A simple template-free 'sputtering deposition and selective etching' process for nanoporous thin films and its application to dye-sensitized solar cells.

A facile and straightforward method is suggested to synthesize nanoporous-TiO₂ thin films for dye-sensitized solar cells (DSSCs). Silver/TiO₂ co-sputtering led to the formation of nanocomposite films which consisted of silver nanoclusters with surrounding TiO₂ matrices, and metal particles were subsequently etched by just immersing in nitric acid. Nanoporous-TiO₂ DSSCs fabricated by this simple and effective process showed power-conversion efficiencies of up to 3.4% at a thickness of only 1.8 μm, which is much superior to that of conventional nanoparticulate-TiO₂ DSSCs with similar thickness.