AIM: We evaluated the effect of incorporating Fluconazole, Chlorhexidine Gluconate, and Silver-Zinc Zeolite as bioactive materials (10% of mass) on the flexural strength of commercially available heat-cured polymethyl methacrylate (PMMA; Travelon). MATERIALS AND METHODS: The following four groups were compared; Group 1: Control group with pure PMMA, Group 2: Antibacterial drug group with chlorhexidine gluconate in powder form + PMMA, Group 3: Antifungal drug group with fluconazole in powder form + PMMA, Group 4: Antimicrobial agent group with silver zinc zeolite in powder form + PMMA. After processing, the specimens were subjected for flexural strength testing using three-point bending test in a universal testing machine. RESULTS: A significant (P < 0.0001) decrease in flexural strength following incorporation of Fluconazole, Chlorhexidine Gluconate, and Silver-Zinc Zeolite to heat polymerized acrylic resin was observed when compared with the control group. The decrease in mean flexural strength was minimal in the fluconazole group. CONCLUSION: Although the addition of a bioactive material to PMMA acrylic is desirable, it is not practical as it reduces flexural strength of the acrylic base.
AIM: We evaluated the effect of incorporating Fluconazole, Chlorhexidine Gluconate, and Silver-Zinc Zeolite as bioactive materials (10% of mass) on the flexural strength of commercially available heat-cured polymethyl methacrylate (PMMA; Travelon). MATERIALS AND METHODS: The following four groups were compared; Group 1: Control group with pure PMMA, Group 2: Antibacterial drug group with chlorhexidine gluconate in powder form + PMMA, Group 3: Antifungal drug group with fluconazole in powder form + PMMA, Group 4: Antimicrobial agent group with silver zinc zeolite in powder form + PMMA. After processing, the specimens were subjected for flexural strength testing using three-point bending test in a universal testing machine. RESULTS: A significant (P < 0.0001) decrease in flexural strength following incorporation of Fluconazole, Chlorhexidine Gluconate, and Silver-Zinc Zeolite to heat polymerized acrylic resin was observed when compared with the control group. The decrease in mean flexural strength was minimal in the fluconazole group. CONCLUSION: Although the addition of a bioactive material to PMMAacrylic is desirable, it is not practical as it reduces flexural strength of the acrylic base.
Authors: Sandra Sato; Márcia Rosa Sobreira Cavalcante; Iara Augusta Orsi; Helena de Freitas Oliveira Paranhos; Osvaldo Zaniquelli Journal: Braz Dent J Date: 2005
Authors: Abbas Falah-Tafti; Abbas Ali Jafari; Mohammad Hossein Lotfi-Kamran; Hossein Fallahzadeh; Reyhana Sadat Hayan Journal: Dent Res J (Isfahan) Date: 2010