Ultrasonication-assisted manufacture of cellulose nanocrystals esterified with acetic acid.

Esterified cellulose nanocrystals (E-CNCs) are cellulose derivatives that could be applied in biomedical and chemical industries. E-CNCs were prepared with cellulose pulp using a mixture of 17.5M acetic and 18.4M sulfuric acid with the aid of ultrasonication. The effects of esterification time (3-7h), ultrasonication time (with a frequency of 40 kHz, 0 to 6h) and temperature (68-75 °C) on the yield and degree of substitution (DS) of E-CNCs were evaluated. The sample obtained without ultrasonication had the lowest yield and DS value of 48.16% and 0.22, respectively, whereas ultrasonication for 5h at 70 °C resulted in a yield of 85.38% and a DS value of 0.46. Characterization indicated the successful esterification of hydroxyl groups of cellulose, and the width of rod-shaped E-CNCs was from 10 to 100 nm. The study provides a simple and convenient method to manufacture E-CNCs.