Ying Xiao1, Xia Wang, Wei Wang, Di Zhao, Minhua Cao. 1. Key Laboratory of Cluster Science, Ministry of Education of China, Beijing Key Laboratory of Photoelectronic/Electrophotonic Conversion Materials, Department of Chemistry, Beijing Institute of Technology , Beijing 100081, P. R. China.
Abstract
A facile and low-cost strategy is demonstrated for preparing MnO/C-N hybrid, in which the MnO nanoparticles chemically combine with N-doped C by Mn-N bonding to achieve the hybridization of MnO with N-doped C. When served as an anode in lithium ion batteries (LIBs), the resultant hybrid manifested high capacity, excellent cyclability, and superior rate capability. A lithium storage capacity of 1699 mAh g(-1) could be obtained at 0.5 A g(-1) after 170 discharge-charge cycles. Even at a current density up to 5 A g(-1), a high reversible capacity (907.8 mAh g(-1)) can be retained after 400 cycles. The excellent lithium storage performance of the MnO/C-N hybrid can be ascribed to the synergetic effects of several factors including the unique hybrid structure, the N-doping and the chemical bonding of MnO and N-doped C.
A facile and low-cost strategy is demonstrated for preparing MnO/C-N hybrid, in which the n class="Chemical">MnO nanoparticles chemically combine with N-doped C by Mn-N bonding to achieve the hybridization of MnO with N-doped C. When served as an anode in lithium ion batteries (LIBs), the resultant hybrid manifested high capacity, excellent cyclability, and superior rate capability. A lithium storage capacity of 1699 mAh g(-1) could be obtained at 0.5 A g(-1) after 170 discharge-charge cycles. Even at a current density up to 5 A g(-1), a high reversible capacity (907.8 mAh g(-1)) can be retained after 400 cycles. The excellent lithium storage performance of the MnO/C-N hybrid can be ascribed to the synergetic effects of several factors including the unique hybrid structure, the N-doping and the chemical bonding of MnO and N-doped C.