2D SiNx photonic crystal coated Y3Al5O12:Ce3+ ceramic plate phosphor for high-power white light-emitting diodes.

This paper reports the optical effects of a two-dimensional (2D) SiNx photonic crystal layer (PCL) on Y3Al5O12:Ce3+ (YAG:Ce) yellow ceramic plate phosphor (CPP) in order to enhance the forward emission of YAG:Ce CPP-capped high-power white light-emitting diodes (LEDs). By adding the 2D SiNx PCL with a 580 nm lattice constant, integrated yellow emission was improved by a factor of 1.72 compared to that of a conventional YAG:Ce CPP capped on a blue LED cup. This enhanced forward yellow emission is attributed to increased extraction of yellow emission light and improved absorption of blue excitation light through Bragg scattering and/or the leaky modes produced by the 2D PCLs. The introduction of 2D PCL can also reduce the wide variation of optical properties as a function of both ambient temperature and applied current, compared to those of a high-power YAG:Ce CPP-capped LED.