Morphology and thermal properties of PLA-cellulose nanofibers composites.

Biodegradable nanocomposites were obtained from polylactic acid (PLA) and cellulose nanofibers with diameters ranging from 11 nm to 44 nm. The influence of treated (with 3-aminopropyltriethoxysilane) and untreated nanofibers on the thermal properties of PLA was investigated in detail using multiple session Differential Scanning Calorimetry (DSC) analysis. The nucleating effect of the cellulose nanofibers was confirmed by all the DSC runs (two melting and two crystallization steps). The morphology of both neat PLA and nanocomposites was explored for the first time using a new powerful AFM technique, Peak Force QNM (Quantitative Mechanical Property Mapping at the Nanoscale), which emphasized the nanolevel characteristics by elastic modulus mapping. QNM analyses showed a better dispersion of the silane treated nanofibers in the matrix as compared to the untreated ones. Moreover, a higher degree of crystallinity was detected in the PLA composites containing untreated nanofibers compared to the composites with treated ones.