AIM: The aim of this study was to compare the micro hardness of a nanohybrid composite resin after brushing with two herbal and one non-herbal whitening toothpastes. MATERIALS AND METHODS: We divided Eighty disk-shaped specimens of a nanohybrid composite (Tetric N Ceram, Ivoclar Vivadent, Asia) into 4 groups of 20 specimens each: Groups A, B, C, and D. Group A was control, Group B was brushed with Colgate total advanced whitening (Colgate-Palmolive (India) Limited), Group C with Salt and Lemon, Dabur (Dabur International Limited, Dubai, UAE), and Group D with HiOra Shine, Himalaya (The Himalaya Drug Company, India). The specimens were polished using medium, fine, and superfine discs (Sof-lex, 3M, ESPE, USA) and subsequently placed at 37°C in distilled water. They were brushed for 2 minutes twice daily with a soft motorized toothbrush (Colgate 360 sonic power battery-operated tooth brush, Colgate Palmolive, India) for 30 days. The samples were rinsed under running water to remove the toothpaste and stored in distilled water at 37°C until the readout was taken on the Vickers's hardness tester for microhardness. RESULTS: The results revealed that the difference among the groups was statistically significant (P < 0.001). Tukey's test showed that reduction in microhardness for Group B was significantly higher than that for Group C and Group D (P < 0.001). CONCLUSION: Within the limitations of this study, non-herbal whitening toothpaste had a greater impact on the microhardness of nanohybrid resin composite than herbal whitening toothpastes.
AIM: The aim of this study was to compare the micro hardness of a nanohybrid composite resin after brushing with two herbal and one non-herbal whitening toothpastes. MATERIALS AND METHODS: We divided Eighty disk-shaped specimens of a nanohybrid composite (Tetric N Ceram, Ivoclar Vivadent, Asia) into 4 groups of 20 specimens each: Groups A, B, C, and D. Group A was control, Group B was brushed with Colgate total advanced whitening (Colgate-Palmolive (India) Limited), Group C with Salt and Lemon, Dabur (Dabur International Limited, Dubai, UAE), and Group D with HiOra Shine, Himalaya (The Himalaya Drug Company, India). The specimens were polished using medium, fine, and superfine discs (Sof-lex, 3M, ESPE, USA) and subsequently placed at 37°C in distilled water. They were brushed for 2 minutes twice daily with a soft motorized toothbrush (Colgate 360 sonic power battery-operated tooth brush, Colgate Palmolive, India) for 30 days. The samples were rinsed under running water to remove the toothpaste and stored in distilled water at 37°C until the readout was taken on the Vickers's hardness tester for microhardness. RESULTS: The results revealed that the difference among the groups was statistically significant (P < 0.001). Tukey's test showed that reduction in microhardness for Group B was significantly higher than that for Group C and Group D (P < 0.001). CONCLUSION: Within the limitations of this study, non-herbal whitening toothpaste had a greater impact on the microhardness of nanohybrid resin composite than herbal whitening toothpastes.