OBJECTIVE: The purpose of this study was to investigate the influence of post surface conditioning methods on the surface roughness and microtensile bond strength (μTBS) of zirconia posts to a resin cement. BACKGROUND DATA: Debonding at the post-adhesive interface is a major problem for zirconia posts. METHODS: A total of 25 zirconia posts (n=5) were prepared as follows: untreated (control, group C), airborne-particle abraded (group AA), silica coated (group SC), Nd:YAG laser irradiated (group N), and Er:YAG laser irradiated (group E). Prior to application of a dual-cured resin cement on the posts, roughness values of the post surfaces were detected with a profilometer. Specimens were then sectioned to obtain rectangular sticks for μTBS. After sticks were stored in distilled water at 37°C for 24 h, μTBS values were determined in a universal testing machine at a crosshead speed of 1 mm/min until failure. Furthermore, scanning electron microscopic (SEM) analysis was performed for one specimen of each group to evaluate the post surface morphology. One-way ANOVA and post-hoc comparison tests (α=0.05) were performed on all data. RESULTS: All surface treatment groups demonstrated significant higher μTBS values than the control group (p<0.001). The highest mean force value was observed in group SC. In addition, similar bond strength results were detected between group SC and group E (p=0.669). None of treatment groups resulted in significant improvement in roughness values of the post (p<0.05), except group N. CONCLUSIONS: All surface treatments were found to be effective methods to achieve a durable bond between zirconia posts to resin cement.
OBJECTIVE: The purpose of this study was to investigate the influence of post surface conditioning methods on the surface roughness and microtensile bond strength (μTBS) of zirconia posts to a resin cement. BACKGROUND DATA: Debonding at the post-adhesive interface is a major problem for zirconia posts. METHODS: A total of 25 zirconia posts (n=5) were prepared as follows: untreated (control, group C), airborne-particle abraded (group AA), silica coated (group SC), Nd:YAG laser irradiated (group N), and Er:YAG laser irradiated (group E). Prior to application of a dual-cured resin cement on the posts, roughness values of the post surfaces were detected with a profilometer. Specimens were then sectioned to obtain rectangular sticks for μTBS. After sticks were stored in distilled water at 37°C for 24 h, μTBS values were determined in a universal testing machine at a crosshead speed of 1 mm/min until failure. Furthermore, scanning electron microscopic (SEM) analysis was performed for one specimen of each group to evaluate the post surface morphology. One-way ANOVA and post-hoc comparison tests (α=0.05) were performed on all data. RESULTS: All surface treatment groups demonstrated significant higher μTBS values than the control group (p<0.001). The highest mean force value was observed in group SC. In addition, similar bond strength results were detected between group SC and group E (p=0.669). None of treatment groups resulted in significant improvement in roughness values of the post (p<0.05), except group N. CONCLUSIONS: All surface treatments were found to be effective methods to achieve a durable bond between zirconia posts to resin cement.
Authors: Verónica García-Sanz; Vanessa Paredes-Gallardo; Omel Mendoza-Yero; Miguel Carbonell-Leal; Alberto Albaladejo; José María Montiel-Company; Carlos Bellot-Arcís Journal: PLoS One Date: 2018-01-02 Impact factor: 3.240