Cyclic fatigue resistance of yttria-stabilized tetragonal zirconia polycrystals with hot isostatic press processing.

This study investigated the influence of surface roughness and cyclic loading on fatigue resistance in Y-TZP subjected to hot isostatic pressing (HIP). Fifty Y-TZP cylinders 3.0 mm in diameter were divided into Group A (polished by centerless method; TZP-CP) or Group B (blasted and acid-etched: TZP-SB150E). Twenty five cp-titanium cylinders (Ti-SB150E) were used as a control. Static and cyclic tests were carried out according to ISO 14801. The cyclic fatigue test was performed in distilled water at 37°C. Surface morphology and roughness as well as crystal phase on the surfaces were also evaluated. Fracture force under the static test was 1,765N (TZP-CP), 1,220N (TZP-SB150E), and 850 N (yield force, Ti-SB150E). Fracture values under the cyclic test decreased to approximately 70% of those under the static tests. These results indicate that HIPed Y-TZP with a 3.0-mm diameter has sufficient durability for application to dental implants.