Tobias T Tauböck1, Zrinka Tarle2, Danijela Marovic2, Thomas Attin3. 1. Department of Preventive Dentistry, Periodontology and Cariology, Center for Dental Medicine, University of Zurich, Plattenstrasse 11, CH-8032 Zurich, Switzerland. Electronic address: tobias.tauboeck@zzm.uzh.ch. 2. Department of Endodontics and Restorative Dentistry, School of Dental Medicine, University of Zagreb, Gunduliceva 5, HR-10000 Zagreb, Croatia. 3. Department of Preventive Dentistry, Periodontology and Cariology, Center for Dental Medicine, University of Zurich, Plattenstrasse 11, CH-8032 Zurich, Switzerland.
Abstract
OBJECTIVES: To investigate the influence of pre-heating of high-viscosity bulk-fill composite materials on their degree of conversion and shrinkage force formation. METHODS: Four bulk-fill composite materials (Tetric EvoCeram Bulk Fill-TECBF, x-tra fil-XF, QuixFil-QF, SonicFill-SF) and one conventional nano-hybrid resin composite (Tetric EvoCeram-TEC) were used. The test materials were either kept at room temperature or pre-heated to 68°C by means of a commercial heating device, before being photoactivated with a LED curing unit for 20s at 1170mW/cm(2). Shrinkage forces (n=5) of 1.5-mm-thick specimens were recorded in real-time for 15min inside a temperature-controlled chamber at 25°C (simulating intraoral temperature after rubber dam application) with a custom-made stress analyzer. Degree of conversion (n=5) was determined at the bottom of equally thick (1.5mm) specimens using Fourier transform infrared spectroscopy. Data were analyzed with Student's t-test, ANOVA and Tukey's HSD post-hoc test (α=0.05). RESULTS: Composite pre-heating significantly increased the degree of conversion of TECBF, but had no effect on monomer conversion of the other materials investigated. For each of the test materials, pre-heated composite generated significantly lower shrinkage forces than room-temperature composite. At both temperature levels, TECBF created the significantly highest shrinkage forces, and QF caused significantly higher shrinkage forces than both XF and TEC. CONCLUSIONS: Both the composite material and the pre-cure temperature affect shrinkage force formation. Pre-heating of bulk-fill and conventional restorative composites prior to photoactivation decreases polymerization-induced shrinkage forces without compromising the degree of conversion. CLINICAL SIGNIFICANCE: Composite pre-heating significantly reduces shrinkage force formation of high-viscosity bulk-fill and conventional resin composites, while maintaining or increasing the degree of monomer conversion, dependent upon the specific composite material used.
OBJECTIVES: To investigate the influence of pre-heating of high-viscosity bulk-fill composite materials on their degree of conversion and shrinkage force formation. METHODS: Four bulk-fill composite materials (Tetric EvoCeram Bulk Fill-TECBF, x-tra fil-XF, QuixFil-QF, SonicFill-SF) and one conventional nano-hybrid resin composite (Tetric EvoCeram-TEC) were used. The test materials were either kept at room temperature or pre-heated to 68°C by means of a commercial heating device, before being photoactivated with a LED curing unit for 20s at 1170mW/cm(2). Shrinkage forces (n=5) of 1.5-mm-thick specimens were recorded in real-time for 15min inside a temperature-controlled chamber at 25°C (simulating intraoral temperature after rubber dam application) with a custom-made stress analyzer. Degree of conversion (n=5) was determined at the bottom of equally thick (1.5mm) specimens using Fourier transform infrared spectroscopy. Data were analyzed with Student's t-test, ANOVA and Tukey's HSD post-hoc test (α=0.05). RESULTS: Composite pre-heating significantly increased the degree of conversion of TECBF, but had no effect on monomer conversion of the other materials investigated. For each of the test materials, pre-heated composite generated significantly lower shrinkage forces than room-temperature composite. At both temperature levels, TECBF created the significantly highest shrinkage forces, and QF caused significantly higher shrinkage forces than both XF and TEC. CONCLUSIONS: Both the composite material and the pre-cure temperature affect shrinkage force formation. Pre-heating of bulk-fill and conventional restorative composites prior to photoactivation decreases polymerization-induced shrinkage forces without compromising the degree of conversion. CLINICAL SIGNIFICANCE: Composite pre-heating significantly reduces shrinkage force formation of high-viscosity bulk-fill and conventional resin composites, while maintaining or increasing the degree of monomer conversion, dependent upon the specific composite material used.