Is there lattice contraction in multicomponent metal oxides? Case study for GdVO4:Eu3+ nanoparticles.

Metal oxide nanomaterials have been found to have great potential for diverse applications due to their unique relationships between structure and properties. Lattice expansion as particle size reduces was previously considered to be general for metal oxide nanomaterials. It is now a great challenge to see if lattice contraction could be induced by the size effect for metal oxide nanomaterials. ABO4 metal oxides (e.g., CaWO4, GdVO4, and CdWO4) are some of the most important functional materials with many applications, while such oxides at the nanoscale are never reported to show a lattice contraction. This work presents a first report on the variation from lattice expansion to lattice contraction by tuning the microstructures of GdVO4:Eu(3+) nanocrystals. A hydrothermal method was adopted to synthesize GdVO4:Eu(3+) nanocrystals, and then these nanoparticles were calcined at 600 ° C in air. It is found that particle size reduction led to a lattice contraction for the calcined samples, which is in contrast to the lattice expansion observed for the hydrothermally synthesized counterparts or many other metal oxide nanomaterials. In addition, the lattice symmetry of the calcined samples remained almost a constant. The results indicate that the negative surface stress was eliminated by calcination treatment, leading to a homogeneous compression process in the lattice structure of the calcined GdVO4:Eu(3+) nanocrystals. Furthermore, Eu(3+) was taken as a structural probe and a luminescence center to study the local environments pertinent to these structural changes and to optimize the photoluminescence performance.