Guar gum based biodegradable, antibacterial and electrically conductive hydrogels.

Guar gum-polyacrylic acid-polyaniline based biodegradable electrically conductive interpenetrating network (IPN) structures were prepared through a two-step aqueous polymerization. Hexamine and ammonium persulfate (APS) were used as a cross linker-initiator system to crosslink the poly(AA) chains on Guar gum (Ggum) backbone. Optimum reaction conditions for maximum percentage swelling (7470.23%) were time (min) = 60; vacuum (mmHg) = 450; pH = 7.0; solvent (mL) = 27.5; [APS] (mol L(-1)) = 0.306 × 10(-1); [AA] (mol L(-1)) = 0.291 × 10(-3) and [hexamine] (mol L(-1))=0.356 × 10(-1). The semi-interpenetrating networks (semi-IPNs) were converted into IPNs through impregnation of polyaniline chains under acidic and neutral conditions. Fourier transform infra-red spectroscopy (FTIR), thermogravimetric analysis (TGA) and scanning electron microscopy (SEM) techniques were used to characterize the semi-IPNs and IPNs. Synthesized semi-IPNs and IPNs were further evaluated for moisture retention in different soils, antibacterial and biodegradation behavior.