Luminescence and energy transfer properties of Ca2Ba3(PO4)3Cl and Ca2Ba3(PO4)3Cl:A (A = Eu2+/Ce3+/Dy3+/Tb3+) under UV and low-voltage electron beam excitation.

Pure Ca2Ba3(PO4)3Cl and rare earth ion (Eu(2+)/Ce(3+)/Dy(3+)/Tb(3+)) doped Ca2Ba3(PO4)3Cl phosphors with the apatite structure have been prepared via a Pechini-type sol-gel process. X-ray diffraction (XRD) and structure refinement, photoluminescence (PL) spectra, cathodoluminescence (CL) spectra, absolute quantum yield, as well as lifetimes were utilized to characterize samples. Under UV light excitation, the undoped Ca2Ba3(PO4)3Cl sample shows broad band photoluminescence centered near 480 nm after being reduced due to the defect structure. Eu(2+) and Ce(3+) ion doped Ca2Ba3(PO4)3Cl samples also show broad 5d → 4f transitions with cyan and blue colors and higher quantum yields (72% for Ca2Ba3(PO4)3Cl:0.04Eu(2+); 67% for Ca2Ba3(PO4)3Cl:0.016Ce(3+)). For Dy(3+) and Tb(3+) doped Ca2Ba3(PO4)3Cl samples, they give strong line emissions coming from 4f → 4f transitions. Moreover, the Ce(3+) ion can transfer its energy to the Tb(3+) ion in the Ca2Ba3(PO4)3Cl host, and the energy transfer mechanism has been demonstrated to be a resonant type, via a dipole-quadrupole interaction. However, under the low voltage electron beam excitation, Tb(3+) ion doped Ca2Ba3(PO4)3Cl samples present different luminescence properties compared with their PL spectra, which is ascribed to the different excitation mechanism. On the basis of the good PL and CL properties of the Ca2Ba3(PO4)3Cl:A (A = Ce(3+)/Eu(2+)/Tb(3+)/Dy(3+)), Ca2Ba3(PO4)3Cl might be promising for application in solid state lighting and field-emission displays.