Red/blue-shift dual-directional regulation of α-(Ca, Sr)2SiO4:Eu(2+) phosphors resulting from the incorporation content of Eu(2+)/Sr(2+) ions.

In this work, tunable emission from green to red and the inverse tuning from red to green in α-(Ca, Sr)2SiO4:Eu(2+) phosphors were demonstrated magically by varying the incorporation content of Eu(2+) and Sr(2+) ions, respectively. The tunable emission properties and the tuning mechanism of red-shift resulting from the Eu(2+) content as well as that of blue-shift induced by the Sr(2+) content were investigated in detail. As a result of fine-controlling the incorporation content of Eu(2+), the emission peak red-shifts from 541 nm to 640 nm. On the other hand, the emission peak inversely blue-shifts from 640 nm to 546 nm through fine-adjusting the incorporation content of Sr(2+). The excellent tuning characteristics for α-(Ca, Sr)2SiO4:Eu(2+) phosphors presented in this work exhibited their various application prospects in solid-state lighting combining with a blue chip or a near-UV chip.