Facile synthesis of main-chain degradable block copolymers for performance enhanced dismantlable adhesion.

Block copolymers consisting of readily degradable polyperoxides and non-degradable vinyl polymers as the block segments were successfully synthesized by reversible chain transfer catalyzed polymerization, which is one of living radical polymerization techniques. The block copolymers showed characteristic morphology and wettability being different from the polymer blends. When block copolymers containing polyperoxide and polymethacrylate blocks were heated below 150 °C, the polyperoxide blocks were completely degraded and the polymethacrylate blocks were recovered without degradation. Block copolymers containing a poly(2-ethylhexyl methacrylate) block were then investigated as a dismantlable adhesion material, which requires adequate bonding strength during use and easy debonding on demand. Among the several block copolymers, the one consisting of poly(2-ethylhexyl methacrylate) and polyperoxide from methyl sorbate (PPMS) (M(n) = 4900) exhibited good performance as a pressure-sensitive adhesive (PSA). After heating the test specimens in a temperature range from 60 to 100 °C, PSA performance, which was evaluated by 180° peel strength and shear holding power measurements, was significantly diminished. Especially, after heating at 100 °C for 1 h, spontaneous debonding of some test specimens was observed because of the evolution of volatile acetaldehyde from PPMS.