Andrew Lau1, Jianying Li1, Young Cheul Heo1, Alex Fok2. 1. Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA. 2. Minnesota Dental Research Center for Biomaterials and Biomechanics, School of Dentistry, University of Minnesota, Minneapolis, MN, USA. Electronic address: alexfok@umn.edu.
Abstract
OBJECTIVE: To investigate the polymerization shrinkage kinetics of dental resin composites by measuring in real time the full-field shrinkage strain using a novel technique based on digital image correlation (DIC). METHODS: Polymerization shrinkage in resin composite specimens (Filtek LS and Z100) was measured as a function of time and position. The main experimental setup included a CCD camera and an external shutter inversely synchronized to that of the camera. The specimens (2 mm × 4 mm × 5 mm) were irradiated for 40s at 1200 mW/cm(2), while alternating image acquisition and obstruction of the curing light occurred at 15 fps. The acquired images were processed using proprietary software to obtain the full-field strain maps as a function of time. RESULTS: Z100 showed a higher final shrinkage value and rate of development than LS. The final volumetric shrinkage for Z100 and LS were 1.99% and 1.19%, respectively. The shrinkage behavior followed an established shrinkage strain kinetics model. The corresponding characteristic time and reaction order exponent for LS and Z100 were calculated to be approximately 23s and 0.84, and 14s and 0.7, respectively, at a distance of 1.0mm from the irradiated surface, the position where maximum shrinkage strain occurred. Thermal expansion from the exothermic reaction could have affected the accuracy of these parameters. SIGNIFICANCE: The new DIC method using an inversely synchronized shutter provided realtime, full-field results that could aid in assessing the shrinkage strain kinetics of dental resin composites as a function of specimen depth. It could also help determine the optimal curing modes for dental resin composites.
OBJECTIVE: To investigate the polymerization shrinkage kinetics of dental resin composites by measuring in real time the full-field shrinkage strain using a novel technique based on digital image correlation (DIC). METHODS: Polymerization shrinkage in resin composite specimens (Filtek LS and Z100) was measured as a function of time and position. The main experimental setup included a CCD camera and an external shutter inversely synchronized to that of the camera. The specimens (2 mm × 4 mm × 5 mm) were irradiated for 40s at 1200 mW/cm(2), while alternating image acquisition and obstruction of the curing light occurred at 15 fps. The acquired images were processed using proprietary software to obtain the full-field strain maps as a function of time. RESULTS: Z100 showed a higher final shrinkage value and rate of development than LS. The final volumetric shrinkage for Z100 and LS were 1.99% and 1.19%, respectively. The shrinkage behavior followed an established shrinkage strain kinetics model. The corresponding characteristic time and reaction order exponent for LS and Z100 were calculated to be approximately 23s and 0.84, and 14s and 0.7, respectively, at a distance of 1.0mm from the irradiated surface, the position where maximum shrinkage strain occurred. Thermal expansion from the exothermic reaction could have affected the accuracy of these parameters. SIGNIFICANCE: The new DIC method using an inversely synchronized shutter provided realtime, full-field results that could aid in assessing the shrinkage strain kinetics of dental resin composites as a function of specimen depth. It could also help determine the optimal curing modes for dental resin composites.
Authors: Yu-Xin Lou; Wei Ren; Bo Dong; Xing-Qiang Yang; Lei Zhao; Yu-Qing Lu; Xue-Qi Gan; Li Yue Journal: Hua Xi Kou Qiang Yi Xue Za Zhi Date: 2021-02-01
Authors: Guilherme Dos Santos Sousa; Gabriel Felipe Guimarães; Edilmar Marcelino; José Eduardo Petit Rodokas; Arilson José de Oliveira Júnior; Ivana Cesarino; Alcides Lopes Leão; Carla Dos Santos Riccardi; Mohammad Arjmand; Rafael Plana Simões Journal: Polymers (Basel) Date: 2021-06-23 Impact factor: 4.329
Authors: Aleksandra Mitrović; Dušan Antonović; Ivan Tanasić; Nenad Mitrović; Gordana Bakić; Dejana Popović; Miloš Milošević Journal: Biomed Res Int Date: 2019-11-17 Impact factor: 3.411