Mechanical response of dental cements as determined by nanoindentation and scanning electron microscopy.

This study evaluated the effects of nanoindentation on the surface of white mineral trioxide aggregate (WMTA), Bioaggregate and Nano WMTA cements. Cements were mixed according to the manufacturer directions, condensed inside glass tubes, and randomly divided into three groups (n = 8). Specimens were soaked in synthetic tissue fluid (pH = 7.4) and incubated for 3 days. Cement pellets were subjected to nanoindentation tests and observed by scanning electron microscopy. Then, the images were processed and the number of cracks and total surface area of defects on the surface were calculated and analyzed using ImageJ. Data were submitted to one-way analysis of variance and a post hoc Tukey's test. The lowest number of cracks and total surface of defects were detected in Nano WMTA samples; however, it was not significantly different from WMTA samples (p = 0.588), while the highest values were noticed in Bioaggregate specimens that were significantly different from Nano WMTA and WMTA (p = 0.0001). The surface of WMTA and Nano WMTA showed more resistance after exposure to nano-compressive forces which indicated a better surface tolerance against these forces and crack formation. This suggests these substances are more tolerant cement materials which can predictably withstand loaded situations in a clinical scenario.