Novel docetaxel-loaded nanoparticles based on PCL-Tween 80 copolymer for cancer treatment.

BACKGROUND: The formulation of docetaxel available for clinical use (Taxotere) contains a high concentration of polysorbate 80 (Tween 80). After incorporation of Tween 80 into poly-ɛ-caprolactone (PCL)-Tween 80 copolymer, the relative amount of Tween 80 should be decreased and the advantages of PCL and Tween 80 should be combined.
METHODS: A novel PCL-Tween 80 copolymer was synthesized from ɛ-caprolactone and Tween 80 in the presence of stannous octoate as a catalyst via ring opening polymerization. Two types of nanoparticle formulation were made from commercial PCL and a self-synthesized PCL-Tween 80 copolymer using a modified solvent extraction/evaporation method.
RESULTS: The nanoparticles were found by field emission scanning electron microscopy to have a spherical shape and be 200 nm in diameter. The copolymers could encapsulate 10% of the drug in the nanoparticles and release 34.9% of the encapsulated drug over 28 days. PCL-Tween 80 nanoparticles could be internalized into the cells and had higher cellular uptake than the PCL nanoparticles. The drug-loaded PCL-Tween 80 nanoparticles showed better in vitro cytotoxicity towards C6 cancer cells than commercial Taxotere at the same drug concentration.
CONCLUSION: Nanoparticles using PCL-Tween 80 copolymer as drug delivery vehicles may have a promising outcome for cancer patients.

Introduction

Cancer remains a major health problem worldwide. The use of polymeric nanoparticles as drug delivery vehicles for anticancer therapeutics has great potential to revolutionize the future of cancer therapy. However, nanoparticles can be rapidly eliminated/excreted by macrophages in the reticuloendothelial system located primarily in the liver and spleen, resulting in a short half-life in the circulation after intravenous administration.1 Various attempts have been made to achieve a longer circulation time to avoid or reduce the absorption of nanoparticles onto phagocytes.2 Previous studies have shown that nanoparticles coated with a neutral hydrophilic outer layer can generate stealth particles and decrease phagocytic uptake, and thus significantly increase the blood circulation time with a high level of drug concentration in nonreticuloendothelial organs, such as the intestines and kidney.3,4 A number of surfactants, such as poloxamines,4 poloxamers, D-α-tocopheryl polyethylene glycol 1000 succinate (TPGS),5 polyethylene glycol,6 and Tween 804,7 have been used as coating materials. Importantly, some coating surfactants may help nanoparticles cross the gastrointestinal and blood-brain barriers.8,9 Systemically administered chemotherapy is often ineffective in the treatment of central nervous system diseases. One reason for this low efficacy is insufficient drug delivery to the brain due to the presence of the blood–brain barrier, which restricts exchange of solutes between the blood and extracellular brain fluid. Tween 80-coated nanoparticles have been reported to have the ability to transport loaded drugs across the blood–brain barrier after intravenous injection.8–10 It has been reported that polybutylcyanoacrylate nanoparticles are able to deliver hexapeptide dalargin, doxorubicin, and other agents which are significantly obstructed by the blood–brain barrier.11 This may be because the nanoparticles can adsorb apoliproprotein E, which mimics low-density lipoprotein, onto the nanoparticle surface and thus be uptaken via receptor-mediated endocytosis by endothelial cells in the brain capillaries.12–15 It was reported that Tween 80-coated polybutylcyanoacrylate nanoparticles could enhance brain concentrations of administered doxorubicin by about 60-fold in mice.16 Tween 80 is a polyethylene sorbitol ester, with a calculated molecular weight of 1310 Da, assuming 20 ethylene oxide units, one sorbitol, and one oleic acid as the primary fatty acid. Tween 80 is widely used in biochemical applications, including for solubilizing proteins, isolating nuclei from cells in cell culture, growing tubercle bacilli, and emulsifying and dispersing substances in medicinal and food products.17

Docetaxel is one of the most potent anticancer agents, and has activity against a wide range of tumors. Its commercial formulation, Taxotere®, is formulated with a high concentration of Tween 80 (40 g/L), which has been found to have severe side effects, including hypersensitivity reactions, cumulative fluid retention, nausea, mouth sores, fatigue, hair loss, peripheral neuropathy, and anemia, and has shown incompatibility with commonly used polyvinyl chloride intravenous administration sets.18 Therefore, investigation of alternative formulations of docetaxel without Tween 80 or with addition of a low concentration of Tween 80 is under way, and several approaches based on docetaxel conjugation,19 nanoparticles,20 liposomes,21 polymeric nanoparticles,22 micelles,23 and prodrugs24 have been proposed. In addition, poly-ɛ-caprolactone (PCL) is a very attractive synthetic polymer due to its properties of high permeability, lack of toxicity, and biodegradability.25 In this research, we developed PCL-Tween 80 as a novel copolymer and a novel PCL-Tween 80 nanoparticle as a potential drug carrier for cancer chemotherapy. Using this design, the relative amount of Tween 80 would be decreased and the advantages of PCL and Tween 80 would be combined after the incorporation of Tween 80 into a PCL-Tween 80 copolymer.

Materials and methods

Materials

PCL (molecular weight 42,000 Da), stannous octoate [Sn(OOCC7H15)2], and Tween 80 were supplied by Sigma- Aldrich (St Louis, MO). The monomer, ɛ-caprolactone, was purchased from Acros Organics (Geel, Belgium). TPGS [C33O5H54(CH2CH2O)23] was from Pubmed Co, Ltd, ( Shenzhen, China). Docetaxel of purity 99.8% was purchased from Pubmed. Fetal bovine serum was obtained from Gibco (Life Technologies, AG, Switzerland). Acetonitrile and methanol were purchased from EM Science (ChromAR, high-pressure liquid chromatography grade, Mallinckrodt Baker, Phillipsburg, NJ). All other chemicals used were of the highest quality commercially available. Ultrapure water produced by Boon Environmental Industry Co, Ltd, (Tianjin, China) was used throughout all the experiments.

Synthesis of PCL-Tween 80 copolymer

As shown in Figure 1, PCL-Tween 80 copolymer was synthesized from ɛ-caprolactone and Tween 80 in the presence of stannous octoate as a catalyst via ring opening polymerization. Briefly, 9 g of ɛ-caprolactone, 1 g of Tween 80, and 0.02 mL of stannous octoate were added to a flask. The mixture was heated to 160°C and allowed to react for 12 hours. Synthesis was carried out in an oxygen-free and moisture-free environment. The product was dissolved in dichloromethane and then precipitated in excess cold methanol to remove unreacted ɛ-caprolactone monomers and Tween 80. The final product was collected by filtration and vacuum-dried at 45°C for two days.

Figure 1

Schematic diagram of the synthesis of PCL-Tween 80 copolymer.

Abbreviation: PCL, poly-ɛ-caprolactone.

Characterization of PCL-Tween 80 copolymer

A Fourier transform infrared spectrophotometer (Thermo Nicolet, Madison, WI) was used to investigate the molecular structure of the PCL-Tween 80 copolymer. Briefly, samples for Fourier transform infrared analysis were prepared by grinding 99% KBr with 1% copolymer and then pressing the mixture into a transparent tablet. The Tween 80 content and number-averaged molecular weight of the copolymer were determined by 1H nuclear magnetic resonance (NMR) in CDCl3 at 300 Hz (Bruker ACF300). The weight-averaged molecular weight and molecular weight distribution were determined by gel permeation chromatography. Thermogravimetric analysis (TGA 2050 thermogravimetric analyzer, Perkin Elmer, Waltham, MA) was carried out to investigate the thermal properties of the copolymer. During thermogravimetric analysis, about 5–15 mg of the copolymer sample was heated from 0°C to 600°C at a rate of 10°C/minute. The weight loss pattern in the copolymer thermogram could be related to the composition of the copolymer.

Preparation of docetaxel-loaded nanoparticles

The nanoparticles were prepared by a solvent extraction/ evaporation method with slight modification.18 Briefly, with a theoretical loading of 10%, 11.1 mg of docetaxel and 100 mg PCL-Tween 80 copolymer were dissolved in 8 mL dichloromethane to prepare the nanoparticles. The solution formed was poured into 120 mL of 0.03% (w/v) TPGS solution under gentle stirring. The mixture was sonicated for 120 seconds at 25 W output to form an oil/water emulsion. The emulsion was then evaporated overnight under reduced pressure to remove the dichloromethane. The particle suspension was centrifuged at 23,000 rpm for 15 minutes and then washed three times to remove the emulsifier and unencapsulated drug. The resulting particles were resuspended in 10 mL of deionized water and freeze-dried. The fluorescent coumarin 6-loaded PCL-Tween 80 nanoparticles were prepared in the same way, except that 0.1% (w/v) coumarin 6 was encapsulated instead of docetaxel. Docetaxel-loaded PCL nanoparticles were prepared by the same procedure.

Nanoparticle characterization

Particle size and zeta potential

The particle size and size distribution of the nanoparticles were measured by dynamic light scattering (Zetasizer Nano ZS90, Malvern Instruments Ltd, Worcestershire, UK). The dried particles (about 2 mg) were suspended in deionized water before measurement. The zeta potential of the nanoparticles was determined by laser Doppler anemometry (Zetasizer Nano ZS90). The measurement was performed in triplicate.

Surface morphology

The surface morphology of the nanoparticles was observed by field emission scanning electron microscopy using a JEOL JSM-6700F system (JEOL, Tokyo, Japan) operated at a 5.0 kV accelerating voltage. To prepare samples for field emission scanning electron microscopy, a drop of the particle suspension was placed on a grid or stud, and the supernatant liquid was removed with a capillary after the particles were allowed to settle. The particles were then coated with a platinum layer using a JFC-1300 automatic fine platinum coater (JEOL) for 30 seconds.

Drug content and encapsulation efficiency

Drug loading content and encapsulation efficiency of the nanoparticles were determined by high-pressure liquid chromatography (LC 1200, Agilent Technologies, Santa Clara, CA) as described previously.25 In short, 5 mg of the nanoparticles were dissolved in 1 mL dichloromethane under vigorous vortexing. The organic solution was transferred to 5 mL of mobile phase consisting of deionized water and acetonitrile (50:50, v/v). A nitrogen stream was introduced to evaporate the dichloromethane for about 15 minutes, and then a clear solution was obtained for high-pressure liquid chromatographic analysis. A reverse-phase Inertsil® C-18 column (150 mm × 4.6 mm, pore size 5 mm, GL Science Inc, Tokyo, Japan) was used. The flow rate of the mobile phase was 1 mL/minute. The column effluent was detected at 227 nm with an ultraviolet-visible detector. The drug encapsulation efficiency was defined as the ratio between the amount of docetaxel encapsulated in the nanoparticles and that added in the process. Experiments were performed in triplicate, and results are expressed as the mean ± standard deviation.

In vitro release studies

In this assay, 15 mg aliquots of drug-loaded nanoparticles, weighed by an electronic balance (XS105DU, Mettler Toledo, Greifensee, Switzerland), were dispersed in 5 mL of release medium (phosphate buffer solution, pH 7.4, containing 0.05% w/v Tween 80) to form a suspension. Tween 80 was used to increase the solubility of docetaxel in the buffer solution and avoid binding of docetaxel to the tube wall. The suspension was transferred into a regenerated cellulose dialysis membrane (Spectra/Por 6, molecular weight cutoff 1000, Spectrum, Houston, TX). The closed bag was then put into a centrifuge tube and immersed in 15 mL of release medium. The tube was put in an orbital water bath shaking at 120 rpm and at 37°C; 10 mL aliquots of solutions were periodically removed for analysis and replaced with fresh medium. The collected samples were extracted with 2 mL dichloromethane and reconstituted in a 5 mL mobile phase. A nitrogen stream was introduced to evaporate the dichloromethane. The analysis procedure was the same as for the measurement of drug encapsulation efficiency.

In vitro cell test

Cell culture

Glioma C6 cell lines were obtained from the American Tissue Culture Collection (Rockville, MD) and cultured using the methods described by Freshney.26 Briefly, cells (104 cells/mL) were seeded in 75 cm2 tissue culture flasks (15 mL/flask) with Dulbecco’s modified Eagle medium supplemented with 10% fetal bovine serum and 1% antibiotic, and incubated at 37°C in a humidified environment of 5% CO2.

Cellular uptake assay

The cell lines used in the study were cultured in a 96-well black bottom plate at a density of 5 × 103 cells/well for 24 hours, before addition of medium containing fluorescent nanoparticles at a series of concentrations, ie, 100, 200, and 500 μg/mL, and incubation for another 2 hours. The cells were then washed three times with phosphate-buffered solution before dissolving in 0.5% Triton-X 100 NaOH aqueous solution (0.2 N). Particle uptake by the cell monolayers was then determined by measuring the fluorescent intensity with a microplate reader. The fluorescent intensity of the coumarin 6-loaded nanoparticles was determined in a similar manner prior to the experiment. The results obtained were expressed as a percentage of the total number of coumarin 6-loaded nanoparticles found in the solubilized cells to the total number of coumarin 6-loaded nanoparticles applied to the cells.

For analysis using confocal laser scanning microscopy (Olympus Fluoview FV-1000, Olympus Optical Co, Ltd, Tokyo, Japan), the cells were first cultured on Lab-Tek™ chambered coverglass for 24 hours (104 cells/chamber). The cell monolayers were then incubated with medium containing PCL-Tween 80 nanoparticles (200 μg/mL) for 2 hours and rinsed three times with phosphate-buffered solution. After fixing with ethanol for 20 minutes, they were washed again with phosphate-buffered solution, and stained thereafter with 4′,6-diamidino-2-phenylindole dihydrochloride (DAPI, Fluka, Buche, Switzerland) for 30 minutes and rinsed again to remove the free dye. The cells were then viewed and imaged by confocal laser scanning microscopy with imaging software. Images of the cells were determined with a differential interference contrast channel, and the images of coumarin 6-loaded nanoparticles and the nuclei of cells stained by DAPI were recorded using a blue channel (DAPI) with excitation at 340 nm and a green channel (coumarin 6) with excitation at 488 nm.

Cell viability assay

In this study, in vitro cancer cell viability was assessed using an MTT toxic assay, which is widely used to evaluate the cytotoxic activity of drugs or biomaterials. This method is based on the capacity of living cells to metabolize the yellow tetrazolium salt, MTT, to a chromophore formazan product, the absorbance of which can be determined by spectrophotometric measurement. C6 glioma cells (passages 6–10) were used for in vitro evaluation of the cytotoxicity of docetaxel-loaded PCL-Tween 80 nanoparticles in comparison with docetaxel formulated in Tween 80 (Taxotere) and docetaxel-loaded PCL nanoparticles. The cells were cultured in 20 mL of Dulbecco’s modified Eagle medium supplemented with 10% fetal bovine serum and 1% antibiotic-antimycotic in a 75 cm2 culture flask. The culture flask was incubated at 37°C in a humidified environment containing 5% CO2. The medium was replenished every other day until confluency was reached. The cells were harvested with 0.125% of trypsin-ethylenediamine tetra-acetic acid solution and seeded in 96-well transparent plates (Costar, Corning, NY) at 4 × 104 cells/well.

When the cells seeded in the 96-well transparent plates are at about 70% confluence, the culture medium in the wells was replaced with 100 μL of the drug-loaded nanoparticle suspension or Taxotere in fresh medium, with drug concentrations ranging from 0.25 to 25 μg/mL for 24 and 72 hours of incubation. The drug-loaded nanoparticles were sterilized by gamma irradiation before the cytotoxicity test. Six wells were used for each nanoparticle sample. One row of 12 wells was used as a positive control, in which only culture medium was added to the wells. At the designated times, medium containing the drug was removed and the cells were washed twice with 50 μL of phosphate-buffered solution, after which 90 μL of culture medium and 10 μL of MTT were added to each of the wells. The cells were incubated for 3–4 hours and the solution was then removed from the precipitate. A total of 100 mL of 2-propanol was added to the wells and the level of absorbance was measured using a microplate reader. Untreated cells were used as a control with 100% viability, and cells without addition of MTT were used as a blank to calibrate the spectrophotometer to zero absorbance.

Statistical analyses

The data were expressed as the mean ± standard deviation. The significance of differences was assessed using the Student’s t-test, with P < 0.05 considered to indicate a statistically significant difference.

Results and discussion

As shown in Figure 1, PCL-Tween 80 copolymers were synthesized by ring opening polymerization in the presence of ɛ-caprolactone and Tween 80. The PCL-Tween 80 copolymer was then characterized by 1H NMR in CDCl3, and the spectrum is shown in Figure 2. The peak at 3.65 ppm could be attributed to the −CH2 protons of the polyethylene oxide part of Tween 80 in the copolymers. The small peaks in the aliphatic region belong to various moieties of −CH3 and −CH2 protons in the Tween 80 tails. The peaks at 4.06 (peak A), 2.31 (peak C), 1.60–1.70 (peak D), and 1.35–1.43 (peak E) were assigned to −OCH2, −COCH2, −CH2(4 H) and −CH2(2 H) segments of PCL, respectively.25

Figure 2

Typical 1H-NMR spectra of PCL-Tween 80 copolymer.

Abbreviations: PCL, poly-ɛ-caprolactone; NMR, nuclear magnetic resonance.

Figure 3 shows the Fourier transform infrared spectra of the PCL-Tween 80 copolymer. In the PCL-Tween 80 spectrum, the carbonyl band of PCL-Tween 80 copolymer appears at 1729 cm−1. The bands in the range 2867–2950 cm−1 are assigned to the −CH2 stretching band of PCL. The absorption band at 3400–3650 cm−1 is attributed to the terminal hydroxyl group and that at 1044–1298 cm−1 is due to C–O stretching.27 Of these, the band at 1243 cm−1 is assigned to asymmetric COC stretching.28 The band at 1298 cm−1 has been used in the literature to investigate the crystallinity change in PCL.29 The results confirmed the successful synthesis of PCL-Tween 80 copolymer.

Figure 3

Fourier transform infrared spectra of PCL-Tween 80 copolymer.

Abbreviation: PCL, poly-ɛ-caprolactone.

In the gel permeation chromatography analysis, we confirmed that the PCL-Tween 80 copolymer was synthesized by ring-opening polymerization. The product was not a physical mixture of Tween 80 and ɛ-caprolactone. The number-averaged molecular weight calculated from the gel permeation chromatograph was 21,656. The molecular weight of the PCL-Tween 80 copolymer could also be calculated using the ratio between the NMR peak areas at 1.35–1.43 (peak area 1.07) and 3.65 (peak area 0.23). The number-averaged molecular weight of the PCL-Tween 80 copolymer was determined to be 18,388. It seems that the molecular weight detected by gel permeation chromatography and NMR were the same. In addition, the feeding ratio of ɛ-caprolactone and the Tween 80 molecular mass were 90% and 10%, respectively. However, the ratio of ɛ-caprolactone and Tween 80 molecular mass integrated into the PCL-Tween 80 copolymer was 92.88% and 7.12%.

Thermogravimetric analysis was performed on the synthesized copolymers to investigate their thermal properties. Figure 4 shows typical thermal degradation profiles for PCL-Tween 80 copolymer, which have two main regions of weight loss. Each turning point marked the combustion of a new component in the copolymers. The 200°C–420°C and 420°C–550°C combustion zones were attributed to the PCL and Tween 80 parts of the copolymers, respectively. These results further confirmed successful synthesis of PCL-Tween 80 copolymer.

Figure 4

Thermogravimetric profiles of PCL-Tween 80 copolymer.

Abbreviation: PCL, poly-ɛ-caprolactone.

Characterization of drug-loaded nanoparticles

Size, zeta potential, and encapsulation efficiency

The particle size data for the docetaxel-loaded PCL-Tween 80 nanoparticles, drug-free PCL-Tween 80 nanoparticles, and docetaxel-loaded PCL nanoparticles fabricated in this study are shown in Table 1. Physicochemical characteristics, such as particle size and surface properties, play key roles in determining their in vitro drug release, cellular uptake, and cytotoxicity of these nanoparticles, as well as their in vivo pharmacokinetics and biodistribution, and thereby the therapeutic efficacy of the encapsulated drug.30–32 Permeability of the particles through the intestinal mucosa decreases with increasing particle size, reaching a cutoff at around 500 nm.31 The resulting nanoparticles were 200–280 nm in diameter, which is in the size range favoring cellular uptake of nanoparticles.32 The average size of the PCL-Tween 80 nanoparticles was much smaller and the size distribution much narrower than that of the PCL nanoparticles. This may be due to the self-emulsifying function of the Tween 80 component in the copolymer. There was also evidence that the amphipathic Tween 80 surfactants align themselves at the oil-water interface to promote stability of the particles by lowering the surface energy and thus resisting particle coalescence and flocculation.25,32 It can be also seen from Table 1 that the PCL-Tween 80 nanoparticles could achieve around 80% drug encapsulation efficiency at 10% drug loading, which is much higher than that achieved by the PCL nanoparticles. The drug-loaded PCL-Tween 80 nanoparticles showed a negative surface charge of around −20 mV. Compared with the PCL nanoparticles, the zeta potential of which is around −13.55 mV, a great increase in the absolute value of the zeta potential could be observed for the PCL-Tween 80 nanoparticles, which may result in higher dispersion stability. The recent literature has reported that a higher absolute value of the zeta potential indicates a more stable suspension, and a lower value indicates colloid instability, which could lead to aggregation of nanoparticles.33,34

Table 1

Characterization of nanoparticles (n = 3)

Sample	Polymer	Theoretical drug loading	Size (nm)	PDI	ZP (mV)	EE (%)
ANP	PCL-Tween 80	10%	204.95 ± 3.66	0.201 ± 0.23	−20.14 ± 0.15	81.98 ± 2.61
BNP	PCL-Tween 80	0	192.45 ± 1.93	0.163 ± 0.17	−18.33 ± 0.31	0
CNP	PCL-Tween 80	*	217.36 ± 2.02	0.241 ± 0.09	−22.25 ± 0.29	Not shown
DNP	PCL	10%	258.48 ± 5.95	0.301 ± 0.15	−13.55 ± 0.19	71.44 ± 3.61
ENP	PCL	*	223.33 ± 3.33	0.236 ± 0.31	−16.26 ± 0.22	Not shown

Note: Coumarin 6.

Abbreviations: PDI, polydispersity index; ZP, zeta potential; EE, encapsulation efficiency; ANP, PCL-Tween 80 nanoparticles; DNP, docetaxel-loaded PCL nanoparticles; BNP, drug-free PCL-Tween 80 nanoparticles; ENP, coumarin 6-loaded PCL nanoparticles; CNP, coumarin 6-loaded PCL-Tween 80 nanoparticles.

The surface morphology of the docetaxel-loaded PCL-Tween 80 nanoparticles was investigated by field emission scanning electron microscopy. Figure 5 shows the field emission scanning electron microscopic images for docetaxel-loaded PCL-Tween 80 nanoparticles. Further, these images confirmed the particle size determined by dynamic light scattering. Analysis of particle morphology revealed that the PCL-Tween 80 nanoparticles had a well defined spherical shape and were around 200 nm in diameter.

Figure 5

Field emission scanning electron microscopy image of docetaxel-loaded PCL-Tween 80 nanoparticles.

Abbreviation: PCL, poly-ɛ-caprolactone.

In vitro drug release

The in vitro drug release profiles for PCL and PCL-Tween 80 nanoparticles in the first 28 days are presented in Figure 6. A biphasic release pattern of drug release was observed from both polymeric nanoparticles. However, the drug release from the PCL-Tween 80 nanoparticles was found to be 25.76% and 34.90% of the encapsulated drug in the first 5 days and at 28 days, respectively, which was much faster than that of the PCL nanoparticles, ie, 18.25% and 24.73%, respectively, for the same time periods. The more rapid drug release from the PCL-Tween 80 nanoparticles may be attributable to the lower molecular weight and higher hydrophilicity of the PCL-Tween 80 copolymer in comparison with the PCL nanoparticles.

Figure 6

In vitro release profile of docetaxel-loaded PCL-Tween 80 nanoparticles and docetaxel-loaded PCL nanoparticles.

Abbreviations: PCL, poly-ɛ-caprolactone; NPs, nanoparticles.

Uptake of coumarin 6-loaded nanoparticles by C6 cells

A C6 glioma cell line was used to investigate the uptake of polymeric nanoparticles by brain cancer cells. It is becoming clear that the therapeutic effects of drug-loaded nanoparticles would depend on internalization and sustained retention of the nanoparticles by diseased cells.18–35 Fluorescence uptake by C6 cells could be a useful model for assessing the in vitro therapeutic effect of various docetaxel formulations for brain cancer. As shown in Table 1, the coumarin 6-loaded nanoparticles used for cellular uptake research were highly relevant to the docetaxel-loaded nanoparticles in terms of their size and zeta potential. Thus, cellular uptake of coumarin 6-loaded PCL-Tween 80 nanoparticles and PCL nanoparticles was compared in this research using a C6 model brain cancer cell line. Uptake of coumarin 6-loaded nanoparticles by C6 cells was assayed following 2 hours of incubation, and the results are shown in Figure 7. The cellular nanoparticle uptake efficiency in C6 cells was found to be dose-dependent for both formulations. The cellular uptake efficiency of PCL-Tween 80 nanoparticles was 1.63-fold, 1.76-fold, and 1.74-fold higher than that of PCL nanoparticles at incubated particle concentrations of 100, 250, and 500 μg/mL, respectively. It has been reported that the uptake of Tween 80-coated nanoparticles by bovine brain capillary cells is better than that of uncoated particles.36 Furthermore, it has been demonstrated that the mechanism of cellular uptake for biodegradable microparticles or nanoparticles is size-dependent.18,37 Thus, it is reasonable to expect that PCL-Tween 80 nanoparticles would have a higher cellular uptake due to the Tween 80 coating and their smaller particle size.

Figure 7

Cellular uptake of coumarin 6-loaded PCL-Tween 80 nanoparticles and coumarin 6-loaded PCL nanoparticles by C6 cells after 2 hours of incubation.

Note: *P < 0.05.

Abbreviation: PCL, poly-ɛ-caprolactone.

Figure 8 shows confocal laser scanning microscopic images of C6 cells after 2 hours of incubation with coumarin 6-loaded PCL-Tween 80 nanoparticles at a 200 μg/mL concentration. The images were obtained from the DAPI (blue) channel, the green fluorescent protein (green) channel, and the overlay of the two channels. It can be observed from Figure 8 that the fluorescence of the coumarin 6-loaded PCL-Tween 80 nanoparticles (green) is located in the cytoplasm around the nucleus (blue, stained by DAPI), indicating that the nanoparticles have been internalized into the cells.

Figure 8

Confocal laser scanning microscopy images of C6 cells after 2 hours of incubation with coumarin 6-loaded PCL-Tween 80 nanoparticles at 37.0°C. The cells were stained by DAPI (blue) and the coumarin 6-loaded nanoparticles are green. The cellular uptake was visualized by overlaying images obtained by green fluorescent protein filter and DAPI filter: left image from DAPI channel (A); center image from green fluorescent protein channel (B); right image from combined green fluorescent protein channel and DAPI channel (C).

Abbreviation: PCL, poly-ɛ-caprolactone.

Assessment of nanoparticle cytotoxicity

A C6 glioma cell line was also used to investigate the cytotoxicity of the docetaxel-loaded copolymers, which was compared with that for the commercial formulation, ie, Taxotere. The drug-loaded nanoparticles were sterilized by gamma radiation to exclude any sample contamination effect, and were then suspended and cultured with the C6 cells. Figure 9 shows the viability of C6 cells after 24, 48, and 72 hours of cell culture with docetaxel formulated in the PCL- Tween 80 nanoparticles and PCL nanoparticles, respectively, in comparison with that of the Taxotere formulation at the same 0.25, 2.5, 12.5, and 25 μg/mL docetaxel dose (n = 6). It can be concluded from Figure 9 that both nanoparticle formulations have advantages in decreasing cancer cell viability versus the current clinical dosage form, and that PCL-Tween 80 nanoparticles can have even better effects than PCL nanoparticles. For example, viability of C6 cells after 24 hours of incubation at the 12.5 μg/mL drug concentration was 77.45% for Taxotere, 71.22% (ie, a 27.63% increase in cytotoxicity) for PCL-Tween 80 nanoparticles, and 75.75% (ie, a 7.54% increase in cytotoxicity) for PCL nanoparticles. Furthermore, compared with Taxotere, the cytotoxicity of C6 cells was increased by 64.52% (P < 0.05, n = 6) and 98.88% (P < 0.05, n = 6) for PCL-Tween 80 nanoparticles after 48 and 72 hours of incubation at the 12.5 μg/mL drug concentration, respectively. Such advantages of the nanoparticle formulations may have contributed to the effects of the Tween 80 component in enhancing cellular uptake of the nanoparticles. The advantage of cancer cell viability of the PCL-Tween 80 nanoparticles < PCL nanoparticles < the Taxotere formulation is dependent on incubation time and drug concentration. As time went on, both nanoparticle formulations showed better in vitro therapeutic effects in C6 cells than commercial Taxotere. This may be contributed to by the controlled-release characteristics of the nanoparticle formulation. For example, the cumulative drug release was only 17.71%, 20.90%, and 23.33% for PCL-Tween 80 nanoparticles after 24, 48, and 72 hours (Figure 6), respectively, and the release started from 0%, while Taxotere immediately became 100% available for the C6 cells in culture.

Figure 9

Viability of C6 cells after 24 (A), 48 (B), and 72 (C) hours of cell culture with docetaxel formulated in ANP and DNP in comparison with Taxotere® at the same docetaxel dose.

Note: n = 6, *P < 0.05.

Abbreviations: PCL, poly-ɛ-caprolactone; ANP, PCL-Tween 80 nanoparticles; DNP, PCL nanoparticles.

Conclusion

A novel PCL-Tween 80 copolymer was successfully synthesized in this research. PCL-Tween 80 nanoparticles were prepared by a modified solvent extraction/evaporation method. Docetaxel was chosen as the prototype anticancer drug due to its excellent therapeutic activity against a wide spectrum of cancers. The nanoparticles were found by field emission scanning electron microscopy to be of spherical shape and around 200 nm in diameter. The copolymers could encapsulate 10% of the drug in the nanoparticles and had released 34.9% ± 2.23% of the drug by 28 days. The PCL-Tween 80 nanoparticles could be internalized into cells and had higher cellular uptake than PCL nanoparticles. The drug-loaded PCL-Tween 80 nanoparticles showed better in vitro cytotoxicity towards C6 glioma cells than commercial Taxotere at the same drug concentration. However, the effects of the nanoparticle formulation should actually be better given their controlled-release features. Further in vivo investigations, including pharmacokinetics, biodistribution, pharmacodynamics, and toxicity, will be carried out to evaluate the potential of these copolymer nanoparticles to be used as drug delivery vehicles.