Interaction behaviors at the interface between liquid Al-Si and solid Ti-6Al-4V in ultrasonic-assisted brazing in air.

Power ultrasonic vibration (20 kHz, 6 μm) was applied to assist the interaction between a liquid Al-Si alloy and solid Ti-6Al-4V substrate in air. The interaction behaviors, including breakage of the oxide film on the Ti-6Al-4V surface, chemical dissolution of solid Ti-6Al-4V, and interfacial chemical reactions, were investigated. Experimental results showed that numerous 2-20 μm diameter-sized pits formed on the Ti-6Al-4V surface. Propagation of ultrasonic waves in the liquid Al-Si alloy resulted in ultrasonic cavitation. When this cavitation occurred at or near the liquid/solid interface, many complex effects were generated at the small zones during the bubble implosion, including micro-jets, hot spots, and acoustic streaming. The breakage behavior of oxide films on the solid Ti-6Al-4V substrate, excessive chemical dissolution of solid Ti-6Al-4V into liquid Al-Si, abnormal interfacial chemical reactions at the interface, and phase transformation between the intermetallic compounds could be wholly ascribed to these ultrasonic effects. An effective bond between Al-Si and Ti-6Al-4V can be produced by ultrasonic-assisted brazing in air.