OBJECTIVES: The aim of this study was to thermo-polymerize under high pressure four commercially available dental resin composites to obtain and characterize composite blocks suitable for CAD/CAM procedures. METHODS: Gradia (GC, Japan), Vita VM LC (Vita Zahnfabrik, Germany), Grandio (VOCO, Germany), and EsthetX (Dentsply, Germany), were selected for this study. Paradigm (3 M ESPE, USA), a CAD/CAM composite block, was included for comparison. Composite blocks were obtained through polymerization at high-temperature high-pressure (HT/HP). Samples for mechanical/physical characterizations were cut from Paradigm and HT/HP composite blocks while control samples were obtained by photo-polymerizing (PP) the materials in molds. Flexural strength (σ(f)), fracture toughness (K(IC)), hardness, and density (ρ) were determined and compared by pairwise t-tests (α=0.05). Fractured surfaces were characterized under a scanning electron microscope. RESULTS: The results have shown that HT/HP polymerization resulted in a significant (p<0.05) increase in σ(f), hardness, and ρ for all composites investigated. Even if K(IC) of all materials was increased by HT/HP polymerization, significant increases were detected only for Gradia and EsthetX. The Weibull modulus of HT/HP polymerized composites was higher than that of PP counterparts. HT/HP materials had higher σ(f), Weibull modulus, and K(IC) compared to Paradigm. The most significant SEM observation of fractured K(IC) specimens from all the materials tested was the presence of fewer and smaller voids in HT/HP polymerized composites. SIGNIFICANCE: The results of this study suggest that HT/HP polymerization could be used to obtain dental resin composite blocks with superior mechanical properties, suitable for CAD/CAM processing.
OBJECTIVES: The aim of this study was to thermo-polymerize under high pressure four commercially available dental resin composites to obtain and characterize composite blocks suitable for CAD/CAM procedures. METHODS: Gradia (GC, Japan), Vita VM LC (Vita Zahnfabrik, Germany), Grandio (VOCO, Germany), and EsthetX (Dentsply, Germany), were selected for this study. Paradigm (3 M ESPE, USA), a CAD/CAM composite block, was included for comparison. Composite blocks were obtained through polymerization at high-temperature high-pressure (HT/HP). Samples for mechanical/physical characterizations were cut from Paradigm and HT/HP composite blocks while control samples were obtained by photo-polymerizing (PP) the materials in molds. Flexural strength (σ(f)), fracture toughness (K(IC)), hardness, and density (ρ) were determined and compared by pairwise t-tests (α=0.05). Fractured surfaces were characterized under a scanning electron microscope. RESULTS: The results have shown that HT/HP polymerization resulted in a significant (p<0.05) increase in σ(f), hardness, and ρ for all composites investigated. Even if K(IC) of all materials was increased by HT/HP polymerization, significant increases were detected only for Gradia and EsthetX. The Weibull modulus of HT/HP polymerized composites was higher than that of PP counterparts. HT/HP materials had higher σ(f), Weibull modulus, and K(IC) compared to Paradigm. The most significant SEM observation of fractured K(IC) specimens from all the materials tested was the presence of fewer and smaller voids in HT/HP polymerized composites. SIGNIFICANCE: The results of this study suggest that HT/HP polymerization could be used to obtain dental resin composite blocks with superior mechanical properties, suitable for CAD/CAM processing.
Authors: Faris A Alshahrani; Shorouq Khalid Hamid; Lujain Ali Alghamdi; Firas K Alqarawi; Yousif A Al-Dulaijan; Hamad S AlRumaih; Haidar Alalawi; Maram A Al Ghamdi; Fawaz Alzoubi; Mohammed M Gad Journal: Dent J (Basel) Date: 2022-06-08
Authors: Richard Fürst; Eliška Fürst; Tomáš Vlach; Jakub Řepka; Marek Pokorný; Vladimír Mózer Journal: Materials (Basel) Date: 2021-04-22 Impact factor: 3.623