OBJECTIVE: To evaluate the durability of the bond of different resin cement systems to normal dentin (ND) and caries-affected dentin (CAD) with and without simulated intrapulpal pressure (IPP). METHODS AND MATERIALS: Molars with midcoronal caries were used. Occlusal enamel was cut to expose both dentin substrates (ND and CAD). Dentin substrates were differentiated using visual, tactile, caries-detecting dye, and dye-permeability methods. Prepared crown segments were equally divided according to the tested resin cement systems: etch-and-rinse resin cement, self-etch resin cement containing methacryloyloxydecyl dihydrogen phosphate (MDP), and self-adhesive resin cement. In addition to the dentin substrates and the resin cement types, the effect of application/storage conditions (with or without simulated IPP and with or without thermocycling) were tested. A microtensile bond strength test was done using a universal testing machine. Failure modes were determined using a scanning electron microscope. RESULTS: Etch-and-rinse resin cement strength values were significantly affected by the difference in the dentin substrates as well as the different application/storage conditions. Self-etch adhesive containing MDP bonded equally to ND and CAD and remained stable under all tested conditions. Self-adhesive resin cement revealed a similar bond to ND and CAD; however, its values were the lowest, especially when IPP and thermocycling were combined. Mixed failure was the predominant failure mode. CONCLUSIONS: Etch-and-rinse resin cement was sensitive to dentin substrate and application/storage conditions. Resin cement with self-etch adhesive containing MDP revealed more reliable bonding to ND/CAD even when IPP and thermocycling were combined. The bonding of the self-adhesive resin cement could not compete with other resin cements.
OBJECTIVE: To evaluate the durability of the bond of different resin cement systems to normal dentin (ND) and caries-affected dentin (CAD) with and without simulated intrapulpal pressure (IPP). METHODS AND MATERIALS: Molars with midcoronal caries were used. Occlusal enamel was cut to expose both dentin substrates (ND and CAD). Dentin substrates were differentiated using visual, tactile, caries-detecting dye, and dye-permeability methods. Prepared crown segments were equally divided according to the tested resin cement systems: etch-and-rinse resin cement, self-etch resin cement containing methacryloyloxydecyl dihydrogen phosphate (MDP), and self-adhesive resin cement. In addition to the dentin substrates and the resin cement types, the effect of application/storage conditions (with or without simulated IPP and with or without thermocycling) were tested. A microtensile bond strength test was done using a universal testing machine. Failure modes were determined using a scanning electron microscope. RESULTS: Etch-and-rinse resin cement strength values were significantly affected by the difference in the dentin substrates as well as the different application/storage conditions. Self-etch adhesive containing MDP bonded equally to ND and CAD and remained stable under all tested conditions. Self-adhesive resin cement revealed a similar bond to ND and CAD; however, its values were the lowest, especially when IPP and thermocycling were combined. Mixed failure was the predominant failure mode. CONCLUSIONS: Etch-and-rinse resin cement was sensitive to dentin substrate and application/storage conditions. Resin cement with self-etch adhesive containing MDP revealed more reliable bonding to ND/CAD even when IPP and thermocycling were combined. The bonding of the self-adhesive resin cement could not compete with other resin cements.