Influence of volume and activation mode on polymerization shrinkage forces of resin cements.

The concern with the polymerization shrinkage of restorative resin composites also applies to resin cements. The aim of this study was to evaluate the influence of volume and polymerization mode on forces generated during polymerization shrinkage (FGPS) of resin cements. Two light-cured resin cements--Variolink II (VL; Ivoclar Vivadent) and Nexus 3 (NX; Kerr)--and two self-cured resin cements - Multilink (ML; Ivoclar Vivadent) and Cement Post (CP; Angelus) - were inserted between two rectangular steel bases (6x2 mm) with distance set at 0.1, 0.3 and 0.5 mm, establishing a variation of volume. These steel bases were attached to a universal test machine with 50 kg load cell and forces (N) were registered for 10 min. Values of maximum forces generated by each material were subjected to two-way ANOVA and Tukey's test for individual comparisons (α=0.05). VL, NX and CP developed increasing FGPS as the volume of material increased, while ML presented the opposite behavior. It may be concluded that higher volume increases FGPS even with a concomitant decrease of C-factor, unless the resin cements present lower force generation rates as a function of time in combination with a low C-factor, resulting in stress relief and consequently lower values of FGPS.