Amanda Fahning Magno1, André da Costa Monini1, Marisa Veiga Capela2, Lídia Parsekian Martins3, Renato Parsekian Martins4. 1. Private practice, Ribeirão Preto, São Paulo, Brazil. 2. Professor, Faculdade de Química de Araraquara, Universidade Estadual Paulista, Araraquara, São Paulo, Brazil. 3. Professor, Faculdade de Odontologia de Araraquara, Universidade Estadual Paulista, Araraquara, São Paulo, Brazil. 4. Private practice, Araraquara, São Paulo, Brazil; adjunct professor, Orthodontics Graduate Program, Faculdade de Odontologia de Araraquara, Universidade Estadual Paulista, Araraquara, São Paulo, Brazil. Electronic address: dr_renatopmartins@hotmail.com.
Abstract
INTRODUCTION: Our objectives were to determine whether there are changes on the load deflection rate (L/DP) and the average force (FP) of the superelastic pseudoplateau, and whether permanent deformation is changed in nickel-titanium closed-coil springs (CCSs) after 6 months of clinical use. METHODS: Twenty-two nickel-titanium CCSs (Sentalloy 100 g; Dentsply GAC, York, Pa) were subjected to tensile mechanical testing at 37°C on activations varying from 3.2 to 16.0 mm before and after 6 months of clinical use. A regression line was fitted over the most horizontal area of the unloading part of the stress-strain graph of every CCS, and its slope was used as L/DP. The FP was determined by the midpoint of the longest segment of the curve that could be fit within the regression line with a R(2) of at least 0.999, and permanent deformation was determined graphically by obtaining the strain value when the measured stress reached zero. The data were analyzed by 3 analyses of variance at 2 levels, with 5% of significance. RESULTS: Time and activation significantly influenced the variables tested (P < 0.001). Time increased the L/DP and permanent deformation but decreased the FP. Activation decreased L/DP, FP, and permanent deformation. Significant interactions between time and activation were detected for FP (P = 0.013) and deformation (P < 0.001). CONCLUSIONS: After 6 months of active clinical use, the analyzed springs had a significant but small increase in their L/DP; FP dropped up to 88%, and the CCSs deformed up to 1.26 mm.
INTRODUCTION: Our objectives were to determine whether there are changes on the load deflection rate (L/DP) and the average force (FP) of the superelastic pseudoplateau, and whether permanent deformation is changed in nickel-titanium closed-coil springs (CCSs) after 6 months of clinical use. METHODS: Twenty-two nickel-titanium CCSs (Sentalloy 100 g; Dentsply GAC, York, Pa) were subjected to tensile mechanical testing at 37°C on activations varying from 3.2 to 16.0 mm before and after 6 months of clinical use. A regression line was fitted over the most horizontal area of the unloading part of the stress-strain graph of every CCS, and its slope was used as L/DP. The FP was determined by the midpoint of the longest segment of the curve that could be fit within the regression line with a R(2) of at least 0.999, and permanent deformation was determined graphically by obtaining the strain value when the measured stress reached zero. The data were analyzed by 3 analyses of variance at 2 levels, with 5% of significance. RESULTS: Time and activation significantly influenced the variables tested (P < 0.001). Time increased the L/DP and permanent deformation but decreased the FP. Activation decreased L/DP, FP, and permanent deformation. Significant interactions between time and activation were detected for FP (P = 0.013) and deformation (P < 0.001). CONCLUSIONS: After 6 months of active clinical use, the analyzed springs had a significant but small increase in their L/DP; FP dropped up to 88%, and the CCSs deformed up to 1.26 mm.