PURPOSE: To evaluate the effectiveness of three types of abutments in the maintenance of screw joint preload before and after cyclic loading as well as to observe possible microdamage in the structure of the components using a scanning electron microscope (SEM). MATERIALS AND METHODS:Forty-five external-hex implants were embedded in epoxy resin, received their respective abutments, and were randomly divided into three experimental groups (n = 15): (1) machined titanium (Ti) abutments; (2) pre-machined gold (Au) abutments; and (3) machined zirconia (ZrO(2)) abutments. The abutment screws were tightened according to the manufacturer's recommended torque. Initially, a static bending test was performed using five specimens of each group to determine the load applied in the cyclic loading test. Thus, 10 specimens of each group were used to measure the reverse torque value (preload) of the abutment screw before and after loading. A cyclic loading (0.5 × 10(6) cycles; 15 Hz) between 11 and 211 N was applied at an angle of 30 degrees to the long axis of the implants. The group means were compared using analysis of variance and the Tukey test (α = .05). RESULTS: The reverse torque analysis before cyclic loading showed no significant difference among the groups (P > .05). After cyclic loading, all preload means decreased significantly. The lowest decrease in preload was observed in the Ti group, whereas the highest decrease was observed in the ZrO(2) group, with a significant difference noted between them (P = .010). The Au group presented an intermediate decrease, with no significant difference compared to the other groups (P > .05). SEM images showed structural changes in the mating surfaces of the abutments after cyclic loading. CONCLUSION: The load application reduced the preload means significantly in all groups, and more significantly in the ZrO(2) group.
RCT Entities:
PURPOSE: To evaluate the effectiveness of three types of abutments in the maintenance of screw joint preload before and after cyclic loading as well as to observe possible microdamage in the structure of the components using a scanning electron microscope (SEM). MATERIALS AND METHODS: Forty-five external-hex implants were embedded in epoxy resin, received their respective abutments, and were randomly divided into three experimental groups (n = 15): (1) machined titanium (Ti) abutments; (2) pre-machined gold (Au) abutments; and (3) machined zirconia (ZrO(2)) abutments. The abutment screws were tightened according to the manufacturer's recommended torque. Initially, a static bending test was performed using five specimens of each group to determine the load applied in the cyclic loading test. Thus, 10 specimens of each group were used to measure the reverse torque value (preload) of the abutment screw before and after loading. A cyclic loading (0.5 × 10(6) cycles; 15 Hz) between 11 and 211 N was applied at an angle of 30 degrees to the long axis of the implants. The group means were compared using analysis of variance and the Tukey test (α = .05). RESULTS: The reverse torque analysis before cyclic loading showed no significant difference among the groups (P > .05). After cyclic loading, all preload means decreased significantly. The lowest decrease in preload was observed in the Ti group, whereas the highest decrease was observed in the ZrO(2) group, with a significant difference noted between them (P = .010). The Au group presented an intermediate decrease, with no significant difference compared to the other groups (P > .05). SEM images showed structural changes in the mating surfaces of the abutments after cyclic loading. CONCLUSION: The load application reduced the preload means significantly in all groups, and more significantly in the ZrO(2) group.
Authors: Ana Sofia Vinhas; Carlos Aroso; Filomena Salazar; Paula López-Jarana; José Vicente Ríos-Santos; Mariano Herrero-Climent Journal: Int J Environ Res Public Health Date: 2020-11-23 Impact factor: 3.390
Authors: John Eversong Lucena de Vasconcelos; Jefferson David Melo de Matos; Daher Antonio Queiroz; Guilherme da Rocha Scalzer Lopes; Bruna Caroline Gonçalves Vasconcelos de Lacerda; Marco Antonio Bottino; Cecilia Pedroso Turssi; Roberta Tarkany Basting; Flávia Lucisano Botelho do Amaral; Fabiana Mantovani Gomes França Journal: Materials (Basel) Date: 2022-08-03 Impact factor: 3.748