OBJECTIVES: The aim of this work is to synthesize a novel stable and biodegradable nitric oxide (NO) donor polymer based on a chitosan backbone. This polymer needed to be linked to glutathione (GSH), which was nitrosated in a second step. This polymer has been developed as an NO delivery platform that could be further evaluated for an oral delivery in Crohn's disease. METHODS: The new polymer (named S-nitrosoglutathione-oligosaccharide-chitosan or SNOC) was obtained using a two-step procedure involving the linkage of GSH to chitosan via an amidine reaction followed by a post-nitrosation with NaNO2. The GSH linkage was assessed using NMR, FTIR and an Ellman's test, whereas the final NO amount was determined by the Griess and Saville method. RESULTS: Polymers with different numbers of NO groups were obtained (159.04 ± 64.16 µmol/g of polymer for SNOC G1 and 525.08 ± 151.35 µmol/g of polymer for SNOC G2) depending on the procedure used for production. When tested in an Ussing chamber, SNOC G2 had a sustained release of NO and nitrites for at least 6 h. CONCLUSION: We believe that this type of polymer is adapted for the development of various formulations, including microparticles.
OBJECTIVES: The aim of this work is to synthesize a novel stable and biodegradable nitric oxide (NO) donorpolymer based on a chitosan backbone. This polymer needed to be linked to glutathione (GSH), which was nitrosated in a second step. This polymer has been developed as an NO delivery platform that could be further evaluated for an oral delivery in Crohn's disease. METHODS: The new polymer (named S-nitrosoglutathione-oligosaccharide-chitosan or SNOC) was obtained using a two-step procedure involving the linkage of GSH to chitosan via an amidine reaction followed by a post-nitrosation with NaNO2. The GSH linkage was assessed using NMR, FTIR and an Ellman's test, whereas the final NO amount was determined by the Griess and Saville method. RESULTS: Polymers with different numbers of NO groups were obtained (159.04 ± 64.16 µmol/g of polymer for SNOC G1 and 525.08 ± 151.35 µmol/g of polymer for SNOC G2) depending on the procedure used for production. When tested in an Ussing chamber, SNOC G2 had a sustained release of NO and nitrites for at least 6 h. CONCLUSION: We believe that this type of polymer is adapted for the development of various formulations, including microparticles.