Evaluation of shear bond strength of composite resin bonded to alloy treated with sandblasting and electrolytic etching.

Conservation of natural tooth structure precipitated the emergence of resin-retained fixed partial dentures. The weakest link in this modality is the bond between resin cement and alloy of the retainer. Various alloy surface treatment have been recommended to improve alloy-resin bond. This in vitro study was carried out to observe changes in the Nickel-Chromium alloy (Wiron 99, Bego) surface following sandblasting or electrolytic etching treatment by scanning electron microscope (SEM) and to evaluate the shear bond strength of a resin luting cement bonded to the surface treated alloy. 80 alloy blocks were cast and divided into four groups of 20 each. In groups-A & B, the test surfaces were treated by sandblasting with 50 and 250 μm sized aluminium oxide particles respectively. In groups-C & D, the test surfaces were first treated by sandblasting with 50 and 250 μm sized aluminium oxide particles respectively followed by electrolytic etching. Test surfaces were observed under SEM at 1,000× magnification. Two alloy blocks of each group were luted together by a resin luting cement (Rely X, 3M) and their shear bond strength was tested. The mean shear bond strength in MPa of groups-A to D were 6.44 (±0.74), 8.18 (±0.51), 14.45 (±0.59) and 17.43 (±1.20) respectively. Group-D showed bond strength that is more than clinically acceptable bond strength. It is recommended that before luting resin-retained fixed partial dentures, the fitting surface of the retainer should be electrolytically etched to achieve adequate micromechanical retention.