Layer-by-layer assembly of aquaporin Z-incorporated biomimetic membranes for water purification.

We fabricated a biomimetic nanofiltration (NF) membrane by immobilizing an Aquaporin Z (AqpZ)-incorporated supported lipid bilayer (SLB) on a layer-by-layer (LbL) complex polyelectrolyte membrane to achieve excellent permeability and salt rejection with a high stability. The polyelectrolyte membranes were prepared by LbL assembly of poly(ethylenimine) (PEI) with positive charges and poly(sodium 4-styrenesulfonate) (PSS) with negative charges alternately on a porous hydrolyzed polyacrylonitrile (H-PAN) substrate. AqpZ-incorporated 1,2-dioleloyl-sn-glycero-3-phosphocholine (DOPC)/1,2-dioleoyl-3-trimethylammo-nium-propane (chloride salt) (DOTAP) vesicles with positive charges were deposited on the H-PAN/PEI/PSS polyelectrolytes membrane surface. The resulting biomimetic membrane exhibited a high flux of 22 L·m(-2)·h(-1) (LMH), excellent MgCl2 rejection of ∼97% and NaCl rejection of ∼75% under an operation pressure of 0.4 MPa. Due to the attractive electrostatic interaction between SLB and the polyelectrolyte membrane, the biomimetic membrane showed satisfactory stability and durability as well as stable NF flux and rejection for at least 36 h. In addition, the AqpZ-containing biomimetic membrane was immersed in a 0.24 mM (critical micellar concentration, CMC) Triton X-100 solution for 5 min. The flux and rejection were slightly influenced by the Triton X-100 treatment. The current investigation demonstrated that the AqpZ-incorporated biomimetic membranes fabricated by the LbL method led to excellent separation performances and robust structures that withstand a high operation pressure for a relatively long time.