Color-tunable and white luminescence properties via energy transfer in single-phase KNaCa2(PO4)2:A (A = Ce3+, Eu2+, Tb3+, Mn2+, Sm3+) phosphors.

A series of single-phase phosphors based on KNaCa2(PO4)2 (KNCP):A (A = Ce(3+), Eu(2+), Tb(3+), Mn(2+), Sm(3+)) have been prepared via the Pechini-type sol-gel method. Photoluminescence (PL) and cathodoluminescence (CL) properties of Ce(3+)-, Eu(2+)-, Tb(3+)-, Mn(2+)-, and Sm(3+)-activated KNCP phosphors were investigated. For the A singly doped KNCP samples, they exhibit the characteristic emissions of the A activator. Na(+) ions exhibit the best charge compensation result among Li(+), Na(+), and K(+) ions for Ce(3+)-, Tb(3+)-, and Sm(3+)-doped KNCP samples. The energy transfers from Ce(3+) to Tb(3+) and Mn(2+) ions as well as Eu(2+) to Tb(3+) and Mn(2+) have been validated. The emission colors of KNCP:Ce(3+)/Eu(2+), Tb(3+)/Mn(2+), Na(+) samples can be adjusted by energy transfer process and changing the Tb(3+)/Mn(2+) concentration. More importantly, white light emission in KNCP:Eu(2+), Mn(2+) system has been obtained. The KNCP:Tb(3+), Na(+) sample shows tunable luminescence from blue to cyan and then to green with the change of Tb(3+) concentration due to the cross-relaxation from (5)D3 to (5)D4. A white emission can also be realized in the single-phase KNCP host by reasonably adjusting the doping concentrations of Tb(3+) and Sm(3+) (reddish-orange emission) under low-voltage electron beam excitation. Additionally, the temperature-dependent PL properties of as-prepared phosphors reveal that the KNCP host has good thermal stability. Therefore, the KNCP:A (A = Ce(3+), Eu(2+), Tb(3+), Mn(2+), Sm(3+)) phosphors could be regarded as good candidates for UV W-LEDs and FEDs.