OBJECTIVE: This study aimed to evaluate and compare the mechanical properties of five commercial core materials using fracture toughness (FT), Knoop hardness number (KHN), diametral tensile strength (DTS), and dynamic elastic moduli (DEM). METHODS: Composite material specimens were produced (Rock Core, CosmeCore, ParaCore, MultiCore Flow, and Filtek Supreme Plus). The FT test (n = 15) was performed using notchless triangular prism (NTP) specimens. FT was determined using an Instron testing machine. KHN (n = 3) was evaluated using three indentations applied on each specimen. DTS test (n = 15) was measured using an Instron testing machine. The density. of the specimens (n = 3) was determined by water displacement method. Dynamic Young's, shear moduli, and Poisson's ratio (n = 3) were measured by an ultrasonic method. Statistical analysis was conducted using ANOVA and a Tukey B rank order test (P = 0.05). RESULTS: Rock Core presented the lowest FT values. Filtek Supreme Plus and CosmeCore exhibited significantly higher KHN values than the rest of the materials. CosmeCore had the highest DTS value, which was statistically significant only compared to Rock Core. For DEM, Filtek Supreme Plus exhibited significantly higher Young's and shear moduli than the rest of the materials (P < 0.05). CONCLUSIONS: Results demonstrated significant differences in the FT, KHN, and DTS values of the core build-up materials tested. According to the elastic behavior of the core composite materials, Rock Core had the lowest Young's values.
OBJECTIVE: This study aimed to evaluate and compare the mechanical properties of five commercial core materials using fracture toughness (FT), Knoop hardness number (KHN), diametral tensile strength (DTS), and dynamic elastic moduli (DEM). METHODS: Composite material specimens were produced (Rock Core, CosmeCore, ParaCore, MultiCore Flow, and Filtek Supreme Plus). The FT test (n = 15) was performed using notchless triangular prism (NTP) specimens. FT was determined using an Instron testing machine. KHN (n = 3) was evaluated using three indentations applied on each specimen. DTS test (n = 15) was measured using an Instron testing machine. The density. of the specimens (n = 3) was determined by water displacement method. Dynamic Young's, shear moduli, and Poisson's ratio (n = 3) were measured by an ultrasonic method. Statistical analysis was conducted using ANOVA and a Tukey B rank order test (P = 0.05). RESULTS: Rock Core presented the lowest FT values. Filtek Supreme Plus and CosmeCore exhibited significantly higher KHN values than the rest of the materials. CosmeCore had the highest DTS value, which was statistically significant only compared to Rock Core. For DEM, Filtek Supreme Plus exhibited significantly higher Young's and shear moduli than the rest of the materials (P < 0.05). CONCLUSIONS: Results demonstrated significant differences in the FT, KHN, and DTS values of the core build-up materials tested. According to the elastic behavior of the core composite materials, Rock Core had the lowest Young's values.