2.7 μm emission properties of Er3+ doped tungsten-tellurite glass sensitized by Yb3+ ions.

With a 980 nm laser diode (LD) pumped, the sensitized effect of Yb(3+) ions on 2.7 μm emission properties and energy transfer mechanism in Yb(3+)/Er(3+) co-doped tungsten-tellurite glass were investigated in present paper. Based on absorption spectra, Judd-Ofelt parameters and radiative transition probabilities were calculated and analyzed. The emission spectra were tested and the optimized concentration ratio of Yb(3+) to Er(3+) ions was found to be 3:0.5 with a largest calculated emission cross-section (6.05×10(-21) cm(2)) corresponding to Er(3+):(4)I11/2→(4)I13/2 transition. When the concentration ratio of Yb(3+) to Er(3+) ions was 4:0.5, 1.5 μm and 2.7 μm emission decreased while up-conversion increased. The decreased 1.5 μm and 2.7 μm emission were induced by the saturation of Er(3+):(4)I13/2 level. In brief, the advantageous spectroscopic characteristics indicated that Yb(3+)/Er(3+) co-doped tungsten-tellurite glass may be a promising candidate for application of 2.7 μm emission.