OBJECTIVES: To evaluate the effects of aging and temperature on working time (WT) and setting time (ST) of several dual-cured resin cements. METHODS: WT and ST were determined with a thermo-controlled stage oscillating rheometer. New cement kits were used for the study. Cements were mixed according to instructions and dispensed on the oscillating stage that was preset at 22°C or 37°C. Rheologic charts were generated from the beginning of mixing until no further oscillation was detected. After initial measurements, cement kits were aged at 37°C for 12 weeks, and WT/ST was determined again at both temperatures. Five samples were read for each material and condition. Data were analyzed with repeated measures analysis of variance and a Tukey test at α=5% for each individual material. RESULTS: The WT and ST of all cements were significantly affected by temperature and aging (p<0.05). In general, higher temperature accelerated WT/ST, but aging effects were material dependent. Some materials presented reduced WT/ST, whereas others showed increased WT/ST, regardless of the temperature. CONCLUSIONS: The WT and ST were significantly affected by temperature variation and aging condition. Although temperature changes appeared to affect all materials similarly, aging effects were material dependent.
OBJECTIVES: To evaluate the effects of aging and temperature on working time (WT) and setting time (ST) of several dual-cured resin cements. METHODS: WT and ST were determined with a thermo-controlled stage oscillating rheometer. New cement kits were used for the study. Cements were mixed according to instructions and dispensed on the oscillating stage that was preset at 22°C or 37°C. Rheologic charts were generated from the beginning of mixing until no further oscillation was detected. After initial measurements, cement kits were aged at 37°C for 12 weeks, and WT/ST was determined again at both temperatures. Five samples were read for each material and condition. Data were analyzed with repeated measures analysis of variance and a Tukey test at α=5% for each individual material. RESULTS: The WT and ST of all cements were significantly affected by temperature and aging (p<0.05). In general, higher temperature accelerated WT/ST, but aging effects were material dependent. Some materials presented reduced WT/ST, whereas others showed increased WT/ST, regardless of the temperature. CONCLUSIONS: The WT and ST were significantly affected by temperature variation and aging condition. Although temperature changes appeared to affect all materials similarly, aging effects were material dependent.