Hongye Yang1, Dandan Pei2, Zhiyong Chen1, Jinmei Lei1, Liqun Zhou1, Cui Huang3. 1. The State Key Laboratory Breeding Base of Basic Science of Stomatology (Hubei-MOST) & Key Laboratory for Oral Biomedical Ministry of Education, School & Hospital of Stomatology, Wuhan University, Wuhan, People's Republic of China. 2. The State Key Laboratory Breeding Base of Basic Science of Stomatology (Hubei-MOST) & Key Laboratory for Oral Biomedical Ministry of Education, School & Hospital of Stomatology, Wuhan University, Wuhan, People's Republic of China; Department of Prosthodontics, Stomatology Hospital of Xi'an Jiaotong University College of Medicine, Xi'an, Shaanxi, People's Republic of China. 3. The State Key Laboratory Breeding Base of Basic Science of Stomatology (Hubei-MOST) & Key Laboratory for Oral Biomedical Ministry of Education, School & Hospital of Stomatology, Wuhan University, Wuhan, People's Republic of China. Electronic address: huangcui@whu.edu.cn.
Abstract
OBJECTIVES: To evaluate the effects of different application sequence of calcium-containing desensitising pastes on bonding effectiveness and tubule occlusion during etch-and-rinse (E&R) adhesive restoration. METHODS: Seventy molars were sectioned parallel to the occlusal plane, polished and randomly divided into seven groups (n=10). Group 1 was etched with 35% phosphoric acid for 15s. Groups 2-4 were treated with different calcium-containing desensitisers, including an arginine-calcium carbonate (Arg-CaCO3)-containing paste, a casein phosphopeptide-amorphous calcium phosphate (CPP-ACP)-containing paste and a calcium-sodium phosphosilicate (Novamin)-containing paste, respectively. Afterward, these groups were etched with 35% phosphoric acid for 15s. Groups 5-7 were initially etched and then treated with Arg-CaCO3-, CPP-ACP- and Novamin-containing desensitisers, respectively. In each group, samples were equally distributed into two subgroups (n=5) to bond with either a two-step E&R adhesive Adper SingleBond 2 (SB) or a three-step E&R adhesive Adper ScotchBond Multi-Purpose (SBMP). The microtensile bond strengths (MTBS) were tested and fracture modes were analyzed by stereomicroscopy and field-emission scanning electron microscopy (FESEM). Eight additional dentine disks were prepared to evaluate tubule occlusion prior to bonding using FESEM. RESULTS: The application sequence of calcium-containing desensitising pastes did not significantly affect MTBS irrespective of two-step SB (P>0.05) or three-step SBMP E&R adhesives (P>0.05). Effective dentinal tubule occlusion was observed in the mode of etching-desensitising. CONCLUSIONS: Applying calcium-containing desensitisers (particularly Arg-CaCO3- and Novamin-based) after etching during E&R adhesive restoration could achieve effective tubule occlusion without affecting the bonding strength.
OBJECTIVES: To evaluate the effects of different application sequence of calcium-containing desensitising pastes on bonding effectiveness and tubule occlusion during etch-and-rinse (E&R) adhesive restoration. METHODS: Seventy molars were sectioned parallel to the occlusal plane, polished and randomly divided into seven groups (n=10). Group 1 was etched with 35% phosphoric acid for 15s. Groups 2-4 were treated with different calcium-containing desensitisers, including an arginine-calcium carbonate (Arg-CaCO3)-containing paste, a casein phosphopeptide-amorphous calcium phosphate (CPP-ACP)-containing paste and a calcium-sodium phosphosilicate (Novamin)-containing paste, respectively. Afterward, these groups were etched with 35% phosphoric acid for 15s. Groups 5-7 were initially etched and then treated with Arg-CaCO3-, CPP-ACP- and Novamin-containing desensitisers, respectively. In each group, samples were equally distributed into two subgroups (n=5) to bond with either a two-step E&R adhesive Adper SingleBond 2 (SB) or a three-step E&R adhesive Adper ScotchBond Multi-Purpose (SBMP). The microtensile bond strengths (MTBS) were tested and fracture modes were analyzed by stereomicroscopy and field-emission scanning electron microscopy (FESEM). Eight additional dentine disks were prepared to evaluate tubule occlusion prior to bonding using FESEM. RESULTS: The application sequence of calcium-containing desensitising pastes did not significantly affect MTBS irrespective of two-step SB (P>0.05) or three-step SBMP E&R adhesives (P>0.05). Effective dentinal tubule occlusion was observed in the mode of etching-desensitising. CONCLUSIONS: Applying calcium-containing desensitisers (particularly Arg-CaCO3- and Novamin-based) after etching during E&R adhesive restoration could achieve effective tubule occlusion without affecting the bonding strength.