OBJECTIVE: The aim of the study was to provide data on the fracture strength of monolithic high translucent Y-TZP crowns and porcelain-veneered high translucent Y-TZP crown cores and to compare that data with the fracture strength of porcelain-veneered Y-TZP crown cores and monolithic lithium disilicate glass-ceramic crowns. MATERIALS AND METHODS: Sixty standardized crowns divided into six groups (n = 10) were fabricated: monolithic high translucent Y-TZP crowns, brand A, monolithic high translucent Y-TZP crowns, brand B, veneered high translucent Y-TZP crown cores, brand A, veneered high translucent Y-TZP crown cores, brand B, heat-pressed monolithic lithium disilicate crowns and veneered Y-TZP crown cores. All crowns were thermocycled, cemented onto dies, cyclically pre-loaded and finally loaded to fracture. RESULTS: The monolithic Y-TZP groups showed significantly higher fracture strength (2795 N and 3038 N) compared to all other groups. The fracture strength in the veneered Y-TZP group (2229 N) was significantly higher than the monolithic lithium disilicate group (1856 N) and the veneered high translucent Y-TZP groups (1480 N and 1808 N). CONCLUSIONS: The fracture strength of monolithic high translucent Y-TZP crowns is considerably higher than that of porcelain-veneered Y-TZP crown cores, porcelain-veneered high translucent Y-TZP crown cores and monolithic lithium disilicate crowns. The fracture strength of a crown made of monolithic high translucent Y-TZP is, with a large safety margin, sufficient for clinical use for the majority of patients. Porcelain-veneered Y-TZP crown cores show higher fracture resistance than monolithic lithium disilicate crowns.
OBJECTIVE: The aim of the study was to provide data on the fracture strength of monolithic high translucent Y-TZP crowns and porcelain-veneered high translucent Y-TZP crown cores and to compare that data with the fracture strength of porcelain-veneered Y-TZP crown cores and monolithic lithium disilicate glass-ceramic crowns. MATERIALS AND METHODS: Sixty standardized crowns divided into six groups (n = 10) were fabricated: monolithic high translucent Y-TZP crowns, brand A, monolithic high translucent Y-TZP crowns, brand B, veneered high translucent Y-TZP crown cores, brand A, veneered high translucent Y-TZP crown cores, brand B, heat-pressed monolithic lithium disilicate crowns and veneered Y-TZP crown cores. All crowns were thermocycled, cemented onto dies, cyclically pre-loaded and finally loaded to fracture. RESULTS: The monolithic Y-TZP groups showed significantly higher fracture strength (2795 N and 3038 N) compared to all other groups. The fracture strength in the veneered Y-TZP group (2229 N) was significantly higher than the monolithic lithium disilicate group (1856 N) and the veneered high translucent Y-TZP groups (1480 N and 1808 N). CONCLUSIONS: The fracture strength of monolithic high translucent Y-TZP crowns is considerably higher than that of porcelain-veneered Y-TZP crown cores, porcelain-veneered high translucent Y-TZP crown cores and monolithic lithium disilicate crowns. The fracture strength of a crown made of monolithic high translucent Y-TZP is, with a large safety margin, sufficient for clinical use for the majority of patients. Porcelain-veneered Y-TZP crown cores show higher fracture resistance than monolithic lithium disilicate crowns.
Authors: Marina Amaral; Regina F Villefort; Renata Marques Melo; Gabriel K R Pereira; Yu Zhang; Luiz Felipe Valandro; Marco Antonio Bottino Journal: J Mech Behav Biomed Mater Date: 2017-03-07
Authors: Regina Furbino Villefort; Marina Amaral; Gabriel Kalil Rocha Pereira; Tiago Moreira Bastos Campos; Yu Zhang; Marco Antonio Bottino; Luiz Felipe Valandro; Renata Marques de Melo Journal: Dent Mater Date: 2017-01-21 Impact factor: 5.304