Stabilization of ferromagnetic order in La(0.7)Sr(0.3)MnO3-SrRuO3 Superlattices.

The study of spatially confined complex oxides is of wide interest, since correlated electrons at interfaces might form exotic phases. Here La(0.7)Sr(0.3)MnO(3)/SrRuO(3) superlattices with coherently grown interfaces were studied by structural techniques, magnetization, and magnetotransport measurements. Magnetization measurements showed that ferromagnetic order in ultrathin La(0.7)Sr(0.3)MnO(3) layers is stabilized in the superlattices down to layer thicknesses of at least two unit cells. This stabilization is destroyed, if the ferromagnetic layers are separated by two unit cell thick SrTiO(3) layers. The resistivity of the superlattices showed metallic behavior and was dominated by the conducting SrRuO(3) layers, the off-diagonal resistivity showed an anomalous Hall effect from both SrRuO(3) and La(0.7)Sr(0.3)MnO(3) layers. This shows that the La(0.7)Sr(0.3)MnO(3) layers are not only ferromagnetic but also highly conducting; probably a conducting hole gas is induced at the interfaces that stabilizes the ferromagnetic order. This result opens up an alternative route for the fabrication of two-dimensional systems with long-range ferromagnetic order.