidic conditions before reaching the colon. In the present study, to improve its stability in the presence of acid, a newly developed CS-laurate (CS-LA) material was evaluated as a coating dispersion for the development of colon-specific drug delivery systems. Two types of CS with different molecular weights, CS250 and CS600, were used to prepare CS-LA films by the casting method. The CS250-LA films had smooth surfaces, whereas the surfaces of the CS600-LA films were rough, indicating that the CS250-LA dispersion could form a denser film than CS600-LA. Both of these CS-LA films maintained a constant shape over 22 h in a pH 1.2 HCl/NaCl buffer, where the corresponding CS films rapidly disintegrated. In addition, the CS250-LA film showed specific colon degradability in a pH 6.0 phosphate buffered solution containing 1.0% (w/v) β-glucosidase. As a result of tensile strength and elongation at the break, both CS-LA films were found to have flexible film properties. Finally, the release of acetaminophen from disks coated with CS250-LA dispersions was significantly suppressed in fluids at pH 1.2 and 6.8, whereas disks coated with CS solution rapidly released the drug in pH 1.2 fluids. Taken together, this study shows that LA modification could be a useful approach in preparing CS films with acid stability and colonic degradability properties without requiring overcoating.