Oxidation of rubrene thin films: an electronic structure study.

The performances of organic semiconductor devices are crucially linked with their stability at the ambient atmosphere. The evolution of electronic structures of 20 nm thick rubrene films exposed to ambient environment with time has been studied by UV and X-ray photoemission spectroscopy (UPS and XPS), near edge X-ray absorption fine structure (NEXAFS) spectroscopy, and density functional theory (DFT). XPS, NEXAFS data, and DFT calculated values suggest the formation of rubrene-epoxide and rubrene-endoperoxide through reaction of tetracene backbone with oxygen of ambient environment. Angle dependent XPS measurement indicates that the entire probed depth of the films reacts with oxygen by spending only about 120 min in ambient environment. The HOMO peak of pristine rubrene films almost disappears by exposure of 120 min to ambient environment. The evolution of the valence band (occupied states) and NEXAFS (unoccupied states) spectra indicates that the films become more insulating with exposure as the HOMO-LUMO gap increases on oxidation. Oxygen induced chemical reaction completely destroys the delocalized nature of the electron distribution in the tetracene backbone of rubrene. The results are relevant to the performance and reliability of rubrene based devices in the environment.