PURPOSE: The purpose of this study was to formulate and characterize experimental antibacterial fluoride-releasing sealants and compare them with commercial sealants for fluoride release, recharge, adhesion, and microleakage. METHODS: Two experimental sealants (Exp-1, Exp-2) containing a synthesized antibacterial fluoride-releasing monomer and fluoride-releasing filler were formulated. Exp-2 also contained NovaMin nanoparticles. Commercial sealants Clinpro (CL) FluroShield (FS), and SeLECT Defense (E34) were also included. Fluoride release from disk samples in deionized water was measured daily using an ion-selective electrode for 14 days, and after recharging with Neutra-Foam (2.0% sodium fluoride), fluoride was measured for 5 days. Microtensile bonding strengths (MTBS) to enamel were tested after 24-hour storage in water at 37°C or thermocycling 5-55°C for 1,000 cycles. A microleakage test was conducted on extracted teeth using a dye-penetration method. The data were analyzed using analysis of variance with the Tukey's honestly significant difference test and Kruskal-Wallis test. RESULTS: Exp-1 and Exp-2 had significantly higher fluoride release and recharge capabilities than CL and FL (P<.05). All tested sealants had similar MTBS before and after thermocycling. Exp-2 and Exp-1 had significantly lower microleakage scores (P<.05) than other groups. CONCLUSION: The experimental sealants had higher fluoride release and recharge capabilities and similar or better retention than commercial sealants.
PURPOSE: The purpose of this study was to formulate and characterize experimental antibacterial fluoride-releasing sealants and compare them with commercial sealants for fluoride release, recharge, adhesion, and microleakage. METHODS: Two experimental sealants (Exp-1, Exp-2) containing a synthesized antibacterial fluoride-releasing monomer and fluoride-releasing filler were formulated. Exp-2 also contained NovaMin nanoparticles. Commercial sealants Clinpro (CL) FluroShield (FS), and SeLECT Defense (E34) were also included. Fluoride release from disk samples in deionized water was measured daily using an ion-selective electrode for 14 days, and after recharging with Neutra-Foam (2.0% sodium fluoride), fluoride was measured for 5 days. Microtensile bonding strengths (MTBS) to enamel were tested after 24-hour storage in water at 37°C or thermocycling 5-55°C for 1,000 cycles. A microleakage test was conducted on extracted teeth using a dye-penetration method. The data were analyzed using analysis of variance with the Tukey's honestly significant difference test and Kruskal-Wallis test. RESULTS:Exp-1 and Exp-2 had significantly higher fluoride release and recharge capabilities than CL and FL (P<.05). All tested sealants had similar MTBS before and after thermocycling. Exp-2 and Exp-1 had significantly lower microleakage scores (P<.05) than other groups. CONCLUSION: The experimental sealants had higher fluoride release and recharge capabilities and similar or better retention than commercial sealants.
Authors: Maristela M Lobo; Reginaldo B Gonçalves; Luiz André F Pimenta; Ana Karina B Bedran-Russo; Patrícia N R Pereira Journal: J Biomed Mater Res B Appl Biomater Date: 2005-10 Impact factor: 3.368
Authors: Maha Ibrahim AlGhannam; Mana'a Saleh AlAbbas; Jumanah Abdulla AlJishi; Muath Abdulrahman AlRuwaili; Jehan AlHumaid; Maria Salem Ibrahim Journal: Polymers (Basel) Date: 2022-02-17 Impact factor: 4.329